ACRYPET IR H70

Technical Datasheet |Supplied by Mitsubishi Chemical

ACRYPET? IR H70 by Mitsubishi Chemical is an impact modified polymethylmethacrylate (PMMA) grade. Contains UV ray absorber and exhibits good heat resistance and looks. ACRYPET? IR H70 is recommended for manufacturing of lights, window of LCD and exterior parts of automobile.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14g/cc	1.14g/cc	ISO 1183; JIS K7112
Water Absorption	0.30 % @Time 86400 sec	0.30 % @Time 24.0 hour	ISO 62
Linear Mold Shrinkage	0.0040-0.0080cm/cm	0.0040-0.0080in/in	MRC method
Melt Flow	0.60g/10 min @Load 3.80 kg, Temperature 230 °C	0.60g/10 min @Load 8.39 lb, Temperature 446 °F	ISO 1133
Spiral Flow	170cm @Thickness 2.00 mm, Temperature 230 °C	66.9in @Thickness 0.0787 in, Temperature 446 °F	MRC method
	260cm @Thickness 2.00 mm, Temperature 250 °C	102in @Thickness 0.0787 in, Temperature 482 °F	MRC method
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	38	38	ISO 2039
Tensile Strength	39.0MPa	5660psi	1A/5; ISO 527
Elongation at Break	39 %	39 %	1A/5; ISO 527
Modulus of Elasticity	1.40GPa	203ksi	1A/1; ISO 527
Flexural Strength	57.0MPa	8270psi	ISO 178
Flexural Modulus	1.50GPa	218ksi	ISO 178
Izod Impact, Unnotched (ISO)	8.80kJ/m2	4.19ft-lb/in2	1A; ISO 180

PMMA ACRYPET IR H70

PMMA原料的特性：

无色透明，透光率达90%---92%，韧性强，比硅玻璃大10倍以上。

光学性、绝缘性、加工性及耐候性佳。

溶解于四氯化碳、苯、甲苯二氯乙烷、三氯甲烷和丙酮等有机溶剂。

具有较高透明度和光亮度，耐热性好，并有坚韧，质硬，刚性特点，热变形温度80℃，弯曲强度110Mpa。

密度1.14—1.20g/cc,变形温度76--116℃，成型收缩率0.2—0.8%。

线膨胀系数0.00005—0.00009/℃,热变形温度68--69℃(74--107℃)

PMMA用途

PMMA具有质轻、价廉，易於成型等优点。溶于有机溶剂如苯甲醚等，可以形成良好的薄膜和良好的介电性能，可以作为有机场效应管的介质层。 [1]

它的成型方法有浇铸，射出成型，机械加工、热成型等。尤其是射出成型，可以大批量生产，制程简单，成本低。因此，它的应用日趋广泛，它广泛用于仪器仪表零件、汽车车灯、光学镜片、透明管道。

有机玻璃压克力（亚克力）在建筑业中的应用在建筑方面，有机玻璃压克力（亚克力）主要应用于建筑采光体、透明屋顶、棚顶、电话亭、楼梯和房间墙壁护板等方面；卫生洁具方面有浴缸、洗脸盆、化妆台等产品。在高速公路及高等级道路照明灯罩及汽车灯具方面的应用发展也相当快。其中，建筑采光体、浴缸、街头广告灯箱和电话亭等方面的市场增长较快，今后的发展空间较大，市场前景十分广阔。