PVDF美国3M 31008 注塑级 耐化学 耐酸碱 耐磨损。
3M Dyneon? PVDF 31008/0003 Polyvinylidene Fluoride
Polymer,Thermoplastic,Fluoropolymer,PVDF
3M
产品说明:
3M? Dyneon? PVDF 31008/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 31008/0003 also has a very low brittleness temperature, for excellent low temperature performance. This material is ideal for insulation and buffering materials for many wire and cable applications and for tubing. PVDF 31008/0003 has excellent flame and smoke performance, with an LOI of 60. PVDF 31008/0003 is designed for high speed extrusion, and can be processed using a variety of conventional thermoplastic conversion techniques. As with all PVDF grades, PVDF 31008/0003 also possesses very good chemical and temperature resistance.
- Copolymer of VF2 and CTFE
- Ultra-flexible
- Very low shrinkage rates
- Wide operating temperature window
- Processable using a variety of thermoplastic conversation techniques
- Excellent low flame and low smoke performance
Information provided by Dyneon, A 3M Company
3M Dyneon? PVDF 31008/0003 Polyvinylidene Fluoride 物性表
物理性能
额定值 (公制)
额定值 (英制)
测试方法
密度
1.76 g/cc
0.0636 lb/in3
ISO 1183
吸水率
= 0.040 %
= 0.040 %
24 hr @ 23°C; ISO 62 (method 1)
Melt Index of Compound
5.0 g/10 min
@Load 2.16 kg, Temperature 230 °C
5.0 g/10 min
@Load 4.76 lb, Temperature 446 °F
ASTM D1238
15 g/10 min
@Load 5.00 kg, Temperature 230 °C
15 g/10 min
@Load 11.0 lb, Temperature 446 °F
ASTM D1238
机械性能
额定值 (公制)
额定值 (英制)
测试方法
抗张强度(断裂)
56.0 MPa
8120 psi
50mm/min; ASTM D638
伸长率 (断裂)
630 %
630 %
50mm/min; ASTM D638
弯曲模量
0.800 GPa
116 ksi
2mm/min; ASTM D790
电气性能
额定值 (公制)
额定值 (英制)
测试方法
体积电阻率
= 1.00e+14 ohm-cm
= 1.00e+14 ohm-cm
10 mA, after 2 min; ASTM D257
表面电阻率
= 1.00e+14 ohm
= 1.00e+14 ohm
1V after 2 min - 500 V; ASTM D257
介电常数
7.0
@Frequency 1e+6 Hz
7.0
@Frequency 1e+6 Hz
ASTM D150
热性能
额定值 (公制)
额定值 (英制)
测试方法
熔融温度
168 °C
334 °F
ASTM D3418
脆化温度
-30.0 °C
-22.0 °F
ASTM D746A
可燃性(UL94)
V-0
V-0
极限氧指数
= 65 %
@Thickness 3.00 mm
= 65 %
@Thickness 0.118 in
Sheet; ASTM D2863
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | 1.76 g/cc | 0.0636 lb/in3 | ISO 1183 |
吸水率 | = 0.040 % | = 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) |
Melt Index of Compound | 5.0 g/10 min
@Load 2.16 kg, Temperature 230 °C
|
5.0 g/10 min
@Load 4.76 lb, Temperature 446 °F
|
ASTM D1238 |
15 g/10 min
@Load 5.00 kg, Temperature 230 °C
|
15 g/10 min
@Load 11.0 lb, Temperature 446 °F
|
ASTM D1238 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(断裂) | 56.0 MPa | 8120 psi | 50mm/min; ASTM D638 |
伸长率 (断裂) | 630 % | 630 % | 50mm/min; ASTM D638 |
弯曲模量 | 0.800 GPa | 116 ksi | 2mm/min; ASTM D790 |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
体积电阻率 | = 1.00e+14 ohm-cm | = 1.00e+14 ohm-cm | 10 mA, after 2 min; ASTM D257 |
表面电阻率 | = 1.00e+14 ohm | = 1.00e+14 ohm | 1V after 2 min - 500 V; ASTM D257 |
介电常数 | 7.0
@Frequency 1e+6 Hz
|
7.0
@Frequency 1e+6 Hz
|
ASTM D150 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
熔融温度 | 168 °C | 334 °F | ASTM D3418 |
脆化温度 | -30.0 °C | -22.0 °F | ASTM D746A |
可燃性(UL94) | V-0 | V-0 | |
极限氧指数 | = 65 %
@Thickness 3.00 mm
|
= 65 %
@Thickness 0.118 in
|
Sheet; ASTM D2863 |