上海汇堡材料科技有限公司
KetaSpire? KT-880UFP
聚醚醚酮
Solvay Specialty Polymers
产品说明：
KetaSpire? KT-880UFP is the high flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-colored, ultra-fine powder form. This ultra-fine PEEK powder is suitable for water borne coatings, electrostatically driven powder coatings, and resin pre-impregnation of continuous fiber composites. This ultra fine powder is produced to a median particle size D50 of about 10 micrometers.
KetaSpire? PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent chemical resistance to acids, bases and a broad range of aggressive organic chemicals, best in class fatigue resistance, high thermal resistance, high purity and ease of melt processing.
These properties make KT-880UFP well-suited for applications in health care, transportation, electronics, chemical processing and other industrial uses.
The resin is also available in a natural-colored pellet form under the grade name KT-880 NT for injection molding applications.
KetaSpire? PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent chemical resistance to acids, bases and a broad range of aggressive organic chemicals, best in class fatigue resistance, high thermal resistance, high purity and ease of melt processing.
These properties make KT-880UFP well-suited for applications in health care, transportation, electronics, chemical processing and other industrial uses.
The resin is also available in a natural-colored pellet form under the grade name KT-880 NT for injection molding applications.
KetaSpire? KT-880UFP 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.30 | g/cm3 | ASTM D792 |
| 吸水率(24 hr) | 0.10 | % | ASTM D570 |
| 颗粒大小 | |||
| D50 | 10.0 | μm | |
| D90 | 15.0 | μm | |
| D99 | 22.0 | μm |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 3650 | MPa | ASTM D638 |
| 抗张强度 | 100 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服 | 5.2 | % | ASTM D638 |
| 断裂1 | 10 到 20 | % | ASTM D638 |
| 弯曲模量 | 3790 | MPa | ASTM D790 |
| 弯曲强度 | 153 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 53 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 | 无断裂 | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa, 未退火) | 160 | °C | ASTM D648 |
| 玻璃转化温度 | 147 | °C | ASTM D3417 |
| 熔融温度 | 343 | °C | ASTM D3417 |
| 线形热膨胀系数 - 流动(-50 到 50°C) | 5.0E-5 | cm/cm/°C | ASTM E831 |
| 注射说明 |
|---|
| Back Pressure: minimum |
| 备注 | |
|---|---|
| 1 . | Tensile test speed = 2 in/min (50 mm/min) |