PFA美国3M 6505 注塑级 耐化学 高温强度良好 无粘性 内衬应用

PFA塑料为少量全氟丙基全氟乙烯基醚与聚四氟乙烯的共聚物。熔融粘结性增强，溶体粘度下降，而性能与聚四氟乙烯相比无变化。此种树脂可以直接采用普通热塑性成型方法加工成制品。适于制作耐腐蚀件，减磨耐磨件、密封件、绝缘件和医疗器械零件，高温电线、电缆绝缘层，防腐设备、密封材料、泵阀衬套，和化学容器。

3M? Dyneon? Fluoroplastic PFA 6505TZ

全氟烷氧基

3M Advanced Materials Division

产品说明：

3M? Dyneon? Fluoroplastic PFA 6505TZ (a fully fluorinated copolymer of tetrafluoroethylene and perfluorovinylether) has exceptional temperature resistance, excellent electrical properties and excellent chemical inertness and weather resistance. It is used in molded valves, pumps, tanks, filters and pipes, in heat trace cables and in wire for appliances.
Features

• Wide service temperature range

• Excellent, almost universal resistance to solvents and chemicals

• Extremely high weathering resistance and UV stability

• Excellent electrical insulation properties

• High limiting oxygen index: Does not support combustion

• Smooth surfaces

• Good non-stick characteristics

• Good low-friction properties

• Broad processing window

• Improved mold release property

3M? Dyneon? Fluoroplastic PFA 6505TZ 物性表

基本信息
特性	低摩擦系数 共聚物 抗溶剂性 抗紫外线性能良好 良好的电气性能 耐化学性良好 耐气候影响性能良好 耐热性，高 无粘性
用途	泵件 电线电缆应用 阀门/阀门部件 管道系统 过滤器 水箱
形式	粒子
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
密度	2.15	g/cm3	ISO 12086
熔流率（熔体流动速率）(372°C/5.0 kg)	5.0	g/10 min	ISO 1133

硬度	额定值	单位制	测试方法
肖氏硬度(邵氏 D)	60	ASTM D2240, ISO 868

机械性能	额定值	单位制	测试方法
拉伸应力(断裂, 23°C)	30.0	MPa	ISO 527-1
拉伸应变(断裂, 23°C)	410	%	ISO 527-1
弯曲模量	550	MPa	ASTM D790

热性能	额定值	单位制	测试方法
熔融温度	310	°C	ISO 12086

可燃性	额定值	单位制	测试方法
极限氧指数	95	%	ASTM D2863

注射	额定值	单位制
加工（熔体）温度	250 到 400	°C