LCP VECTRA E488i

Physical Properties	Metric	English	Comments
Density	1.77g/cc	0.0639lb/in3	ISO 1183
Water Absorption at Saturation	0.0050 %	0.0050 %	ISO 62
Linear Mold Shrinkage, Flow	0.0014cm/cm	0.0014in/in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0043cm/cm	0.0043in/in	ISO 294-4
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	54	54	ISO 2039-2
Tensile Strength at Break	110MPa	16000psi	5mm/min; ISO 527-2/1A
Elongation at Break	1.5 %	1.5 %	5mm/min; ISO 527-2/1A
Tensile Modulus	13.0GPa	1890ksi	50mm/min; ISO 527-2/1A
Flexural Strength	160MPa	23200psi	ISO 178
Flexural Modulus	13.0GPa	1890ksi	ISO 178
Flexural Strain at Break	1.8 %	1.8 %	ISO 178
Compressive Modulus	11.0GPa	1600ksi	ISO 604
Izod Impact, Notched (ISO)	9.00kJ/m2	4.28ft-lb/in2	ISO 180/1A
	28.0kJ/m2 @Temperature 23.0 °C	13.3ft-lb/in2 @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	2.90J/cm2	13.8ft-lb/in2	ISO 179/1eU
Charpy Impact, Notched	1.80J/cm2	8.57ft-lb/in2	ISO 179/1eA

LCP VECTRA E488i

概述

LCP是一类具有杰出性能的新型聚合物。LCP是包含范围很宽的一类材料：

a、溶致性液晶：需要在溶液中加工；

b、热致性液晶：可在熔融状态加工。

最初工业化液晶聚合物是美国DuPont公司开发出来的溶致性聚对亚苯基对苯二甲酰胺（Kevlarreg;）。由于这种类型的聚合物只能在溶液中加工，不能熔融，只能用作纤维和涂料。以下内容只包括热致性LCP。

主要用途

1）LCP塑胶原料其具有高强度、高刚性、耐高温、电绝缘性等十分优良，被用于电子、电气、光导纤维、汽车及宇航等领域。2）用液晶作成的纤维可以做鱼网、******、体育用品、刹车片、光导纤维几显示材料等，还可制成薄膜，用于软质印刷线路、食品包装等。3）LCP塑胶原料已经用于微波炉容器，可以耐高低温。LCP还可以做印刷电路板、人造卫星电子部件、喷气发动机零件；用于电子电气和汽车机械零件或部件；还可以用于医疗方面。4）LCP塑胶原料可以加入高填充剂作为集成电路封装材料，以代替环氧树脂作线圈骨架的封装材料；作光纤电缆接头护套和高强度元件；代替陶瓷作化工用分离塔中的填充材料等。 5）LCP塑胶原料还可以与聚砜、PBT、聚酰胺等塑料共混制成合金，制件成型后其机械强度高，用以代替玻璃纤维增强的聚砜等塑料，既可提高机械强度性能，又可提高使用强度及化学稳定性等。目前正在研究将LCP用于宇航器外部的面板、汽车外装的制动系统等。