广州金丰塑胶原料有限公司
PA66 美国杜邦 10B40 矿物增强 PA66 聚酰胺
原料物性：
DuPont Performance Polymers Minlon? 10B40HS1 BK061 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.51 g/cc | 1.51 g/cc | DAM; ASTM D792 |
| 密度 | 1.51 g/cc | 0.0546 lb/in3 | DAM; ISO 1183 |
| 填料含量 | 40 % | 40 % | DAM |
| 线性成型收缩率 | 0.0040 cm/cm
@Thickness 1.60 mm
|
0.0040 in/in
@Thickness 0.0630 in
|
Flow; DAM |
| 0.0040 cm/cm
@Thickness 3.20 mm
|
0.0040 in/in
@Thickness 0.126 in
|
Flow; DAM | |
| 0.0060 cm/cm
@Thickness 6.40 mm
|
0.0060 in/in
@Thickness 0.252 in
|
Flow; DAM | |
| 0.0090 cm/cm
@Thickness 1.60 mm
|
0.0090 in/in
@Thickness 0.0630 in
|
Transverse; DAM | |
| 0.0090 cm/cm
@Thickness 3.20 mm
|
0.0090 in/in
@Thickness 0.126 in
|
Transverse; DAM | |
| 0.011 cm/cm
@Thickness 6.40 mm
|
0.011 in/in
@Thickness 0.252 in
|
Transverse; DAM | |
| 线性成型收缩率,Flow | 0.0040 cm/cm
@Thickness 2.00 mm
|
0.0040 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.0090 cm/cm
@Thickness 2.00 mm
|
0.0090 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 95.0 MPa
@Temperature 23.0 °C
|
13800 psi
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 抗张强度 | 87.0 MPa
@Temperature 23.0 °C
|
12600 psi
@Temperature 73.4 °F
|
DAM; ASTM D638 |
| 伸长率 (断裂) | 2.5 %
@Temperature 23.0 °C
|
2.5 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 2.5 %
@Temperature 23.0 °C
|
2.5 %
@Temperature 73.4 °F
|
DAM; ASTM D638 | |
| 拉伸模量 | 10.0 GPa
@Temperature 23.0 °C
|
1450 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 弯曲强度 | 148 MPa
@Temperature 23.0 °C
|
21500 psi
@Temperature 73.4 °F
|
DAM; ASTM D790 |
| 弯曲模量 | 8.62 GPa
@Temperature 23.0 °C
|
1250 ksi
@Temperature 73.4 °F
|
DAM; ASTM D790 |
| 9.50 GPa
@Temperature 23.0 °C
|
1380 ksi
@Temperature 73.4 °F
|
DAM; ISO 178 | |
| 悬壁梁缺口冲击强度 | 0.320 J/cm
@Temperature 23.0 °C
|
0.599 ft-lb/in
@Temperature 73.4 °F
|
DAM; ASTM D256 |
| 悬壁梁无缺口冲击强度 | 3.20 J/cm
@Temperature 23.0 °C
|
5.99 ft-lb/in
@Temperature 73.4 °F
|
DAM; ASTM D4812 |
| 悬壁梁缺口冲击强度 | 2.50 kJ/m2
@Temperature -40.0 °C
|
1.19 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 180/1A |
| 3.50 kJ/m2
@Temperature 23.0 °C
|
1.67 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 180/1A | |
| 简支梁缺口冲击强度 | 0.200 J/cm2
@Temperature -40.0 °C
|
0.952 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 179/1eA |
| 0.300 J/cm2
@Temperature 23.0 °C
|
1.43 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 500 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
278 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ASTM E 831 |
| 500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ASTM E 831 | |
| 500 μm/m-°C
@Temperature 55.0 - 160 °C
|
278 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ASTM E 831 | |
| 500 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
278 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ISO 11359-1/-2 | |
| 500 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 500 μm/m-°C
@Temperature 55.0 - 160 °C
|
278 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ISO 11359-1/-2 | |
| 线性热膨胀系数,横向流动 | 53.0 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
29.4 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ISO 11359-1/-2 |
| 53.0 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
29.4 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ASTM E 831 | |
| 66.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
36.7 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 66.0 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
