上海罗地亚PA66 A218 V40 40%玻纤增强高强度高钢性尺寸稳定

Solvay TECHNYL? A 218 V40 PA66, 40% glass fiber, DRY

Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 40% Glass Fiber Filled

Solvay

产品说明:

Description: Polyamide PA66, reinforced with 40% of glass fiber, heat stabilized for injection molding.

Available in: Asia Pacific, Europe and North America

Product Applications: TECHNYL A 218 V40 is used in all sectors of industry, offering and excellent combination between thermal and mechanical properties. This grade is used in: automotive industry, manufacture of components for electrical tools, and transport and building. This product is available in natural and black.

Information provided by Rhodia, Rhodia has been acquired by Solvay.

Solvay TECHNYL? A 218 V40 PA66, 40% glass fiber, DRY 物性表

物理性能额定值 (公制) 额定值 (英制) 测试方法

密度 1.46 g/cc 0.0527 lb/in3 ISO 1183/A

吸水率 0.70 %
@Temperature 23.0 °C, Time 86400 sec
0.70 %
@Temperature 73.4 °F, Time 24.0 hour
ISO 62

线性成型收缩率 0.0057 cm/cm 0.0057 in/in Isotropy

线性成型收缩率,Flow 0.0040 cm/cm 0.0040 in/in

线性成型收缩率，横向 0.0070 cm/cm 0.0070 in/in

机械性能额定值 (公制) 额定值 (英制) 测试方法

抗张强度(断裂) 225 MPa 32600 psi ISO 527 Type 1A

伸长率 (断裂) 2.0 % 2.0 % ISO 527 Type 1A

拉伸模量 13.0 GPa 1890 ksi ISO 527 Type 1A

弯曲模量 10.8 GPa 1570 ksi ISO 178

悬壁梁缺口冲击强度 13.5 kJ/m2 6.42 ft-lb/in2 ISO 180/1eA

简支梁无缺口冲击强度 9.70 J/cm2 46.2 ft-lb/in2 ISO 179/1eU

简支梁缺口冲击强度 1.50 J/cm2 7.14 ft-lb/in2 ISO 179/1eA

电气性能额定值 (公制) 额定值 (英制) 测试方法

体积电阻率 1.00e+14 ohm-cm 1.00e+14 ohm-cm IEC 60093

表面电阻 6.00e+13 ohm 6.00e+13 ohm IEC 60093

介电常数 3.7 3.7 IEC 60250

介电强度 35.0 kV/mm 889 kV/in IEC 60243

耗散因数 0.010 0.010 IEC 60250

相比耐漏电起痕指数(CTI) 450 V 450 V Solution A; IEC 60112

热性能额定值 (公制) 额定值 (英制) 测试方法

线形热膨胀系数 - 流动 20.0 μm/m-°C
@Temperature 23.0 - 85.0 °C
11.1 μin/in-°F
@Temperature 73.4 - 185 °F
ISO 11359

熔融温度 263 °C 505 °F ISO 11357

载荷下热变形温度(1.8 MPa) 255 °C 491 °F ISO 75/Af

可燃性(UL94) HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
1210

极限氧指数 23 % 23 % ISO 4589

加工性能额定值 (公制) 额定值 (英制) 测试方法

进料温度 260 - 280 °C 500 - 536 °F

料筒前部温度 280 - 310 °C 536 - 590 °F

模具温度 60.0 - 90.0 °C 140 - 194 °F

干燥温度 80.0 °C 176 °F

水分含量 = 0.20 % = 0.20 %

材料描述测试方法

Compression Zone 270-300°C

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.46 g/cc	0.0527 lb/in3	ISO 1183/A
吸水率	0.70 % @Temperature 23.0 °C, Time 86400 sec	0.70 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
线性成型收缩率	0.0057 cm/cm	0.0057 in/in	Isotropy
线性成型收缩率,Flow	0.0040 cm/cm	0.0040 in/in
线性成型收缩率，横向	0.0070 cm/cm	0.0070 in/in

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	225 MPa	32600 psi	ISO 527 Type 1A
伸长率 (断裂)	2.0 %	2.0 %	ISO 527 Type 1A
拉伸模量	13.0 GPa	1890 ksi	ISO 527 Type 1A
弯曲模量	10.8 GPa	1570 ksi	ISO 178
悬壁梁缺口冲击强度	13.5 kJ/m2	6.42 ft-lb/in2	ISO 180/1eA
简支梁无缺口冲击强度	9.70 J/cm2	46.2 ft-lb/in2	ISO 179/1eU
简支梁缺口冲击强度	1.50 J/cm2	7.14 ft-lb/in2	ISO 179/1eA

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	1.00e+14 ohm-cm	1.00e+14 ohm-cm	IEC 60093
表面电阻	6.00e+13 ohm	6.00e+13 ohm	IEC 60093
介电常数	3.7	3.7	IEC 60250
介电强度	35.0 kV/mm	889 kV/in	IEC 60243
耗散因数	0.010	0.010	IEC 60250
相比耐漏电起痕指数(CTI)	450 V	450 V	Solution A; IEC 60112

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	20.0 μm/m-°C @Temperature 23.0 - 85.0 °C	11.1 μin/in-°F @Temperature 73.4 - 185 °F	ISO 11359
熔融温度	263 °C	505 °F	ISO 11357
载荷下热变形温度(1.8 MPa)	255 °C	491 °F	ISO 75/Af
可燃性(UL94)	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	1210
极限氧指数	23 %	23 %	ISO 4589

加工性能	额定值 (公制)	额定值 (英制)
进料温度	260 - 280 °C	500 - 536 °F
料筒前部温度	280 - 310 °C	536 - 590 °F
模具温度	60.0 - 90.0 °C	140 - 194 °F
干燥温度	80.0 °C	176 °F
水分含量	= 0.20 %	= 0.20 %

材料描述		测试方法
Compression Zone	270-300°C