基础创新医疗级PC HP4 医疗、保健相关用途 医疗级PC USP Class VI规范
LEXAN? HP4 resin
聚碳酸酯
SABIC Innovative Plastics
产品说明：
Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold release.
LEXAN? HP4 resin 物性表
| 基本信息 |
|
| 黄卡编号 |
- E121562-220863
- E121562-220949
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 多点数据 |
- Elastic Modulus vs Temperature (ASTM D4065)
- Flexural DMA (ASTM D4065)
- Specific Heat vs. Temperature (ASTM D3417)
- Tensile Creep (ASTM D2990)
- Tensile Stress vs. Strain (ASTM D638)
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
|
|
ASTM D792 |
| -- |
1.20 |
g/cm3 |
ASTM D792 |
| -- |
1.19 |
g/cm3 |
ASTM D792 |
| 特定体积 |
0.830 |
cm3/g |
ASTM D792 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) |
11 |
g/10 min |
ASTM D1238 |
| 溶化体积流率（MVR）(300°C/1.2 kg) |
10.0 |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动(3.20 mm) |
0.50 到 0.70 |
% |
内部方法 |
| 吸水率 |
|
|
ASTM D570 |
| 24 hr |
0.15 |
% |
ASTM D570 |
| 平衡, 23°C |
0.35 |
% |
ASTM D570 |
| 平衡, 100°C |
0.58 |
% |
ASTM D570 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度 |
|
|
ASTM D785 |
| M 级 |
70 |
|
ASTM D785 |
| R 级 |
118 |
|
ASTM D785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
| --1 |
2370 |
MPa |
ASTM D638 |
| -- |
2350 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
| 屈服2 |
62.0 |
MPa |
ASTM D638 |
| 屈服 |
63.0 |
MPa |
ISO 527-2/50 |
| 断裂3 |
68.0 |
MPa |
ASTM D638 |
| 断裂 |
70.0 |
MPa |
ISO 527-2/50 |
| 伸长率 |
|
|
| 屈服4 |
7.0 |
% |
ASTM D638 |
| 屈服 |
6.0 |
% |
ISO 527-2/50 |
| 断裂5 |
130 |
% |
ASTM D638 |
| 断裂 |
110 |
% |
ISO 527-2/50 |
| 弯曲模量 |
|
|
| 50.0 mm 跨距6 |
2340 |
MPa |
ASTM D790 |
| --7 |
2300 |
MPa |
ISO 178 |
| 弯曲应力 |
|
|
| -- |
90.0 |
MPa |
ISO 178 |
| 屈服, 50.0 mm 跨距8 |
97.0 |
MPa |
ASTM D790 |
| 泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮) |
10.0 |
mg |
ASTM D1044 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度(23°C) |
35 |
kJ/m2 |
ISO 179/2C |
| 悬壁梁缺口冲击强度 |
|
|
| Colors |
800 |
J/m |
ASTM D256 |
| Natural, Tints |
800 |
J/m |
ASTM D256 |
| 23°C |
800 |
J/m |
ASTM D256 |
| -30°C9 |
10 |
kJ/m2 |
ISO 180/1A |
| 23°C10 |
12 |
kJ/m2 |
ISO 180/1A |
| 无缺口悬臂梁冲击(23°C) |
3200 |
J/m |
ASTM D4812 |
| 装有测量仪表的落镖冲击(23°C, Energy at Peak Load) |
63.0 |
J |
ASTM D3763 |
| 落锤冲击(23°C) |
169 |
J |
ASTM D3029 |
| 拉伸冲击强度11 |
577 |
kJ/m2 |
ASTM D1822 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
| 0.45 MPa, 未退火, 6.40 mm |
137 |
°C |
ASTM D648 |
| 0.45 MPa, 未退火, 100 mm 跨距12 |
136 |
°C |
ISO 75-2/Be |
| 1.8 MPa, 未退火, 6.40 mm |
