PFA塑料为少量全氟丙基全氟乙烯基醚与聚四氟乙烯的共聚物。熔融粘结性增强，溶体粘度下降，而性能与聚四氟乙烯相比无变化。此种树脂可以直接采用普通热塑性成型方法加工成制品。适于制作耐腐蚀件，减磨耐磨件、密封件、绝缘件和医疗器械零件，高温电线、电缆绝缘层，防腐设备、密封材料、泵阀衬套，和化学容器。

3M? Dyneon? Fluoroplastic PFA 6502TZ

全氟烷氧基

3M Advanced Materials Division

产品说明：

3M? Dyneon? Fluoroplastic PFA 6502TZ is a fully fluorinated copolymer of TFE PPVE. The resin has been developed for the transfer molding and extrusion of claddings and linings. The easier processing under low shear rates was one goal and also 3M? Dyneon? PFA 6502T Z Fluorothermoplastic was designed to be used in roughest environments, e. g. in the chemical industry, where high strength and extreme thermal and chemical resistance are required.
Features

• Broad processing window

• Improved mold release property

• Improved stress crack resistance

• Smooth surfaces

• High transparency

• Process targets: Transfer molding and extrusion

3M? Dyneon? Fluoroplastic PFA 6502TZ 物性表

• 基本信息
  特性	高强度 共聚物 耐化学性良好 耐热性，高 清晰度，高 脱模性能良好
  用途	衬里
  形式	粒子
  加工方法	吹塑成型 挤出 树脂传递成型 压缩模塑

  物理性能	额定值	单位制	测试方法
  密度	2.15	g/cm3	ISO 12086
  熔流率（熔体流动速率）(372°C/5.0 kg)	2.0	g/10 min	ISO 1133

  硬度	额定值	单位制	测试方法
  肖氏硬度(邵氏 D)	60	ASTM D2240, ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸应力(断裂, 23°C)	30.0	MPa	ISO 527-1
  拉伸应变(断裂, 23°C)	400	%	ISO 527-1
  弯曲模量	550	MPa	ASTM D790

  热性能	额定值	单位制	测试方法
  熔融温度	310	°C	ISO 12086

  可燃性	额定值	单位制	测试方法
  极限氧指数	95	%	ASTM D2863