Ultraform? N 2640 Z6 UNC
聚甲醛(POM)共聚物
产品说明:
Ultraform N 2640 Z6 UNC is an elastomer-modified injection molding POM grade with excellent impact strength.
Applications
Typical applications include toys components such as bicycle frames, automotive parts such as cladding elements and windshield wiper units, and clips, snap and fastening elements, and other components subject to impact stress.
Ultraform? N 2640 Z6 UNC 物性表
基本信息 |
|
黄卡编号 |
|
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
形式 |
|
加工方法 |
|
物理性能 |
额定值 |
单位制 |
测试方法 |
比重 |
1.33 |
g/cm3 |
ASTM D792, ISO 1183 |
溶化体积流率(MVR)(190°C/2.16 kg) |
4.50 |
cm3/10min |
ISO 1133 |
收缩率 |
|
|
|
流动 : 3.18 mm |
1.9 |
% |
|
垂直流动方向 |
1.6 |
% |
ISO 294-4 |
流动方向 |
1.6 |
% |
ISO 294-4 |
吸水率 |
|
|
|
饱和 |
1.1 |
% |
ASTM D570 |
饱和, 23°C |
1.1 |
% |
ISO 62 |
平衡, 50% RH |
0.25 |
% |
ASTM D570 |
平衡, 23°C, 50% RH |
0.25 |
% |
ISO 62 |
机械性能 |
额定值 |
单位制 |
测试方法 |
拉伸模量(23°C) |
1300 |
MPa |
ISO 527-2 |
抗张强度(屈服, 23°C) |
37.0 |
MPa |
ASTM D638, ISO 527-2 |
伸长率(屈服, 23°C) |
17 |
% |
ASTM D638, ISO 527-2 |
标称拉伸断裂应变(23°C) |
50 |
% |
ISO 527-2 |
拉伸蠕变模量 |
|
|
ISO 899-1 |
1 hr |
825 |
MPa |
ISO 899-1 |
1000 hr |
575 |
MPa |
ISO 899-1 |
弯曲模量(23°C) |
1320 |
MPa |
ASTM D790 |
冲击性能 |
额定值 |
单位制 |
测试方法 |
简支梁缺口冲击强度 |
|
|
ISO 179 |
-30°C |
9.0 |
kJ/m2 |
ISO 179 |
23°C |
18 |
kJ/m2 |
ISO 179 |
简支梁无缺口冲击强度 |
|
|
ISO 179 |
-30°C |
无断裂 |
|
ISO 179 |
23°C |
无断裂 |
|
ISO 179 |
悬壁梁缺口冲击强度 |
|
|
ASTM D256 |
-40°C |
59 |
J/m |
ASTM D256 |
23°C |
160 |
J/m |
ASTM D256 |
热性能 |
额定值 |
单位制 |
测试方法 |
载荷下热变形温度 |
|
|
|
0.45 MPa, 未退火 |
129 |
°C |
ASTM D648 |
1.8 MPa, 未退火 |
71.0 |
°C |
ASTM D648 |
1.8 MPa, 未退火 |
70.0 |
°C |
ISO 75-2/A |
熔融峰值温度 |
166 |
°C |
ASTM D3418, ISO 3146 |
线形热膨胀系数 - 流动 |
|
|
|
-- |
8.0E-5 |
cm/cm/°C |
ASTM E831 |
-- |
1.3E-4 |
cm/cm/°C |
|
RTI Elec |
|
|
UL 746 |
1.50 mm |
50.0 |
°C |
UL 746 |
3.00 mm |
50.0 |
°C |
UL 746 |
RTI Imp |
|
|
UL 746 |
1.50 mm |
50.0 |
°C |
UL 746 |
3.00 mm |
50.0 |
°C |
UL 746 |
RTI |
|
|
UL 746 |
1.50 mm |
50.0 |
°C |
UL 746 |
3.00 mm |
50.0 |
°C |
UL 746 |
电气性能 |
额定值 |
单位制 |
测试方法 |
表面电阻率1 |
1.0E+12 |
ohms |
ASTM D257, IEC 60093 |
体积电阻率 |
|
|
|
1.50 mm |
1.0E+11 |
ohms·cm |
ASTM D257 |
-- |
1.0E+11 |
ohms·cm |
IEC 60093 |
介电强度 |
36 |
kV/mm |
IEC 60243-1 |
介电常数 |
|
|
IEC 60250 |
100 Hz |
4.50 |
|
IEC 60250 |
1 MHz |
4.30 |
|
IEC 60250 |
耗散因数 |
|
|
IEC 60250 |
100 Hz |
0.010 |
|
IEC 60250 |
1 MHz |
0.025 |
|
IEC 60250 |
漏电起痕指数 |
600 |
V |
IEC 60112 |
可燃性 |
额定值 |
单位制 |
测试方法 |
UL 阻燃等级 |
|
|
UL 94 |
1.50 mm |
HB |
|
UL 94 |
3.00 mm |
HB |
|
UL 94 |
注射 |
额定值 |
单位制 |
|
干燥温度 |
80.0 到 110 |
°C |
|
干燥时间 |
2.0 到 4.0 |
hr |
|
建议的最大水分含量 |
0.15 |
% |
|
加工(熔体)温度 |
190 到 230 |
°C |
|
模具温度 |
60.0 到 120 |
°C |
|
注塑压力 |
3.50 到 7.00 |
MPa |
|