| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.08 g/cc | 0.0390 lb/in3 | DAM; ISO 1183 |
| 吸水率 | 1.17 %
@Temperature 23.0 °C
|
1.17 %
@Temperature 73.4 °F
|
DAM; Immersion 24h; ISO 62, Similar to |
| 1.9 %
@Thickness 1.00 mm, Temperature 23.0 °C
|
1.9 %
@Thickness 0.0394 in, Temperature 73.4 °F
|
DAM; Equilibrium 50%RH; ISO 62, Similar to | |
| 线性成型收缩率,Flow | 0.020 cm/cm
@Thickness 2.00 mm
|
0.020 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.018 cm/cm
@Thickness 2.00 mm
|
0.018 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | 110 | 110 | DAM; ISO 2039/2 |
| 抗张强度(断裂) | 45.0 MPa
@Temperature 23.0 °C
|
6530 psi
@Temperature 73.4 °F
|
DAM; 50mm/min; ISO 527 |
| 48.0 MPa
@Temperature 23.0 °C
|
6960 psi
@Temperature 73.4 °F
|
50%RH; 50mm/min; ISO 527 | |
| 抗张强度 | 48.0 MPa
@Strain 50.0 %, Temperature 23.0 °C
|
6960 psi
@Strain 50.0 %, Temperature 73.4 °F
|
50%RH; ISO 527 |
| 50.0 MPa
@Strain 50.0 %, Temperature 23.0 °C
|
7250 psi
@Strain 50.0 %, Temperature 73.4 °F
|
DAM; ISO 527 | |
| 抗张强度(屈服) | 35.5 MPa
@Temperature 23.0 °C
|
5150 psi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 49.0 MPa
@Temperature 23.0 °C
|
7110 psi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 伸长率 (断裂) | 44 %
@Temperature 23.0 °C
|
44 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| = 50 %
@Temperature 23.0 °C
|
= 50 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| = 50 %
@Temperature 23.0 °C
|
= 50 %
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| = 50 %
@Temperature 23.0 °C
|
= 50 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 74 %
@Temperature 23.0 °C
|
74 %
@Temperature 73.4 °F
|
DAM; 50mm/min; ISO 527 | |
| Elongation at Yield | 5.0 %
@Temperature 23.0 °C
|
5.0 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 26.5 %
@Temperature 23.0 °C
|
26.5 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 拉伸模量 | 0.775 GPa
@Temperature 23.0 °C
|
112 ksi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 1.90 GPa
@Temperature 23.0 °C
|
276 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 弯曲模量 | 0.728 GPa
@Temperature 23.0 °C
|
106 ksi
@Temperature 73.4 °F
|
50%RH; ISO 178 |
| 1.80 GPa
@Temperature 23.0 °C
|
261 ksi
@Temperature 73.4 °F
|
DAM; ISO 178 | |
| 悬壁梁缺口冲击强度 | 21.0 kJ/m2
@Temperature -40.0 °C
|
9.99 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 180/1A |
| 77.0 kJ/m2
@Temperature 23.0 °C
|
36.6 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | NB
@Temperature -30.0 °C
|
NB
@Temperature -22.0 °F
|
DAM; ISO 180/1U |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
DAM; ISO 180/1U | |
| 简支梁无缺口冲击强度 | 24.0 J/cm2
@Temperature -40.0 °C
|
114 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 179/1eU |
| 26.0 J/cm2
@Temperature 0.000 °C
|
124 ft-lb/in2
@Temperature 32.0 °F
|
DAM; ISO 179/1eU | |
| 30.0 J/cm2
@Temperature -20.0 °C
|
143 ft-lb/in2
@Temperature -4.00 °F
|
DAM; ISO 179/1eU | |
| NB
@Temperature -30.0 °C
|
NB
@Temperature -22.0 °F
|
DAM; ISO 179/1eU | |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
DAM; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 2.10 J/cm2
@Temperature -40.0 °C
|
9.99 ft-lb/in2
@Temperature -40.0 °F
|
DAM; ISO 179/1eA |
| 2.20 J/cm2
@Temperature -30.0 °C
|
10.5 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eA | |
| 2.20 J/cm2
@Temperature -20.0 °C
|
10.5 ft-lb/in2
@Temperature -4.00 °F
|
DAM; ISO 179/1eA | |
| 2.30 J/cm2
@Temperature -30.0 °C
|
10.9 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eA | |
| 3.60 J/cm2
@Temperature 0.000 °C
|
17.1 ft-lb/in2
@Temperature 32.0 °F
|
DAM; ISO 179/1eA | |
| 8.30 J/cm2
@Temperature 23.0 °C
|
39.5 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 2.40e 12 ohm-cm
