LCP VECTRA MT1310

Physical Properties	Metric	English	Comments
Density	1.62g/cc	0.0585lb/in3	ISO 1183
Moisture Absorption	0.0400 %	0.0400 %	23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow	0.0020cm/cm	0.0020in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0040cm/cm	0.0040in/in	ISO 294-4
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	85	85	ISO 2039-2
Tensile Strength at Break	190MPa	27600psi	5mm/min; ISO 527-2/1A
Elongation at Break	2.1 %	2.1 %	5mm/min; ISO 527-2/1A
Tensile Modulus	15.0GPa	2180ksi	50mm/min; ISO 527-2/1A
Flexural Strength	280MPa	40600psi	ISO 178
Flexural Modulus	14.5GPa	2100ksi	ISO 178
Compressive Strength	100MPa @Strain 1.00 %	14500psi @Strain 1.00 %	ISO 604
Compressive Modulus	14.5GPa	2100ksi	ISO 604
Izod Impact, Notched (ISO)	24.0kJ/m2	11.4ft-lb/in2	ISO 180/1A
	29.0kJ/m2 @Temperature 23.0 °C	13.8ft-lb/in2 @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	3.30J/cm2	15.7ft-lb/in2	ISO 179/1eU
Charpy Impact, Notched	2.60J/cm2	12.4ft-lb/in2	ISO 179/1eA
Tensile Creep Modulus, 1 hour	12600MPa	1.83e 6psi	ISO 899-1
Tensile Creep Modulus, 1000 hours	10900MPa	1.58e 6psi	ISO 899-1

LCP VECTRA MT1310

主要性能

1.高温电气/电子装配：能承受SMT装配工序操作，包括无铅回流焊接。2.卓越的热老化性能，在高温下保持固有特性。

3.卓越的流动性-薄壁，复杂的形状。

4.尺寸稳定性极佳，模塑收缩率低，热膨胀系数极小，可与金属相媲美。

5.在成型时，分子链朝着流动的方向排列，产生一种好似其分子自身将其增强的自增强效果。

6.可获得极高的强和弹性模量。

7.优异的耐化学腐蚀性。

8.模塑速度：周期循环极快。

9.卓越的抗蠕变性。

10.阻燃性。

11.在宽广的温度范围内具有卓越的介电性能。

LCP的主要应用领域：

连接器系列、BOBBIN、接插件、SIMM插口、LED(MID)、QFP插口、微波炉支架、热风筒、烫发器、注射成型线路部件(MID)、光感应器(MID)、水晶振荡器座(MID)、集成块支承座、耳机部件、光缆拉伸件、光缆连接器、光缆接插器、针式打印机的线圈、针式打印机的底座、电扇、照相机快门板、泵的部件、USB系列、CD拾音器部件、印刷电路板、线圈骨架的封装材、作光纤电缆接头护套和高强度元件喷气发动机零件等电子电器。.