PFA美国3M 8502 高粘度 耐化学 低残留 挤出级 管材应用

PFA塑料为少量全氟丙基全氟乙烯基醚与聚四氟乙烯的共聚物。熔融粘结性增强，溶体粘度下降，而性能与聚四氟乙烯相比无变化。此种树脂可以直接采用普通热塑性成型方法加工成制品。适于制作耐腐蚀件，减磨耐磨件、密封件、绝缘件和医疗器械零件，高温电线、电缆绝缘层，防腐设备、密封材料、泵阀衬套，和化学容器。

3M? Dyneon? Fluoroplastic PFA FLEX8502UHPZ

全氟烷氧基

3M Advanced Materials Division

产品说明：

3M? Dyneon? Ultra High Purity PFA FLEX8502UHPZ family exhibits improved environmental stress crack resistance (ESCR) to stress cracking chemicals or such agents that specifically contain fluorosurfactants. In addition, this family offers very low levels of extractable ions, makingit suitable for critical wet chemical processes in the semiconductor industry.
Features

• Significantly longer life in fluorosurfactant containing fluids

• Extremely low level of extractable ions

• Smoother surfaces

• Improved clarity

• Improved flexibility

• Service temperature range up to 240 °C

• Extreme stress crack resistance

3M? Dyneon? Fluoroplastic PFA FLEX8502UHPZ 物性表

基本信息
特性	Low (to None) Ion Content 纯度高 低萃取物 高 ESCR（抗应力开裂）
形式	粒子
加工方法	吹塑成型 树脂传递成型 压缩模塑

物理性能	额定值	单位制	测试方法
密度	2.15	g/cm3	ISO 12086
熔流率（熔体流动速率）(372°C/5.0 kg)	2.0	g/10 min	ISO 1133

硬度	额定值	单位制	测试方法
肖氏硬度(邵氏 D)	60	ASTM D2240, ISO 868

机械性能	额定值	单位制	测试方法
拉伸应力(断裂, 23°C)	35.0	MPa	ISO 527-1
拉伸应变(断裂, 23°C)	330	%	ISO 527-1
弯曲模量	600	MPa	ASTM D790

热性能	额定值	单位制	测试方法
熔融温度	300	°C	ISO 12086

可燃性	额定值	单位制	测试方法
极限氧指数	95	%	ASTM D2863