ACRYPET VH
Technical Datasheet |Supplied by Mitsubishi Chemical
ACRYPET VH by Mitsubishi Chemical is a standard polymethylmethacrylate (PMMA) grade. Contains UV ray absorber and exhibits heat resistance. ACRYPET? VH is recommended for manufacturing of tail lamps of automobile. Is also available without UV ray absorber as ACRYPET VH 000.
Physical Properties物理性质
|
Metric公制数据
|
Comments测试方法
|
Specific Gravity密度
|
1.19g/cc
|
JIS K7112;ISO 1183
|
Water Absorption吸水率
|
0.3 %
|
24 hours;JIS K7209; ISO 62
|
Mold Shrinkage成型收缩率
|
0.2-0.6%
|
MRC Method
|
Melt Index of Compound熔体流动速率
|
JIS K7210;ISO 1133
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
Comments测试方法
|
M scale洛式硬度M
|
101
|
JIS K7202;ISO 2039
|
Tensile Strength at Break抗拉强度
|
77.0MPa
|
JIS K7162; ISO 527
|
Elongation at Break断裂伸长率
|
6 %
|
JIS K7162; ISO 527
|
Flexural Strength抗弯强度
|
140.0MPa
|
JIS K7171; ISO 178
|
Flexural Modulus弯曲弹性模量
|
3.30GPa
|
JIS K7162; ISO 527
|
Izod Impact, Notched悬臂梁缺口冲击强度
|
1.40kJ/m2
|
JIS K7111; ISO 1
|
PMMA ACRYPET VH
聚甲基丙烯酸甲酯(poly(methylmethacrylate),简称PMMA),又称做压克力、亚克力(英文Acrylic)或有机玻璃、Lucite(商品名称),在香港多称做阿加力胶,具有高透明度,低价格,易于机械加工等优点,是平常经常使用的玻璃替代材料。
物理性质
PMMA的密度比玻璃低:PMMA的密度大约在 1.15-1.19 g/cm3,是玻璃(2.40-2.80 g/cm3)的一半、金属铝(属于轻金属)的43%。
PMMA的机械强度较高:PMMA的相对分子质量大约为200万,是长链的高分子聚合物,而且形成分子的链很柔软,因此,PMMA的强度比较高,抗拉伸和抗冲击的能力比普通玻璃高7~18倍。有一种经过加热和拉伸处理过的有机玻璃,其中的分子链段排列得非常有次序,使材料的韧性有显著提高。用钉子钉进这种有机玻璃,即使钉子穿透了,也不产生裂纹。这种有机玻璃被子弹击穿后同样不会破成碎片。因此,拉伸处理的PMMA可用作防弹玻璃,也用作军用飞机上的座舱盖。
PMMA的熔点较低:PMMA的熔点约130–140°C(265–285°F),比玻璃约1000度的高温低很多。
PMMA的透光率较高
可见光:PMMA是目前最优良的高分子透明材料,透光率达到92%,比玻璃的透光度高。
紫外光:石英能完全透过紫外线,但价格高昂,普通玻璃只能透过0.6%的紫外线。PMMA能有效滤除波长小于300nm的紫外光,但300nm至400nm之间滤除效果较差。部分制造商在PMMA表面进行镀膜,以增加其滤除300nm至400nm紫外光的效果和性质。另一方面,在照射紫外光的状况下,与聚碳酸酯相比,PMMA具有更佳的稳定性
红外线:PMMA允许小于2800nm波长的红外线(IR) 通过。更长波长的IR,小于25,000nm时,基本上可被阻挡。存在特殊的有色PMMA,可以让特定波长IR透过,同时阻挡可见光(应用于远程控制或热感应等)。
PMMA的玻璃转化温度为大约105°C。