KetaSpire? KT-880 GF30

KetaSpire? KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire? PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C.

KetaSpire? PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.

These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.

• Beige: KT-880 GF30 BG 20

• Black: KT-880 GF30 BK 95
  KetaSpire? KT-880 GF30 物性表

  基本信息
  黄卡编号
  填料/增强材料
  特性
  用途
  机构评级
  RoHS 合规性
  外观
  形式
  加工方法

  物理性能	干燥	调节后的	单位制	测试方法
  比重	1.53	1.53	g/cm3	ASTM D792
  熔流率（熔体流动速率）(400°C/2.16 kg)	14	14	g/10 min	ASTM D1238
  收缩率1				ASTM D955
  流动 : 3.18 mm	0.10 到 0.30	0.10 到 0.30	%	ASTM D955
  横向流动 : 3.18 mm	1.3 到 1.5	1.3 到 1.5	%	ASTM D955
  吸水率(24 hr)	0.10	0.10	%	ASTM D570

  硬度	干燥	调节后的	单位制	测试方法
  洛氏硬度(M 级)	105	105		ASTM D785

  机械性能	干燥	调节后的	单位制	测试方法
  拉伸模量
  --2	10800	10800	MPa	ASTM D638
  --	11200	11200	MPa	ISO 527-2/1A/1
  拉伸应力
  屈服	174	174	MPa	ISO 527-2/1A/5
  --	162	162	MPa	ASTM D638
  伸长率
  断裂	2.8	2.8	%	ASTM D638
  断裂	2.8	2.8	%	ISO 527-2/1A/5
  弯曲模量
  --	10500	10500	MPa	ASTM D790
  --	10600	10600	MPa	ISO 178
  弯曲强度
  --	260	260	MPa	ASTM D790
  --	239	239	MPa	ISO 178
  压缩强度	183	183	MPa	ASTM D695
  剪切强度	94.4	94.4	MPa	ASTM D732

  冲击性能	干燥	调节后的	单位制	测试方法
  悬壁梁缺口冲击强度
  --	96	96	J/m	ASTM D256
  --	11	11	kJ/m2	ISO 180
  无缺口悬臂梁冲击
  --	850	850	J/m	ASTM D4812
  --	62	62	kJ/m2	ISO 180

  热性能	干燥	调节后的	单位制	测试方法
  载荷下热变形温度(1.8 MPa, 退火)	315	315	°C	ASTM D648
  玻璃转化温度	147	147	°C	ASTM D3418
  熔融峰值温度	343	343	°C	ASTM D3418
  线形热膨胀系数 - 流动(-50 到 50°C)	1.9E-5	1.9E-5	cm/cm/°C	ASTM E831
  比热				DSC
  50°C	1280	1280	J/kg/°C	DSC
  200°C	1700	1700	J/kg/°C	DSC
  导热系数	0.30	0.30	W/m/K	ASTM E1530

  电气性能	干燥	调节后的	单位制	测试方法
  表面电阻率	1.9E 17	1.9E 17	ohms	ASTM D257
  体积电阻率	3.8E 17	3.8E 17	ohms·cm	ASTM D257
  介电强度(3.00 mm)	16	16	kV/mm	ASTM D149
  介电常数				ASTM D150
  60 Hz	3.53	3.53		ASTM D150
  1 kHz	3.53	3.53		ASTM D150
  1 MHz	3.49	3.49		ASTM D150
  耗散因数				ASTM D150
  60 Hz	2.0E-3	2.0E-3		ASTM D150
  1 kHz	2.0E-3	2.0E-3		ASTM D150
  1 MHz	4.0E-3	4.0E-3		ASTM D150

  可燃性	干燥	调节后的	单位制	测试方法
  UL 阻燃等级				UL 94
  0.800 mm	V-0	V-0		UL 94
  1.60 mm	V-0	V-0		UL 94

  充模分析	干燥	调节后的	单位制	测试方法
  熔体粘度(400°C, 1000 sec^-1)	350	350	Pa·s	ASTM D3835

  注射	干燥	单位制
  干燥温度	150	°C
  干燥时间	4.0	hr
  料筒后部温度	365	°C
  料筒中部温度	371	°C
  料筒前部温度	377	°C
  射嘴温度	382	°C
  模具温度	177 到 204	°C
  注射速度	快速
  螺杆压缩比	2.5:1.0 到 3.5:1.0

  备注
  1 .	5" x 0.5" x 0.125"
  2 .	5.0 mm/min

• 机器加工
• 型材挤出成型
• 注射成型
• 粒子
• 浅米色
• RoHS 合规
• FAA FAR 25.853a3
• ISO 10993
• ISO 10993-第一部分
• 薄膜
• 泵件
• 电气/电子应用领域
• 飞机应用
• 工业应用
• 连接器
• 密封件
• 石油/天然气用品
• 外科器械
• 牙齿应用领域
• 医疗/护理用品
• 医疗器材
• 医疗器械
• 尺寸稳定性良好
• 电子束消毒
• 放射性可透的
• 辐射消毒
• 刚性，高
• 高强度
• 高压锅消毒
• 好的消毒性
• 环氧乙烷消毒
• 抗伽马辐射
• 流动性高
• 耐化学性良好
• 耐疲劳性能
• 耐热性，高
• 耐蒸汽
• 热消毒
• 生物兼容性
• 用蒸汽消毒
• 阻燃性
• 玻璃纤维增强材料, 30% 填料按重量
• E140728-100211985