@Temperature 23.0 °C
|
2.40e 12 ohm-cm
@Temperature 73.4 °F
|
50%RH; IEC 60093 |
| 2.50e 16 ohm-cm
@Temperature 23.0 °C
|
2.50e 16 ohm-cm
@Temperature 73.4 °F
|
DAM; IEC 60093 | |
| Surface Resistance | 7.10e 12 ohm
@Temperature 23.0 °C
|
7.10e 12 ohm
@Temperature 73.4 °F
|
50%RH; IEC 60093 |
| 2.70e 15 ohm
@Temperature 23.0 °C
|
2.70e 15 ohm
@Temperature 73.4 °F
|
DAM; IEC 60093 | |
| 介电常数 | 3.2
@Frequency 1.00e 6 Hz, Temperature 23.0 °C
|
3.2
@Frequency 1.00e 6 Hz, Temperature 73.4 °F
|
DAM; IEC 60250 |
| 3.4
@Frequency 100 Hz, Temperature 23.0 °C
|
3.4
@Frequency 100 Hz, Temperature 73.4 °F
|
DAM; IEC 60250 | |
| 3.5
@Frequency 1.00e 6 Hz, Temperature 23.0 °C
|
3.5
@Frequency 1.00e 6 Hz, Temperature 73.4 °F
|
50%RH; IEC 60250 | |
| 6.0
@Frequency 100 Hz, Temperature 23.0 °C
|
6.0
@Frequency 100 Hz, Temperature 73.4 °F
|
50%RH; IEC 60250 | |
| 介电强度 | 26.0 kV/mm
@Thickness 2.00 mm, Temperature 23.0 °C
|
660 kV/in
@Thickness 0.0787 in, Temperature 73.4 °F
|
50%RH; IEC 60243-1 |
| 26.0 kV/mm
@Thickness 2.00 mm, Temperature 23.0 °C
|
660 kV/in
@Thickness 0.0787 in, Temperature 73.4 °F
|
DAM; IEC 60243-1 | |
| 耗散因数 | 0.0050
@Frequency 100 Hz, Temperature 23.0 °C
|
0.0050
@Frequency 100 Hz, Temperature 73.4 °F
|
DAM; IEC 60250 |
| 0.011
@Frequency 1.00e 6 Hz, Temperature 23.0 °C
|
0.011
@Frequency 1.00e 6 Hz, Temperature 73.4 °F
|
DAM; IEC 60250 | |
| 0.038
@Frequency 1.00e 6 Hz, Temperature 23.0 °C
|
0.038
@Frequency 1.00e 6 Hz, Temperature 73.4 °F
|
50%RH; IEC 60250 | |
| 0.176
@Frequency 100 Hz, Temperature 23.0 °C
|
0.176
@Frequency 100 Hz, Temperature 73.4 °F
|
50%RH; IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 600 V
@Thickness 3.00 mm, Temperature 23.0 °C
|
600 V
@Thickness 0.118 in, Temperature 73.4 °F
|
DAM; UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 120 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
66.7 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ASTM E 831 |
| 120 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
66.7 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ISO 11359-1/-2 | |
| 130 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
72.2 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
DAM; ISO 11359-1/-2 | |
| 130 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
72.2 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
DAM; ASTM E 831 | |
| 140 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
77.8 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ASTM E 831 | |
| 140 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
77.8 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 170 μm/m-°C
@Temperature 55.0 - 160 °C
|
94.4 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ASTM E 831 | |
| 170 μm/m-°C
@Temperature 55.0 - 160 °C
|
94.4 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ISO 11359-1/-2 | |
| 线性热膨胀系数,横向流动 | 110 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
61.1 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
DAM; ISO 11359-1/-2 |
| 110 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
61.1 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ISO 11359-1/-2 | |
| 110 μm/m-°C
@Temperature -30.0 - 30.0 °C
|
61.1 μin/in-°F
@Temperature -22.0 - 86.0 °F
|
DAM; ASTM E 831 | |
| 110 μm/m-°C
@Temperature -40.0 - 23.0 °C
|
61.1 μin/in-°F
@Temperature -40.0 - 73.4 °F
|
DAM; ASTM E 831 | |
| 120 μm/m-°C
@Temperature 55.0 - 160 °C
|
66.7 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ASTM E 831 | |
| 120 μm/m-°C
@Temperature 23.0 - 55.0 °C
|
66.7 μin/in-°F
@Temperature 73.4 - 131 °F
|
DAM; ISO 11359-1/-2 | |
| 120 μm/m-°C
@Temperature 55.0 - 160 °C
|
66.7 μin/in-°F
@Temperature 131 - 320 °F
|
DAM; ISO 11359-1/-2 |