CYCOLOY resin grade CX2142ME is an injection moldable PC/ABS blend with Br- and Cl-free flame retardant systems. Key features of good flow, good impact, UL-94 V0 rating at 1.2 mm, and improved chemical resistance to generally used hospital cleaners, make it ideal for a wide variety of applications including enclosures for medical and hopital equipments.
CYCOLOY? CX2142ME resin 物性表
| 基本信息 |
|
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
Chlorine Free 抗撞击性，良好 良好的流动性 耐化学性良好 无溴 阻燃性 |
| 用途 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.19 |
g/cm3 |
ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) |
23 |
g/10 min |
ASTM D1238 |
| 溶化体积流率（MVR） (260°C/2.16 kg) |
21.0 |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动 (3.20 mm) |
0.40 到 0.60 |
% |
内部方法 |
| 吸水率 |
|
|
ISO 62 |
| 饱和, 23°C |
0.20 |
% |
ISO 62 |
| 平衡, 23°C, 50% RH |
0.10 |
% |
ISO 62 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| -- 1 |
2900 |
MPa |
ASTM D638 |
| -- |
2700 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 2 |
64.0 |
MPa |
ASTM D638 |
| 屈服 |
61.0 |
MPa |
ISO 527-2/50 |
| 断裂 3 |
54.0 |
MPa |
ASTM D638 |
| 断裂 |
51.0 |
MPa |
ISO 527-2/50 |
| 伸长率 |
|
|
|
| 屈服 4 |
4.0 |
% |
ASTM D638 |
| 屈服 |
4.0 |
% |
ISO 527-2/50 |
| 断裂 5 |
90 |
% |
ASTM D638 |
| 断裂 |
90 |
% |
ISO 527-2/50 |
| 弯曲模量 |
|
|
|
| 50.0 mm 跨距 6 |
2700 |
MPa |
ASTM D790 |
| -- 7 |
2500 |
MPa |
ISO 178 |
| 弯曲应力 |
|
|
|
| -- |
100 |
MPa |
ISO 178 |
| 屈服, 50.0 mm 跨距 8 |
100 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 9 |
|
|
ISO 179/1eA |
| -30°C |
10 |
kJ/m2 |
ISO 179/1eA |
| 23°C |
15 |
kJ/m2 |
ISO 179/1eA |
| 悬壁梁缺口冲击强度 |
|
|
|
| -30°C |
120 |
J/m |
ASTM D256 |
| 23°C |
600 |
J/m |
ASTM D256 |
| -30°C 10 |
10 |
kJ/m2 |
ISO 180/1A |
| 23°C 11 |
15 |
kJ/m2 |
ISO 180/1A |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) |
63.0 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火, 3.20 mm |
94.0 |
°C |
ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm |
98.0 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm |
84.0 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm |
90.0 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 12 |
84.0 |
°C |
ISO 75-2/Af |
| 维卡软化温度 |
102 |
°C |
ASTM D1525, ISO 306/B50, ISO 306/B120 13 |
| Ball Pressure Test (75°C) |
Pass |
|
IEC 60695-10-2 |
| 线形热膨胀系数 |
|
|
ASTM E831, ISO 11359-2 |
| 流动 : -40 到 40°C |
7.5E-5 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| 横向 : -40 到 40°C |
7.5E-5 |
cm/cm/°C |
ASTM E831, ISO 11359-2 |
| 导热系数 |
0.20 |
W/m/K |
ISO 8302 |
| 可燃性 |
额定值 |
|
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 1.20 mm |
V-0 |
|
UL 94 |
| 2.00 mm |
5VB |
|
UL 94 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
82.2 到 87.8 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 干燥时间，最大 |
8.0 |
hr |
|
| 建议的最大水分含量 |
0.040 |
% |
|
| 建议注射量 |
30 到 80 |
% |
|
| 料筒后部温度 |
221 到 254 |
°C |
|
| 料筒中部温度 |
221 到 266 |
°C |
|
| 料筒前部温度 |
243 到 277 |
°C |
|
| 射嘴温度 |
243 到 277 |
°C |
|
| 加工（熔体）温度 |
243 到 277 |
°C |
|
| 模具温度 |
60.0 到 82.2 |
°C |
|
| 背压 |
0.345 到 0.689 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 排气孔深度 |
0.038 到 0.076 |
mm |
|
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
类型 1, 50 mm/min |
| 3 . |
类型 1, 50 mm/min |
| 4 . |
类型 1, 50 mm/min |
| 5 . |
类型 1, 50 mm/min |
| 6 . |
1.3 mm/min |
| 7 . |
2.0 mm/min |
| 8 . |
1.3 mm/min |
| 9 . |
80*10*3 sp=62mm |
| 10 . |
80*10*3 |
| 11 . |
80*10*3 |
| 12 . |
80*10*4 mm |
| 13 . |
标准 B (120°C/h), 载荷2 (50N) |