DuPont Performance Polymers Minlon? 10B140 BK061 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.50 g/cc | 0.0542 lb/in3 | DAM; ISO 1183 |
| 填料含量 | 40 % | 40 % | DAM |
| Water Absorption | 1.6 %
@Temperature 23.0 °C
|
1.6 %
@Temperature 73.4 °F
|
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 5.0 %
@Temperature 23.0 °C
|
5.0 %
@Temperature 73.4 °F
|
Saturation, immersed; DAM; ISO 62, Similar to |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 54.0 MPa
@Temperature 23.0 °C
|
7830 psi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 82.0 MPa
@Temperature 23.0 °C
|
11900 psi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 伸长率 (断裂) | 3.5 %
@Temperature 23.0 °C
|
3.5 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 9.0 %
@Temperature 23.0 °C
|
9.0 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 拉伸模量 | 3.80 GPa
@Temperature 23.0 °C
|
551 ksi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 6.60 GPa
@Temperature 23.0 °C
|
957 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 悬壁梁缺口冲击强度 | 3.50 kJ/m2
@Temperature 23.0 °C
|
1.67 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 180/1A |
| 4.00 kJ/m2
@Temperature 23.0 °C
|
1.90 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 180/1A | |
| 简支梁无缺口冲击强度 | 3.50 J/cm2
@Temperature 23.0 °C
|
16.7 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eU |
| 6.00 J/cm2
@Temperature 23.0 °C
|
28.6 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.350 J/cm2
@Temperature 23.0 °C
|
1.67 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA |
| 0.450 J/cm2
@Temperature 23.0 °C
|
2.14 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 相比耐漏电起痕指数(CTI) | = 600 V
@Temperature 23.0 °C
|
= 600 V
@Temperature 73.4 °F
|
DAM; UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 240 °C | 464 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 170 °C | 338 °F | DAM; ISO 75-1/-2 |
| UL RTI | 105 °C
@Thickness 0.710 mm
|
221 °F
@Thickness 0.0280 in
|
DAM; UL 746B |
| 120 °C
@Thickness 3.00 mm
|
248 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
| 120 °C
@Thickness 1.50 mm
|
248 °F
@Thickness 0.0591 in
|
DAM; UL 746B | |
| UL RTI，机械冲击 | 65.0 °C
@Thickness 0.710 mm
|
149 °F
@Thickness 0.0280 in
|
DAM; UL 746B |
| 105 °C
@Thickness 1.50 mm
|
221 °F
@Thickness 0.0591 in
|
DAM; UL 746B | |
| 115 °C
@Thickness 3.00 mm
|
239 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
| UL RTI，机械无冲击 | 65.0 °C
@Thickness 0.710 mm
|
149 °F
@Thickness 0.0280 in
|
DAM; UL 746B |
| 115 °C
@Thickness 1.50 mm
|
239 °F
@Thickness 0.0591 in
|
DAM; UL 746B | |
| 115 °C
@Thickness 3.00 mm
|
239 °F
@Thickness 0.118 in
|
DAM; UL 746B | |
| 可燃性(UL94) | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; UL94 |
| HB
@Thickness 0.710 mm
|
HB
@Thickness 0.0280 in
|
DAM; UL94 | |
| HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
DAM; UL94 | |
| HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
DAM; IEC 60695-11-10 | |
| HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
DAM; IEC 60695-11-10 | |
| HB
@Thickness 0.710 mm
|
HB
@Thickness 0.0280 in
|
DAM; IEC 60695-11-10 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 285 - 305 °C | 545 - 581 °F | DAM |
| 295 °C | 563 °F | DAM; Optimum | |
| 模具温度 | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| 干燥温度 | 80.0 °C | 176 °F | DAM |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| 水分含量 | = 0.20 % | = 0.20 % | DAM |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | Black Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Filler | Mineral filler | DAM |
| 形式 | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | PA66-MD40 | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Low Warp Resins | DAM |
| Mineral Reinforced Resins | DAM | |
| Mineral Reinforced Resins | DAM | |
| 树脂识别 | PA66-MD40 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |
C、自润性、耐磨性佳、耐药品性优；
D、低温特性佳；
E、具自熄性；
PA66主要用途：
广泛应用于电子电器，仪器仪表、家电、通讯、汽车部件、纺机、体育休闲用品、电子电气、铁路、油管、油箱、医疗机械、及一些精密工程制品。
工业零件：电脑座、椅座、轮框、溜冰鞋 底座、纺织梭、踏板、滑轮 。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车：油箱盖、 散热风扇、门把、进气隔栅、水箱护盖、灯座
纯树脂PA, 防静电PA，导电PA，加纤防火PA，抗紫外线耐候PA，耐高温PA，挤出PA
防火PA， 耐寒PA,
PA66美国杜邦牌号太多就没有一一例出，上面如果没有你要找的型号请联系我们的塑料专员一三七 九零二一 九八九二 有专员专惠
PA66尼龙66的加工流程与注意事项：
干燥处理：如果加工前材料是密封的，那么就没有必要干燥。然而，如果储存容器被打开，那么建议在85C的热空气中干燥处理。如果湿度大于0.2%，还需要进行105C，12小时的真空干燥。
熔化温度：260~290C。对玻璃添加剂的产品为275~280C。熔化温度应避免高于300C。
模具温度：建议80C。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于
薄壁塑件，如果使用低于40C的模具温度，则塑件的结晶度将随着时间而变化，为了保持
塑件的几何稳定性，需要进行退火处理。
注射压力：通常在750~1250bar，取决于材料和产品设计。.
注射速度：高速（对于增强型材料应稍低一些）。
流道和浇口:
由于PA66的凝固时间很短，因此浇口的位置非常重要。浇口孔径不要小于0.5*t
（这里t为塑件厚度）。如果使用热流道，浇口尺寸应比使用常规流道小一些，
因为热流道能够帮助阻止材料过早凝固。如果用潜入式浇口，浇口的直径
应当是0.75mm。喂料区 60～90℃（80℃）
区2 260～290℃（280℃）
区4 280～290℃（290℃）
PA66塑胶原料收缩率：0.7%～2.0%，或者加了30%的玻璃纤维，为0.4%～0.7%；如果提供的温度超过60℃，制品应该为逐渐冷却；逐渐冷却可降低成型后收缩，即制品表现为更好地尺寸稳定性和小的内应力；建议采用蒸气法；尼龙制品可以通过熔液焊剂来检查应力
机器停工时段 无需用其它料清洗；熔料残留在料筒内时间可达20min，此后热降解容易发生
尼龙66分类：
增强PA，防火PA，超韧PA，抗紫外线，耐候PA，防静电PA，导电PA，加纤增强防火PA，高温挤出级PA。
特性：
PA66在成型后仍然具有湿性，其程度主要取决于材料的组成、壁厚以及环境条件。在产品设计时，一定要考虑湿性对几何稳定性的影响。
尼龙66 优点：
典型应用范围:
分类：防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
PA66特性：
2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有湿性，其程度主要取决于材料的组成壁