东莞市常平浩云塑胶经营部
LG ABS AF305HT ABS
LG ABS AF308 ABS
LG ABS AF312 ABS
LG ABS AF312A ABS
LG ABS AF312B ABS
LG ABS AF312C ABS
LG ABS AF312T ABS
LG ABS AF342 ABS
LG ABS AF342F ABS
LG ABS AF342T ABS
LG ABS AF345 ABS
LG ABS AF360 ABS
LG ABS AF360C ABS
LG ABS AF360S ABS
LG ABS AF368 ABS
LG ABS AP163 ABS
LG ABS BM662 ABS
LG ABS BM662B ABS
LG ABS EF378 ABS
LG ABS EF378L ABS
LG ABS ER451 ABS
LG ABS ER460 ABS
LG ABS ER461 ABS
LG ABS HF350U ABS
LG ABS HF380 ABS
LG ABS HF380G ABS
LG ABS HF380I ABS
LG ABS HF380NS ABS
LG ABS HF380P ABS
LG ABS HF380U ABS
LG ABS HG173 ABS
LG ABS HG193S ABS
LG ABS HI100 ABS
LG ABS HI100H ABS
LG ABS HI100K ABS
LG ABS HI100X ABS
LG ABS HI110 ABS
LG ABS HI121 ABS
LG ABS HI121H ABS
LG ABS HI121U ABS
LG ABS HI140 ABS
LG ABS HI153 ABS
LG ABS HT700 ABS
LG ABS LG703W ABS
LG ABS LG704W ABS
LG ABS LG709W ABS
LG ABS LG713 ABS
LG ABS LG749W ABS
LG ABS MA201 ABS
LG ABS MA210 ABS
LG ABS MA221 ABS
LG ABS MP211 ABS
LG ABS MP220 ABS
LG ABS MU620 ABS
LG ABS PI641 ABS
LG ABS PI642G ABS
LG ABS PT270 ABS
LG ABS RS650 ABS
LG ABS RS656H ABS
LG ABS RS657 ABS
LG ABS RS657L ABS
LG ABS RS800D ABS
LG ABS RS800M ABS
LG ABS RX710 ABS
LG ABS SG175 ABS
LG ABS SG175G ABS
LG ABS SG175NS ABS
LG ABS SH610A ABS
LG ABS SH610S ABS
LG ABS SH625 ABS
LG ABS TR300 ABS
LG ABS TR551 ABS
LG ABS TR552 ABS
LG ABS TR556 ABS
LG ABS TR557 ABS
LG ABS TR558A ABS
LG ABS XG568 ABS
LG ABS XG569C ABS
LG ABS XG570 ABS
LG ABS XR401 ABS
LG ABS XR401B ABS
LG ABS XR401F ABS
LG ABS XR401I ABS
LG ABS XR401T ABS
LG ABS XR404 ABS
LG ABS XR404HJ ABS
LG ABS XR404T ABS
LG ABS XR407E ABS
LG ABS XR409E ABS
LG ABS XR409H ABS
LG ABS XR409HJ ABS
LG ABS XR419 ABS
LG ABS XR440 ABS
LG ABS XR474 ABS
LG ABS XR474F ABS
LG ABS XR490 ABS
LG Chemical MA221 ABS, High Impact, Low Gloss 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| 吸水率 | 0.19 %
@Temperature 23.0 °C, Time 86400 sec
|
0.19 %
@Temperature 73.4 °F, Time 24.0 hour
|
ASTM D570 |
| 处理 | 0.010 | 0.010 | Injection and Extrusion Molding |
| 线性成型收缩率,Flow | 0.0040 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0040 - 0.0070 in/in
@Thickness 0.126 in
|
ASTM D955 |
| 熔体流动速率 | 5.0 g/10 min
@Load 10.0 kg, Temperature 220 °C
|
5.0 g/10 min
@Load 22.0 lb, Temperature 428 °F
|
ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 100 | 100 | ASTM D785 |
| 抗张强度(屈服) | 42.2 MPa
@Thickness 3.20 mm
|
6120 psi
@Thickness 0.126 in
|
50 mm/min; ASTM D638 |
| 伸长率 (断裂) | = 50 %
@Thickness 3.20 mm
|
= 50 %
@Thickness 0.126 in
|
50 mm/min; ASTM D638 |
| 弯曲强度 | 60.8 MPa
@Thickness 3.20 mm
|
8820 psi
@Thickness 0.126 in
|
15 mm/min; ASTM D790 |
| 弯曲模量 | 2.16 GPa
@Thickness 3.20 mm
|
313 ksi
@Thickness 0.126 in
|
15 mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 3.14 J/cm
@Thickness 6.40 mm, Temperature 23.0 °C
|
5.88 ft-lb/in
@Thickness 0.252 in, Temperature 73.4 °F
|
ASTM D256 |
| 5.69 J/cm
@Thickness 3.20 mm, Temperature 23.0 °C
|
10.7 ft-lb/in
@Thickness 0.126 in, Temperature 73.4 °F
|
ASTM D256 | |
| Izod Impact, Unnotched | 1.47 J/cm
@Thickness 6.40 mm, Temperature -20.0 °C
|
2.76 ft-lb/in
@Thickness 0.252 in, Temperature -4.00 °F
|
ASTM D256 |
| 2.94 J/cm
@Thickness 3.20 mm, Temperature -20.0 °C
|
5.51 ft-lb/in
@Thickness 0.126 in, Temperature -4.00 °F
|
ASTM D256 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa) | 90.0 °C
@Thickness 6.40 mm
|
194 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| 维卡软化温度 | 98.0 °C
@Load 5.00 kg
|
208 °F
@Load 11.0 lb
|
50°C/h; ASTM D1525 |
| 可燃性(UL94) | HB
@Thickness =0.800 mm
|
HB
@Thickness =0.0315 in
|
|
| HB
@Thickness =1.60 mm
|
HB
@Thickness =0.0630 in
|
||
| HB
@Thickness =2.50 mm
|
HB
@Thickness =0.0984 in
|
||
| HB
@Thickness =3.20 mm
|
HB
@Thickness =0.126 in
|
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 料筒后部温度 | 180 - 200 °C | 356 - 392 °F | c |
| 料筒中部温度 | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| 料筒前部温度 | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| 射嘴温度 | 200 - 230 °C | 392 - 446 °F | Injection Molding |
| 1区 | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| 2区 | 190 - 210 °C | 374 - 410 °F | Extrusion Molding |
| 3区 | 200 - 230 °C | 392 - 446 °F | Extrusion Molding |
| 4区 | 200 - 230 °C | 392 - 446 °F | Extrusion Molding |
| Adapter Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion Molding |
| 模具温度 | 200 - 230 °C | 392 - 446 °F | Extrusion Molding |
| 加工（熔体）温度 | 200 - 230 °C | 392 - 446 °F | Injection and Extrusion Molding |
| 模具温度 | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Roll Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Bottom, Extrusion |
| 70.0 - 90.0 °C | 158 - 194 °F | Middle, Extrusion | |
| 70.0 - 100 °C | 158 - 212 °F | Top, Extrusion | |
| 干燥温度 | 70.0 - 80.0 °C | 158 - 176 °F | Injection and Extrusion Molding |
| 干燥时间 | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection and Extrusion Molding |
| 背压 | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| 螺杆转速 | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |