Eastman Tritan FX100 Copolyester 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.19 g/cc | 0.0430 lb/in3 | ASTM D1505 |
| 吸水率 | 0.50 %
@Time 86400 sec
|
0.50 %
@Time 24.0 hour
|
ASTM D570 |
| Water Vapor Transmission | 4.00 g/m2/day
@Temperature 23.0 °C
|
0.258 g/100 in2/day
@Temperature 73.4 °F
|
ASTM F1249 |
| 11.0 g/m2/day
@Temperature 38.0 °C
|
0.708 g/100 in2/day
@Temperature 100 °F
|
ASTM F1249 | |
| Oxygen Transmission | 32.0 cc-mm/m2-24hr-atm | 81.3 cc-mil/100 in2-24hr-atm | ASTM D3985 |
| Carbon Dioxide Transmission | 149 cc-mm/m2-24hr-atm | 378 cc-mil/100 in2-24hr-atm | ASTM D1434 |
| 厚度 | 254 microns | 10.0 mil | Thickness of film tested; ASTM D374 |
| Surface Tension | 8.0 dynes/cm | 8.0 dynes/cm | Polar; ASTM D5946 |
| 39 dynes/cm | 39 dynes/cm | Dispersive; ASTM D5946 | |
| 46 dynes/cm | 46 dynes/cm | Total; ASTM D5946 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(MD : 屈服) | 41.0 MPa | 5950 psi | ASTM D882 |
| 抗张强度(TD : 屈服) | 40.0 MPa | 5800 psi | ASTM D882 |
| 断裂伸长率，MD | 179 % | 179 % | ASTM D882 |
| 断裂伸长率，TD | 203 % | 203 % | ASTM D882 |
| Film Elongation at Yield, MD | 7.0 % | 7.0 % | ASTM D882 |
| Film Elongation at Yield, TD | 7.0 % | 7.0 % | ASTM D882 |
| 割线模量(MD) | 1.50 GPa | 218 ksi | Tangent; ASTM D882 |
| 割线模量(TD) | 1.40 GPa | 203 ksi | Tangent; ASTM D882 |
| 多轴向仪器化冲击能量 | 4.60 J | 3.39 ft-lb | Dynatup; ASTM D3763 |
| 撕裂强度 | 11.0 kN/m | 62.8 pli | MD; Trouser @200/mm/min; ISO 6383-1 |
| 11.0 kN/m | 62.8 pli | TD; Trouser @200/mm/min; ISO 6383-1 | |
| 12.0 kN/m | 68.5 pli | Split tear method, TD; ASTM D1938 | |
| 13.0 kN/m | 74.2 pli | Split tear method, MD; ASTM D1938 | |
| 埃尔曼多夫抗撕强度(MD) | 520 g | 520 g | ASTM D1922 |
| 埃尔曼多夫抗撕强度(TD) | 571 g | 571 g | ASTM D1922 |
| 埃尔曼多夫抗撕强度(MD) | 2.00 g/micron | 50.8 g/mil | ASTM D1922 |
| 埃尔曼多夫抗撕强度(TD) | 2.20 g/micron | 55.9 g/mil | ASTM D1922 |
| Dart Drop | 3.50 g/micron
@Temperature 23.0 °C
|
88.9 g/mil
@Temperature 73.4 °F
|
ASTM 1709A |
| 3.60 g/micron
@Temperature -30.0 °C
|
91.4 g/mil
@Temperature -22.0 °F
|
ASTM 1709A | |
| Dart Drop Test | 882 g
@Temperature 23.0 °C
|
1.94 lb
@Temperature 73.4 °F
|
ASTM 1709A |
| 913 g
@Temperature -30.0 °C
|
2.01 lb
@Temperature -22.0 °F
|
ASTM 1709A | |
| 抗张强度(MD : 断裂) | 59.0 MPa | 8560 psi | ASTM D882 |
| 抗张强度(TD : 断裂) | 52.0 MPa | 7540 psi | ASTM D882 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | 90.0 μm/m-°C | 50.0 μin/in-°F | ASTM D696 |
| 比热容 | 1.72 J/g-°C
@Temperature 60.0 °C
|
0.410 BTU/lb-°F
@Temperature 140 °F
|
DSC |
| 1.88 J/g-°C
@Temperature 100 °C
|
0.450 BTU/lb-°F
@Temperature 212 °F
|
DSC | |
| 2.26 J/g-°C
@Temperature 150 °C
|
0.540 BTU/lb-°F
@Temperature 302 °F
|
DSC | |
| 2.43 J/g-°C
@Temperature 200 °C
|
0.580 BTU/lb-°F
@Temperature 392 °F
|
DSC | |
| 2.59 J/g-°C
@Temperature 250 °C
|
0.620 BTU/lb-°F
@Temperature 482 °F
|
DSC | |
| 玻璃化转变温度，Tg | 110 °C | 230 °F | DSC |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.55 | 1.55 | ASTM D542 |
| 雾度 | 0.70 % | 0.70 % | ASTM D1003 |
| 光泽度 | 161 % | 161 % | @ 60°; ASTM D2457 |
| Yellow Index | 0.50 % | 0.50 % | ASTM D1925 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
| UV Transmittance | 89 %
@Thickness 0.380 mm
|
89 %
@Thickness 0.0150 in
|
UV/Vis Spectro |
| 合规性 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| FDA | Yes | Yes | Repeated use food contact articles |
| NSF | Yes | Yes | Food equipment materials; NSF/ANSI Standard 51 |
| 材料描述 | 测试方法 | |
|---|---|---|
| PPT Tear Resistance, M.D. | 42 N | ASTM D2582 |
| PPT Tear Resistance, T.D. | 56 N | ASTM D2582 |
| Taber Abrasion | 23% haze | ASTM 1044, Average at 25 cycles |