TECNOPRENE 3K2 PP
TECNOPRENE 3K3 PP
TECNOPRENE 3K4 ELU1 PP
TECNOPRENE 3K4 PP
TECNOPRENE 3K6 PP
TECNOPRENE 3KBA24 PP
TECNOPRENE A60K3 PP
TECNOPRENE A60K4 PP
TECNOPRENE A60K5 PP
TECNOPRENE A60K6 F PP
TECNOPRENE A60K6 schwarz 915 PP
TECNOPRENE A60K6 PP
TECNOPRENE AK6 D PP
TECNOPRENE AK6HI PP
TECNOPRENE AK8 PP
TECNOPRENE AKM24 PP
TECNOPRENE AKM43 PP
TECNOPRENE F60K5 UA PP
TECNOPRENE F60K6 PP
TECNOPRENE FK5 D PP
TECNOPRENE FK6 D PP
TECNOPRENE FK7 PP
TECNOPRENE FKB42 PP
TECNOPRENE FKM22 F PP
TECNOPRENE H60K6 PP
TECNOPRENE HK3D PP
TECNOPRENE HKM41D PP
TECNOPRENE T30VC4 PP
TECNOPRENE T30VC5 PP
TECNOPRENE T30VC6 PP
TECNOPRENE T60K4 F NAT005 PP
TECNOPRENE T60VB4 PP
TECNOPRENE V60K6/F natur 005 PP
TECNOPRENE VK6HI T1 PP
TECNOPRENE VK7 PP
TECNOPRENE VKM24 PP
TECNOPRENE X30VC5 PP
TECNOPRENE X30VC6 PP
基本信息 | |
---|---|
填料/增强材料 |
|
特性 |
|
机构评级 |
|
外观 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | 1.13 | g/cm3 | ASTM D792 |
熔流率(熔体流动速率)(230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
收缩率 | 0.60 | % | 内部方法 |
吸水率(23°C, 24 hr) | 0.020 | % | ASTM D570 |
灰份含量 | 30 | % | 内部方法 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
抗张强度(断裂) | 55.0 | MPa | ASTM D638 |
弯曲模量 | 4200 | MPa | ASTM D790 |
弯曲强度 | 90.0 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度(23°C) | 5.0 | kJ/m2 | ISO 179/1eA |
悬壁梁缺口冲击强度(23°C) | 68 | J/m | ASTM D256 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
载荷下热变形温度(1.8 MPa, 未退火) | 134 | °C | ASTM D648 |
线形热膨胀系数 - 流动 | 6.0E-5 | cm/cm/°C | ASTM D696 |
电气性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
表面电阻率 | 1.0E 14 | ohms | ASTM D257 |
介电常数(1 kHz) | 2.50 | ASTM D150 | |
漏电起痕指数 | 600 | V | IEC 60112 |
可燃性 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
UL 阻燃等级(3.20 mm) | HB | UL 94 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 80.0 | °C | |
干燥时间 | 2.0 | hr | |
料筒后部温度 | 190 | °C | |
料筒中部温度 | 210 | °C | |
料筒前部温度 | 230 | °C | |
模具温度 | 50.0 到 70.0 | °C |