DuPont Performance Polymers Rynite? FR543 NC010 PET 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.79 g/cc | 1.79 g/cc | ASTM D792 |
| 密度 | 1.79 g/cc | 0.0647 lb/in3 | ISO 1183 |
| 填料含量 | 43 % | 43 % | |
| Water Absorption | 0.060 %
@Temperature 23.0 °C
|
0.060 %
@Temperature 73.4 °F
|
50%RH,23°C,24h; ASTM D570 |
| 0.11 %
@Temperature 23.0 °C
|
0.11 %
@Temperature 73.4 °F
|
Equilibrium 50%RH; ISO 62, Similar to | |
| 0.62 %
@Temperature 23.0 °C
|
0.62 %
@Temperature 73.4 °F
|
Saturation, immersed; ISO 62, Similar to | |
| 线性成型收缩率 | 0.0013 cm/cm
@Thickness 1.57 mm
|
0.0013 in/in
@Thickness 0.0618 in
|
Flow |
| 0.0020 cm/cm
@Thickness 3.20 mm
|
0.0020 in/in
@Thickness 0.126 in
|
Flow | |
| 0.0048 cm/cm
@Thickness 1.57 mm
|
0.0048 in/in
@Thickness 0.0618 in
|
Transverse | |
| 0.0065 cm/cm
@Thickness 3.20 mm
|
0.0065 in/in
@Thickness 0.126 in
|
Transverse | |
| 线性成型收缩率,Flow | 0.0025 cm/cm | 0.0025 in/in | Annealed; ISO 294-4 |
| 0.0020 cm/cm
@Thickness 2.00 mm
|
0.0020 in/in
@Thickness 0.0787 in
|
ISO 294-4 | |
| 线性成型收缩率，横向 | 0.0105 cm/cm | 0.0105 in/in | Annealed; ISO 294-4 |
| 0.0075 cm/cm
@Thickness 2.00 mm
|
0.0075 in/in
@Thickness 0.0787 in
|
ISO 294-4 | |
| 化合物熔体指数 | 6.0 g/10 min
@Load 2.16 kg, Temperature 280 °C
|
6.0 g/10 min
@Load 4.76 lb, Temperature 536 °F
|
cm3/10 min; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 95 | 95 | ASTM D785 |
| 102 | 102 | ISO 2039/2 | |
| 洛氏硬度（R 级） | 120 | 120 | ASTM D785 |
| 122 | 122 | ISO 2039/2 | |
| 抗张强度(断裂) | 170 MPa
@Temperature 23.0 °C
|
24700 psi
@Temperature 73.4 °F
|
ISO 527 |
| 抗张强度 | 55.2 MPa
@Temperature 150 °C
|
8010 psi
@Temperature 302 °F
|
ASTM D638 |
| 86.5 MPa
@Temperature 90.0 °C
|
12500 psi
@Temperature 194 °F
|
ASTM D638 | |
| 172 MPa
@Temperature 23.0 °C
|
24900 psi
@Temperature 73.4 °F
|
ASTM D638 | |
| 210 MPa
@Temperature -40.0 °C
|
30500 psi
@Temperature -40.0 °F
|
ASTM D638 | |
| 22.4 MPa
@Strain 0.470 %, Temperature 150 °C
|
3250 psi
@Strain 0.470 %, Temperature 302 °F
|
ISO 527 | |
| 27.22 MPa
@Strain 0.430 %, Temperature 120 °C
|
3948 psi
@Strain 0.430 %, Temperature 248 °F
|
ISO 527 | |
| 27.5 MPa
@Strain 0.160 %, Temperature 0.000 °C
|
3990 psi
@Strain 0.160 %, Temperature 32.0 °F
|
ISO 527 | |
| 28.39 MPa
@Strain 0.350 %, Temperature 90.0 °C
|
4118 psi
@Strain 0.350 %, Temperature 194 °F
|
ISO 527 | |
| 29.0 MPa
@Strain 0.140 %, Temperature -40.0 °C
|
4210 psi
@Strain 0.140 %, Temperature -40.0 °F
|
ISO 527 | |
| 30.0 MPa
@Strain 0.210 %, Temperature 40.0 °C
|
4350 psi
@Strain 0.210 %, Temperature 104 °F
|
ISO 527 | |
| 31.0 MPa
@Strain 0.180 %, Temperature 23.0 °C
|
4500 psi
@Strain 0.180 %, Temperature 73.4 °F
|
ISO 527 | |
| 34.9 MPa
@Strain 0.940 %, Temperature 150 °C
|
5060 psi
@Strain 0.940 %, Temperature 302 °F
|
ISO 527 | |
| 35.57 MPa
@Strain 0.310 %, Temperature 60.0 °C
|
5159 psi
@Strain 0.310 %, Temperature 140 °F
|
ISO 527 | |
| 41.5 MPa
@Strain 1.41 %, Temperature 150 °C
|
6020 psi
@Strain 1.41 %, Temperature 302 °F
|
ISO 527 | |
| 41.8 MPa
@Strain 0.830 %, Temperature 120 °C
|
6060 psi
@Strain 0.830 %, Temperature 248 °F
|
ISO 527 | |
| 45.7 MPa
@Strain 1.87 %, Temperature 150 °C
|
6630 psi
@Strain 1.87 %, Temperature 302 °F
|
ISO 527 | |
| 47.19 MPa
@Strain 0.690 %, Temperature 90.0 °C
|
6844 psi
@Strain 0.690 %, Temperature 194 °F
|
ISO 527 | |
| 49.1 MPa
