PFA美国3M 8515 注塑级 耐化学 低残留

PFA塑料为少量全氟丙基全氟乙烯基醚与聚四氟乙烯的共聚物。熔融粘结性增强，溶体粘度下降，而性能与聚四氟乙烯相比无变化。此种树脂可以直接采用普通热塑性成型方法加工成制品。适于制作耐腐蚀件，减磨耐磨件、密封件、绝缘件和医疗器械零件，高温电线、电缆绝缘层，防腐设备、密封材料、泵阀衬套，和化学容器。

3M? Dyneon? Fluoroplastic PFA FLEX8515UHPZ

全氟烷氧基

3M Advanced Materials Division

产品说明：

3M? Dyneon? Ultra High Purity PFA FLEX8515UHPZ family exhibits improved environmental stress crack resistance (ESCR) to stress cracking chemicals or such agents that specifically contain fluorosurfactants. In addition, this family offers very low levels of extractable ions, making it suitable for critical wet chemical processes in the semiconductor industry.
Features

• Significantly longer life in fluorosurfactant containing fluids

• Extremely low level of extractable ions

• Smoother surfaces

• Improved clarity

• Improved flexibility

• Service temperature range up to 240 °C

• Extreme stress crack resistance

3M? Dyneon? Fluoroplastic PFA FLEX8515UHPZ 物性表

基本信息
特性	Low (to None) Ion Content 纯度高 低萃取物 高 ESCR（抗应力开裂）
用途	电线电缆应用
形式	粒子
加工方法	电线线缆挤出成型 注射成型

物理性能	额定值	单位制	测试方法
密度	2.15	g/cm3	ISO 12086
熔流率（熔体流动速率）(372°C/5.0 kg)	15	g/10 min	ISO 1133

硬度	额定值	单位制	测试方法
肖氏硬度(邵氏 D)	60	ASTM D2240, ISO 868

机械性能	额定值	单位制	测试方法
拉伸应力(断裂, 23°C)	35.0	MPa	ISO 527-1
拉伸应变(断裂, 23°C)	330	%	ISO 527-1
弯曲模量	600	MPa	ASTM D790

热性能	额定值	单位制	测试方法
熔融温度	290	°C	ISO 12086

可燃性	额定值	单位制	测试方法
极限氧指数	95	%	ASTM D2863

注射	额定值	单位制
加工（熔体）温度	340 到 370	°C

挤出	额定值	单位制
熔体温度	340 到 370	°C