132 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 100 mm 跨距13 |
125 |
°C |
ISO 75-2/Ae |
| 维卡软化温度 |
|
|
| -- |
154 |
°C |
ASTM D152514 |
| -- |
153 |
°C |
ISO 306/A50 |
| -- |
141 |
°C |
ISO 306/B50 |
| -- |
142 |
°C |
ISO 306/B120 |
| Ball Pressure Test(125°C) |
Pass |
|
IEC 60695-10-2 |
| 线形热膨胀系数 - 流动 |
|
|
| -40 到 95°C |
6.8E-5 |
cm/cm/°C |
ASTM E831 |
| 23 到 80°C |
7.0E-5 |
cm/cm/°C |
ISO 11359-2 |
| 比热 |
1250 |
J/kg/°C |
ASTM C351 |
| 导热系数 |
|
|
| -- |
0.19 |
W/m/K |
ASTM C177 |
| -- |
0.20 |
W/m/K |
ISO 8302 |
| RTI Elec |
130 |
°C |
UL 746 |
| RTI Imp |
130 |
°C |
UL 746 |
| RTI |
130 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E 15 |
ohms |
IEC 60093 |
| 体积电阻率 |
|
|
| -- |
1.0E 17 |
ohms·cm |
ASTM D257 |
| -- |
1.0E 15 |
ohms·cm |
IEC 60093 |
| 介电强度 |
|
|
| 3.20 mm, in Air |
15 |
kV/mm |
ASTM D149 |
| 3.20 mm, 在油中 |
17 |
kV/mm |
IEC 60243-1 |
| 介电常数 |
|
|
| 50 Hz |
3.17 |
|
ASTM D150 |
| 60 Hz |
3.17 |
|
ASTM D150 |
| 1 MHz |
2.96 |
|
ASTM D150 |
| 50 Hz |
2.70 |
|
IEC 60250 |
| 60 Hz |
2.70 |
|
IEC 60250 |
| 1 MHz |
2.70 |
|
IEC 60250 |
| 耗散因数 |
|
|
| 50 Hz |
9.0E-4 |
|
ASTM D150 |
| 60 Hz |
9.0E-4 |
|
ASTM D150 |
| 1 MHz |
0.010 |
|
ASTM D150, IEC 60250 |
| 50 Hz |
1.0E-3 |
|
IEC 60250 |
| 60 Hz |
1.0E-3 |
|
IEC 60250 |
| 相比耐漏电起痕指数(CTI) |
PLC 2 |
|
UL 746 |
| 高电弧燃烧指数(HAI) |
PLC 1 |
|
UL 746 |
| 高电压电弧起痕速率 (HVTR) |
PLC 2 |
|
UL 746 |
| 热丝引燃 (HWI) |
PLC 2 |
|
UL 746 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级(1.47 mm) |
HB |
|
UL 94 |
| 极限氧指数 |
25 |
% |
ASTM D2863, ISO 4589-2 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 折射率 |
1.586 |
|
ASTM D542 |
| 透射率(2540 μm) |
88.0 |
% |
ASTM D1003 |
| 雾度(2540 μm) |
1.0 |
% |
ASTM D1003 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
121 |
°C |
| 干燥时间 |
3.0 到 4.0 |
hr |
| 干燥时间，最大 |
48 |
hr |
| 建议的最大水分含量 |
0.020 |
% |
| 建议注射量 |
40 到 60 |
% |
| 料筒后部温度 |
271 到 293 |
°C |
| 料筒中部温度 |
282 到 304 |
°C |
| 料筒前部温度 |
293 到 316 |
°C |
| 射嘴温度 |
288 到 310 |
°C |
| 加工（熔体）温度 |
293 到 316 |
°C |
| 模具温度 |
71.1 到 93.3 |
°C |
| 背压 |
0.345 到 0.689 |
MPa |
| 螺杆转速 |
40 到 70 |
rpm |
| 排气孔深度 |
0.025 到 0.076 |
mm |
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
类型 1, 50 mm/min |
| 3 . |
类型 1, 50 mm/min |
| 4 . |
类型 1, 50 mm/min |
| 5 . |
类型 1, 50 mm/min |
| 6 . |
1.3 mm/min |
| 7 . |
2.0 mm/min |
| 8 . |
1.3 mm/min |
| 9 . |
80*10*4 |
| 10 . |
80*10*4 |
| 11 . |
Type S |
| 12 . |
120*10*4 mm |
| 13 . |
120*10*4 mm |
| 14 . |
标准 B (120°C/h), 载荷2 (50N) |