东莞市广源新材料科技有限公司
PTFE美国3M TFM1700 PTFE细粉 电气机械性能良好 绝缘薄膜应用
3M Dyneon? TFM? 1700 PTFE
Polymer,Thermoplastic,Fluoropolymer,PTFE
3M Dyneon?
产品说明:
- Meets ASTM D4894 Type III, Grade 1 resin
- Non-free-flowing compression molding powder
- Very fine particle size
- Dense polymer structure, low permeability
- Improved weldability
- Low deformation under load
- Good electrical and mechanical properties
- Increased modulus of elasticity
- Low molding pressure
- Excellent for production of very thin films with superior permeation properties
Information provided by Dyneon, A 3M Company
3M Dyneon? TFM? 1700 PTFE 物性表
物理性能
额定值 (公制)
额定值 (英制)
测试方法
比重
2.16 g/cc
2.16 g/cc
@ 23°C, Sintering Molding; ASTM D4894-98a
体积密度
0.420 g/cc
0.0152 lb/in3
ASTM D4894-98a
粒径
25 μm
25 μm
average; ASTM D4894-98a
变形
4.0 %
4.0 %
2175 psi - permanent, 23°C, Sintering Molding; ASTM D621
8.0 %
8.0 %
2175 psi - 24 hrs, 23°C, Sintering Molding; ASTM D621
9.0 %
9.0 %
2175 psi - 100 hrs, 23°C, Sintering Molding; ASTM D621
机械性能
额定值 (公制)
额定值 (英制)
测试方法
抗张强度(断裂)
33.1 MPa
4800 psi
Sintered Molding; ASTM D4894-98a
伸长率 (断裂)
450 %
450 %
Sintered Molding; ASTM D4894-98a
拉伸模量
0.6498 GPa
94.25 ksi
Sintered Molding; ASTM D638
电气性能
额定值 (公制)
额定值 (英制)
测试方法
介电强度
146 kV/mm
3710 kV/in
ASTM D149-95a
热性能
额定值 (公制)
额定值 (英制)
测试方法
熔融温度
317 - 337 °C
603 - 639 °F
second; ASTM D4894-98a
332 - 352 °C
630 - 666 °F
initial; ASTM D4894-98a
最高工作温度, Air
260 °C
500 °F
最低工作温度, Air
-200 °C
-330 °F
可燃性(UL94)
V-0
V-0
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 2.16 g/cc | 2.16 g/cc | @ 23°C, Sintering Molding; ASTM D4894-98a |
| 体积密度 | 0.420 g/cc | 0.0152 lb/in3 | ASTM D4894-98a |
| 粒径 | 25 μm | 25 μm | average; ASTM D4894-98a |
| 变形 | 4.0 % | 4.0 % | 2175 psi - permanent, 23°C, Sintering Molding; ASTM D621 |
| 8.0 % | 8.0 % | 2175 psi - 24 hrs, 23°C, Sintering Molding; ASTM D621 | |
| 9.0 % | 9.0 % | 2175 psi - 100 hrs, 23°C, Sintering Molding; ASTM D621 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 33.1 MPa | 4800 psi | Sintered Molding; ASTM D4894-98a |
| 伸长率 (断裂) | 450 % | 450 % | Sintered Molding; ASTM D4894-98a |
| 拉伸模量 | 0.6498 GPa | 94.25 ksi | Sintered Molding; ASTM D638 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电强度 | 146 kV/mm | 3710 kV/in | ASTM D149-95a |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 317 - 337 °C | 603 - 639 °F | second; ASTM D4894-98a |
| 332 - 352 °C | 630 - 666 °F | initial; ASTM D4894-98a | |
| 最高工作温度, Air | 260 °C | 500 °F | |
| 最低工作温度, Air | -200 °C | -330 °F | |
| 可燃性(UL94) | V-0 | V-0 |