PA66 TECHNYL A R 218 V30

Product TextsPolyamide 66, reinforced with 30% of glass fibre, heat stabilized, for injection moulding. This grade is commonly used in the automotive industry for engine components.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	10000 / 7500	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	190 / 135	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3 / 4	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	80 / 88	kJ/m2	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	80 / 85	kJ/m2	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	12 / 15	kJ/m2	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	9 / 10.5	kJ/m2	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	263 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	255 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	258 / *	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	25 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
Oxygen index	23 / *	%	ISO 4589-1/-2

PA66 TECHNYL A R 218 V30

PA特性

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。

4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。

PA66应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等