DuPont Performance Polymers Zytel? 103HSL NC010 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 0.980 g/cc | 0.0354 lb/in3 | |
| 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 | |
| 吸水率 | 8.5 %
@Thickness 2.00 mm
|
8.5 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 水分吸收 | 2.60 %
@Thickness 2.00 mm
|
2.60 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 粘度 | 43970 cP
@Shear Rate 5000 1/s, Temperature 300 °C
|
43970 cP
@Shear Rate 5000 1/s, Temperature 572 °F
|
ISO 11403-1 -2 |
| 51430 cP
@Shear Rate 5000 1/s, Temperature 290 °C
|
51430 cP
@Shear Rate 5000 1/s, Temperature 554 °F
|
ISO 11403-1 -2 | |
| 60010 cP
@Shear Rate 5000 1/s, Temperature 280 °C
|
60010 cP
@Shear Rate 5000 1/s, Temperature 536 °F
|
ISO 11403-1 -2 | |
| 100000 cP
@Shear Rate 500 1/s, Temperature 300 °C
|
100000 cP
@Shear Rate 500 1/s, Temperature 572 °F
|
ISO 11403-1 -2 | |
| 134100 cP
@Shear Rate 500 1/s, Temperature 290 °C
|
134100 cP
@Shear Rate 500 1/s, Temperature 554 °F
|
ISO 11403-1 -2 | |
| 180250 cP
@Shear Rate 500 1/s, Temperature 280 °C
|
180250 cP
@Shear Rate 500 1/s, Temperature 536 °F
|
ISO 11403-1 -2 | |
| 粘度测试 | 136 cm3/g | 136 cm3/g | DAM; formic acid 90%; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度 | 14.2 MPa
@Strain 4.71 %, Temperature 150 °C
|
2060 psi
@Strain 4.71 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 |
| 16.3 MPa
@Strain 3.83 %, Temperature 90.0 °C
|
2360 psi
@Strain 3.83 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 16.7 MPa
@Strain 0.530 %, Temperature 23.0 °C
|
2420 psi
@Strain 0.530 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 19.3 MPa
@Strain 4.60 %, Temperature 90.0 °C
|
2800 psi
@Strain 4.60 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 20.1 MPa
@Strain 3.43 %, Temperature 40.0 °C
|
2920 psi
@Strain 3.43 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 23.9 MPa
@Strain 18.8 %, Temperature 150 °C
|
3470 psi
@Strain 18.8 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 25.5 MPa
@Strain 33.0 %, Temperature 150 °C
|
3700 psi
@Strain 33.0 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 29.8 MPa
@Strain 3.02 %, Temperature 23.0 °C
|
4320 psi
@Strain 3.02 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 30.5 MPa
@Strain 14.3 %, Temperature 90.0 °C
|
4420 psi
@Strain 14.3 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 33.6 MPa
@Strain 25.2 %, Temperature 90.0 °C
|
4870 psi
@Strain 25.2 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 34.7 MPa
@Strain 17.4 %, Temperature 90.0 °C
|
5030 psi
@Strain 17.4 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 38.2 MPa
@Strain 30.2 %, Temperature 90.0 °C
|
5540 psi
@Strain 30.2 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 40.1 MPa
@Strain 12.7 %, Temperature 40.0 °C
|
5820 psi
@Strain 12.7 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 45.8 MPa
@Strain 22.0 %, Temperature 40.0 °C
|
6640 psi
@Strain 22.0 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 50.0 MPa
@Strain 11.9 %, Temperature 23.0 °C
|
7250 psi
@Strain 11.9 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 51.7 MPa
@Strain 3.40 %, Temperature 40.0 °C
|
7500 psi
@Strain 3.40 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 55.9 MPa
@Strain 1.93 %, Temperature 23.0 °C
|
8110 psi
@Strain 1.93 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 56.1 MPa
@Strain 20.4 %, Temperature 23.0 °C
|
8140 psi
@Strain 20.4 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 57.5 MPa
@Strain 29.2 %, Temperature 23.0 °C
|
8340 psi
@Strain 29.2 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 61.5 MPa