36.7 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ASTM E 831 | |
| 110 μm/m-°C
@Temperature 55.0 - 160 °C
|
61.1 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ISO 11359-1/-2 | |
| 110 μm/m-°C
@Temperature 55.0 - 160 °C
|
61.1 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ASTM E 831 | |
| 熔融温度 | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 263 °C | 505 °F | DAM; ASTM D3418 | |
| 载荷下热变形温度(1.8 MPa) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| 210 °C | 410 °F | DAM; ASTM D648 | |
| 可燃性(UL94) | HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
DAM; IEC 60695-11-10 |
| HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; IEC 60695-11-10 | |
| HB
@Thickness 0.710 mm
|
HB
@Thickness 0.0280 in
|
DAM; IEC 60695-11-10 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 295 °C | 563 °F | DAM; Optimum |
| 285 - 305 °C | 545 - 581 °F | DAM | |
| 模具温度 | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| 干燥温度 | 80.0 °C | 176 °F | DAM |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| 水分含量 | = 0.20 % | = 0.20 % | DAM |
| 材料描述 | 测试方法 | |
|---|---|---|
| 添加剂 | Heat Stabilizer | DAM |
| 外观 | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| 特性 | Warpage, Low | DAM |
| Filler | Mineral filler | DAM |
| 形式 | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Heat Stabilized | Yes | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | PA66-MD40 | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Low Warp Resins | DAM |
| Mineral Reinforced Resins | DAM | |
| 树脂识别 | PA66-MD40 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
| 用途 | Appliance Components | DAM |
| Automotive Applications | DAM | |
| Gears | DAM | |
| Industrial Applications | DAM | |
| Parts, Engineering | DAM |
PA66自具特性：
A、具高抗张强度；
B、耐韧、耐冲击性特优；
C、自润性、耐磨性佳、耐药品性优；
D、低温特性佳；
E、具自熄性；
PA66主要用途：
广泛应用于电子电器，仪器仪表、家电、通讯、汽车部件、纺机、体育休闲用品、电子电气、铁路、油管、油箱、医疗机械、及一些精密工程制品。
工业零件：电脑座、椅座、轮框、溜冰鞋 底座、纺织梭、踏板、滑轮 。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车：油箱盖、 散热风扇、门把、进气隔栅、水箱护盖、灯座
纯树脂PA, 防静电PA，导电PA，加纤防火PA，抗紫外线耐候PA，耐高温PA，挤出PA
防火PA， 耐寒PA,
PA66美国杜邦牌号太多就没有一一例出，上面如果没有你要找的型号请联系我们的塑料专员一三七 九零二一 九八九二 有专员专惠
PA66尼龙66的加工流程与注意事项：
干燥处理：如果加工前材料是密封的，那么就没有必要干燥。然而，如果储存容器被打开，那么建议在85C的热空气中干燥处理。如果湿度大于0.2%，还需要进行105C，12小时的真空干燥。
熔化温度：260~290C。对玻璃添加剂的产品为275~280C。熔化温度应避免高于300C。
模具温度：建议80C。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于
薄壁塑件，如果使用低于40C的模具温度，则塑件的结晶度将随着时间而变化，为了保持
塑件的几何稳定性，需要进行退火处理。
注射压力：通常在750~1250bar，取决于材料和产品设计。.
注射速度：高速（对于增强型材料应稍低一些）。
流道和浇口:
由于PA66的凝固时间很短，因此浇口的位置非常重要。浇口孔径不要小于0.5*t
（这里t为塑件厚度）。如果使用热流道，浇口尺寸应比使用常规流道小一些，
因为热流道能够帮助阻止材料过早凝固。如果用潜入式浇口，浇口的直径
应当是0.75mm。喂料区 60～90℃（80℃）
区2 260～290℃（280℃）
区4 280～290℃（290℃）
喷嘴 280～290℃（290℃）括号内的温度建议作为基本设定值，行程利用率为35%和65%，模件流长与壁厚之比为50：1到100：1
注射压力：100～160MPa（1000～1600bar），如果是加工薄截面长流道制品（如电线扎带），则需要达到180MPa（1800bar）
背压：2～8MPa（20～80bar），需要准确调节，因为背压太高会造成塑化不均注射速度建议采用相对较快的注射速度；模具有好的通气性否则制品上易出现焦化现象
计量行程 （0.5～3.5）D
预烘干 在80℃温度下烘干4h，除了直接从装料容器内喂料；尼龙有水性，应该保存在防潮容器内和封闭的料斗内；水含量超过0.25%就会造成成型改变
PA66塑胶原料收缩率：0.7%～2.0%，或者加了30%的玻璃纤维，为0.4%～0.7%；如果提供的温度超过60℃，制品应该为逐渐冷却；逐渐冷却可降低成型后收缩，即制品表现为更好地尺寸稳定性和小的内应力；建议采用蒸气法；尼龙制品可以通过熔液焊剂来检查应力
机器停工时段 无需用其它料清洗；熔料残留在料筒内时间可达20min，此后热降解容易发生
尼龙66分类：
增强PA，防火PA，超韧PA，抗紫外线，耐候PA，防静电PA，导电PA，加纤增强防火PA，高温挤出级PA。
PA66在成型后仍然具有湿性，其程度主要取决于材料的组成、壁厚以及环境条件。在产品设计时，一定要考虑湿性对几何稳定性的影响。
尼龙66 优点：
典型应用范围:
分类：防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
PA66特性：
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有湿性，其程度主要取决于材料的组成壁