@Strain 2.34 %, Temperature 150 °C
|
7120 psi
@Strain 2.34 %, Temperature 302 °F
|
ISO 527 | |
| 50.35 MPa
@Strain 0.370 %, Temperature 40.0 °C
|
7303 psi
@Strain 0.370 %, Temperature 104 °F
|
ISO 527 | |
| 50.8 MPa
@Strain 1.23 %, Temperature 120 °C
|
7370 psi
@Strain 1.23 %, Temperature 248 °F
|
ISO 527 | |
| 51.7 MPa
@Strain 2.81 %, Temperature 150 °C
|
7500 psi
@Strain 2.81 %, Temperature 302 °F
|
ISO 527 | |
| 52.4 MPa
@Strain 0.320 %, Temperature 0.000 °C
|
7600 psi
@Strain 0.320 %, Temperature 32.0 °F
|
ISO 527 | |
| 53.8 MPa
@Strain 3.28 %, Temperature 150 °C
|
7800 psi
@Strain 3.28 %, Temperature 302 °F
|
ISO 527 | |
| 53.9 MPa
@Strain 0.280 %, Temperature -40.0 °C
|
7820 psi
@Strain 0.280 %, Temperature -40.0 °F
|
ISO 527 | |
| 55.0 MPa
@Strain 0.520 %, Temperature 60.0 °C
|
7980 psi
@Strain 0.520 %, Temperature 140 °F
|
ISO 527 | |
| 55.6 MPa
@Strain 3.75 %, Temperature 150 °C
|
8060 psi
@Strain 3.75 %, Temperature 302 °F
|
ISO 527 | |
| 56.4 MPa
@Strain 0.350 %, Temperature 23.0 °C
|
8180 psi
@Strain 0.350 %, Temperature 73.4 °F
|
ISO 527 | |
| 56.85 MPa
@Strain 1.63 %, Temperature 120 °C
|
8245 psi
@Strain 1.63 %, Temperature 248 °F
|
ISO 527 | |
| 57.1 MPa
@Strain 4.21 %, Temperature 150 °C
|
8280 psi
@Strain 4.21 %, Temperature 302 °F
|
ISO 527 | |
| 58.5 MPa
@Strain 4.69 %, Temperature 150 °C
|
8480 psi
@Strain 4.69 %, Temperature 302 °F
|
ISO 527 | |
| 59.61 MPa
@Strain 1.03 %, Temperature 90.0 °C
|
8646 psi
@Strain 1.03 %, Temperature 194 °F
|
ISO 527 | |
| 61.26 MPa
@Strain 2.04 %, Temperature 120 °C
|
8885 psi
@Strain 2.04 %, Temperature 248 °F
|
ISO 527 | |
| 64.62 MPa
@Strain 2.44 %, Temperature 120 °C
|
9372 psi
@Strain 2.44 %, Temperature 248 °F
|
ISO 527 | |
| 67.28 MPa
@Strain 2.84 %, Temperature 120 °C
|
9758 psi
@Strain 2.84 %, Temperature 248 °F
|
ISO 527 | |
| 68.2 MPa
@Strain 1.37 %, Temperature 90.0 °C
|
9890 psi
@Strain 1.37 %, Temperature 194 °F
|
ISO 527 | |
| 69.36 MPa
@Strain 3.24 %, Temperature 120 °C
|
10060 psi
@Strain 3.24 %, Temperature 248 °F
|
ISO 527 | |
| 71.09 MPa
@Strain 3.65 %, Temperature 120 °C
|
10310 psi
@Strain 3.65 %, Temperature 248 °F
|
ISO 527 | |
| 71.87 MPa
@Strain 0.730 %, Temperature 60.0 °C
|
10420 psi
@Strain 0.730 %, Temperature 140 °F
|
ISO 527 | |
| 72.35 MPa
@Strain 4.05 %, Temperature 120 °C
|
10490 psi
@Strain 4.05 %, Temperature 248 °F
|
ISO 527 | |
| 72.8 MPa
@Strain 0.560 %, Temperature 40.0 °C
|
10600 psi
@Strain 0.560 %, Temperature 104 °F
|
ISO 527 | |
| 74.5 MPa
@Strain 0.480 %, Temperature 23.0 °C
|
10800 psi
@Strain 0.480 %, Temperature 73.4 °F
|
ISO 527 | |
| 74.52 MPa
@Strain 1.70 %, Temperature 90.0 °C
|
10810 psi
@Strain 1.70 %, Temperature 194 °F
|
ISO 527 | |
| 75.5 MPa
@Strain 0.420 %, Temperature -40.0 °C
|
11000 psi
@Strain 0.420 %, Temperature -40.0 °F
|
ISO 527 | |
| 75.9 MPa
@Strain 0.470 %, Temperature 0.000 °C
|
11000 psi
@Strain 0.470 %, Temperature 32.0 °F
|
ISO 527 | |
| 79.34 MPa
@Strain 2.04 %, Temperature 90.0 °C
|
11510 psi
@Strain 2.04 %, Temperature 194 °F
|
ISO 527 | |
| 83.14 MPa
@Strain 2.41 %, Temperature 90.0 °C
|
12060 psi
@Strain 2.41 %, Temperature 194 °F
|
ISO 527 | |
| 83.19 MPa
@Strain 0.940 %, Temperature 60.0 °C
|
12070 psi
@Strain 0.940 %, Temperature 140 °F
|
ISO 527 | |
| 85.76 MPa
@Strain 2.75 %, Temperature 90.0 °C
|
12440 psi
@Strain 2.75 %, Temperature 194 °F
|
ISO 527 |