@Strain 10.3 %, Temperature 40.0 °C
|
8920 psi
@Strain 10.3 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 65.8 MPa
@Strain 17.9 %, Temperature 40.0 °C
|
9540 psi
@Strain 17.9 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 78.5 MPa
@Strain 3.39 %, Temperature 23.0 °C
|
11400 psi
@Strain 3.39 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 2.40 MPa
@Strain 0.444 %, Time 3.60e 6 sec
|
348 psi
@Strain 0.444 %, Time 1000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 2.40 MPa
@Strain 0.558 %, Time 3.60e 7 sec
|
348 psi
@Strain 0.558 %, Time 10000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 2.40 MPa
@Strain 0.261 %, Time 36000 sec
|
348 psi
@Strain 0.261 %, Time 10.0 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 2.40 MPa
@Strain 0.340 %, Time 360000 sec
|
348 psi
@Strain 0.340 %, Time 100 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 2.40 MPa
@Strain 0.202 %, Time 3600 sec
|
348 psi
@Strain 0.202 %, Time 1.00 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 9.60 MPa
@Strain 0.902 %, Time 3600 sec
|
1390 psi
@Strain 0.902 %, Time 1.00 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 9.60 MPa
@Strain 1.47 %, Time 360000 sec
|
1390 psi
@Strain 1.47 %, Time 100 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 9.60 MPa
@Strain 1.15 %, Time 36000 sec
|
1390 psi
@Strain 1.15 %, Time 10.0 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 9.60 MPa
@Strain 2.36 %, Time 3.60e 7 sec
|
1390 psi
@Strain 2.36 %, Time 10000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 9.60 MPa
@Strain 1.89 %, Time 3.60e 6 sec
|
1390 psi
@Strain 1.89 %, Time 1000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 19.2 MPa
@Strain 4.58 %, Time 3.60e 6 sec
|
2780 psi
@Strain 4.58 %, Time 1000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 19.2 MPa
@Time 3600 sec, Strain 2.49 %
|
2780 psi
@Time 1.00 hour, Strain 2.49 %
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 19.2 MPa
@Strain 3.04 %, Time 36000 sec
|
2780 psi
@Strain 3.04 %, Time 10.0 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 19.2 MPa
@Strain 5.50 %, Time 3.60e 7 sec
|
2780 psi
@Strain 5.50 %, Time 10000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 19.2 MPa
@Strain 3.73 %, Time 360000 sec
|
2780 psi
@Strain 3.73 %, Time 100 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
| 抗张强度(屈服) | 55.0 MPa | 7980 psi | 50%RH; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | 20 % | 20 % | DAM; Nominal; ISO 527-1/-2 |
| = 50 % | = 50 % | 50%RH; Nominal; ISO 527-1/-2 | |
| 屈服伸长率 | 4.5 % | 4.5 % | DAM; ISO 527-1/-2 |
| 4.5 % | 4.5 % | DAM; ISO 527-3 | |
| 25 % | 25 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 1.40 GPa | 203 ksi | 50%RH; ISO 527-1/-2 |
| 3.10 GPa | 450 ksi | DAM; ISO 527-1/-2 | |
| 弯曲模量 | 1.20 GPa | 174 ksi | 50%RH; ISO 178 |
| 2.80 GPa | 406 ksi | DAM; ISO 178 | |
| 剪切模量 | 0.1454 GPa
@Temperature 150 °C
|
21.09 ksi
@Temperature 302 °F
|
DAM; Dynamic; ISO 11403-1 -2 |
| 0.170 GPa
@Temperature 110 °C
|
24.7 ksi
@Temperature 230 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
| 0.5141 GPa
@Temperature 60.0 °C
|
74.57 ksi
@Temperature 140 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
| 0.963 GPa
@Temperature 10.0 °C
|
140 ksi
@Temperature 50.0 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
| 0.9984 GPa
@Temperature -20.0 °C
|
144.8 ksi
@Temperature -4.00 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
| 1.065 GPa
@Temperature -50.0 °C
|
154.5 ksi
@Temperature -58.0 °F
|
DAM; Dynamic; ISO 11403-1 -2 |
?