PA66 Zytel 80G43HS1L BK104

Physical Properties	Metric	English	Comments
Density	1.43g/cc	0.0517lb/in3	DAM; ISO 1183
Melt Density	1.27g/cc @Temperature =262 °C	0.0459lb/in3 @Temperature =504 °F
Water Absorption	4.9 % @Thickness 2.00 mm	4.9 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	1.50 % @Thickness 2.00 mm	1.50 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow	0.0020cm/cm	0.0020in/in	DAM; ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0060cm/cm	0.0060in/in	DAM; ISO 294-4, 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	169MPa	24500psi	DAM; ISO 527-1/-2
Elongation at Break	3.3 %	3.3 %	DAM; ISO 527-1/-2
Tensile Modulus	11.7GPa	1700ksi	DAM; ISO 527-1/-2
Flexural Modulus	10.3GPa	1490ksi	DAM; ISO 178
Poissons Ratio	0.33	0.33	DAM; ISO 527-1/-2
Izod Impact, Notched (ISO)	78.0kJ/m2 @Temperature 23.0 °C	37.1ft-lb/in2 @Temperature 73.4 °F	DAM; ISO 180/1U
Izod Impact, Unnotched (ISO)	14.0kJ/m2 @Temperature -40.0 °C	6.66ft-lb/in2 @Temperature -40.0 °F	DAM; ISO 180/1A
	23.0kJ/m2 @Temperature 23.0 °C	10.9ft-lb/in2 @Temperature 73.4 °F	DAM; ISO 180/1A
Charpy Impact Unnotched	9.00J/cm2 @Temperature 23.0 °C	42.8ft-lb/in2 @Temperature 73.4 °F	DAM; ISO 179/1eU
Charpy Impact, Notched	1.50J/cm2 @Temperature -40.0 °C	7.14ft-lb/in2 @Temperature -40.0 °F	DAM; ISO 179/1eA
	2.30J/cm2 @Temperature 23.0 °C	10.9ft-lb/in2 @Temperature 73.4 °F	DAM; ISO 179/1e

PA66 Zytel 80G43HS1L BK104

PA特性

1、具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差

2、PA66在较高温度也能保持较强的强度和刚度。PA66在成型后仍然具有吸湿性，其程度主要取决于材料的组成、壁厚以及环境条件。

3、在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。

4、PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。

PA66应用

高温电气插座零件、电气零件、齿轮、轴承、滚子、弹簧支架、滑轮、螺栓、叶轮、风扇叶片、螺旋桨、高压封口垫片、阀座、输油管、储油容器、绳索、扎带、传动皮带、砂轮粘合剂、电池箱、绝缘电气零件、线芯、抽丝等