DuPont Performance Polymers Zytel? E42A NC010 Nylon 66 (Unverified Data**) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 |
| Water Absorption | 2.7 %
@Temperature 23.0 °C
|
2.7 %
@Temperature 73.4 °F
|
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 8.5 %
@Temperature 23.0 °C
|
8.5 %
@Temperature 73.4 °F
|
Saturation, immersed; DAM; ISO 62, Similar to | |
| 粘度 | 109000 cP
@Shear Rate 7000 1/s, Temperature 305 °C
|
109000 cP
@Shear Rate 7000 1/s, Temperature 581 °F
|
DAM; ISO 11443 |
| 119000 cP
@Shear Rate 7000 1/s, Temperature 295 °C
|
119000 cP
@Shear Rate 7000 1/s, Temperature 563 °F
|
DAM; ISO 11443 | |
| 136000 cP
@Shear Rate 5000 1/s, Temperature 305 °C
|
136000 cP
@Shear Rate 5000 1/s, Temperature 581 °F
|
DAM; ISO 11443 | |
| 144000 cP
@Shear Rate 7000 1/s, Temperature 275 °C
|
144000 cP
@Shear Rate 7000 1/s, Temperature 527 °F
|
DAM; ISO 11443 | |
| 150000 cP
@Shear Rate 5000 1/s, Temperature 295 °C
|
150000 cP
@Shear Rate 5000 1/s, Temperature 563 °F
|
DAM; ISO 11443 | |
| 182000 cP
@Shear Rate 5000 1/s, Temperature 275 °C
|
182000 cP
@Shear Rate 5000 1/s, Temperature 527 °F
|
DAM; ISO 11443 | |
| 243000 cP
@Shear Rate 2000 1/s, Temperature 305 °C
|
243000 cP
@Shear Rate 2000 1/s, Temperature 581 °F
|
DAM; ISO 11443 | |
| 274000 cP
@Shear Rate 2000 1/s, Temperature 295 °C
|
274000 cP
@Shear Rate 2000 1/s, Temperature 563 °F
|
DAM; ISO 11443 | |
| 342000 cP
@Shear Rate 2000 1/s, Temperature 275 °C
|
342000 cP
@Shear Rate 2000 1/s, Temperature 527 °F
|
DAM; ISO 11443 | |
| 360000 cP
@Shear Rate 1000 1/s, Temperature 305 °C
|
360000 cP
@Shear Rate 1000 1/s, Temperature 581 °F
|
DAM; ISO 11443 | |
| 413000 cP
@Shear Rate 1000 1/s, Temperature 295 °C
|
413000 cP
@Shear Rate 1000 1/s, Temperature 563 °F
|
DAM; ISO 11443 | |
| 431000 cP
@Shear Rate 700 1/s, Temperature 305 °C
|
431000 cP
@Shear Rate 700 1/s, Temperature 581 °F
|
DAM; ISO 11443 | |
| 501000 cP
@Shear Rate 700 1/s, Temperature 295 °C
|
501000 cP
@Shear Rate 700 1/s, Temperature 563 °F
|
DAM; ISO 11443 | |
| 504000 cP
@Shear Rate 500 1/s, Temperature 305 °C
|
504000 cP
@Shear Rate 500 1/s, Temperature 581 °F
|
DAM; ISO 11443 | |
| 535000 cP
@Shear Rate 1000 1/s, Temperature 275 °C
|
535000 cP
@Shear Rate 1000 1/s, Temperature 527 °F
|
DAM; ISO 11443 | |
| 593000 cP
@Shear Rate 500 1/s, Temperature 295 °C
|
593000 cP
@Shear Rate 500 1/s, Temperature 563 °F
|
DAM; ISO 11443 | |
| 664000 cP
@Shear Rate 700 1/s, Temperature 275 °C
|
664000 cP
@Shear Rate 700 1/s, Temperature 527 °F
|
DAM; ISO 11443 | |
| 806000 cP
@Shear Rate 500 1/s, Temperature 275 °C
|
806000 cP
@Shear Rate 500 1/s, Temperature 527 °F
|
DAM; ISO 11443 | |
| 线性成型收缩率,Flow | 0.014 cm/cm
@Thickness 2.00 mm
|
0.014 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.014 cm/cm
@Thickness 2.00 mm
|
0.014 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度 | 13.4 MPa
@Strain 3.00 %, Temperature 90.0 °C
|
1940 psi
@Strain 3.00 %, Temperature 194 °F
|
50%RH; ISO 527 |
| 14.5 MPa
@Strain 5.00 %, Temperature 120 °C
|
2100 psi
@Strain 5.00 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 15.9 MPa
@Strain 3.00 %, Temperature 60.0 °C
|
2310 psi
@Strain 3.00 %, Temperature 140 °F
|
50%RH; ISO 527 | |
| 17.6 MPa
@Strain 5.00 %, Temperature 120 °C
|
2550 psi
@Strain 5.00 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 19.7 MPa
@Strain 3.00 %, Temperature 40.0 °C
|
2860 psi
@Strain 3.00 %, Temperature 104 °F
|
50%RH; ISO 527 | |
| 20.9 MPa
@Strain 10.0 %, Temperature 120 °C
|
3030 psi
@Strain 10.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 21.1 MPa
@Strain 6.00 %, Temperature 90.0 °C
|
3060 psi
@Strain 6.00 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 21.8 MPa
@Strain 5.00 %, Temperature 90.0 °C
|
3160 psi
@Strain 5.00 %, Temperature 194 °F
|
DAM; ISO 527 | |
| 22.4 MPa
@Strain 0.800 %, Temperature 40.0 °C
|
3250 psi
@Strain 0.800 %, Temperature 104 °F
|
DAM; ISO 527 | |
| 23.5 MPa
@Strain 10.0 %, Temperature 120 °C
|
3410 psi
@Strain 10.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 24.2 MPa
@Strain 15.0 %, Temperature 120 °C
|
3510 psi
@Strain 15.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 24.8 MPa
@Strain 6.00 %, Temperature 60.0 °C
|
3600 psi
@Strain 6.00 %, Temperature 140 °F
|
50%RH; ISO 527 | |
| 24.9 MPa
@Strain 0.800 %, Temperature 23.0 °C
|
3610 psi
@Strain 0.800 %, Temperature 73.4 °F
|
DAM; ISO 527 | |
| 25.8 MPa
@Strain 9.00 %, Temperature 90.0 °C
|
3740 psi
@Strain 9.00 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 26.1 MPa
@Strain 20.0 %, Temperature 120 °C
|
3790 psi
@Strain 20.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 26.3 MPa
@Strain 15.0 %, Temperature 120 °C
|
3810 psi
@Strain 15.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 27.2 MPa
@Strain 25.0 %, Temperature 120 °C
|
3950 psi
@Strain 25.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 27.2 MPa
@Strain 3.00 %, Temperature 60.0 °C
|
3950 psi
@Strain 3.00 %, Temperature 140 °F
|
DAM; ISO 527 | |
| 27.9 MPa
@Strain 30.0 %, Temperature 120 °C
|
4050 psi
@Strain 30.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 27.9 MPa
@Strain 20.0 %, Temperature 120 °C
|
4050 psi
@Strain 20.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 28.2 MPa
@Strain 35.0 %, Temperature 120 °C
|
4090 psi
@Strain 35.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 28.3 MPa
@Strain 40.0 %, Temperature 120 °C
|
4100 psi
@Strain 40.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 28.4 MPa
@Strain 45.0 %, Temperature 120 °C
|
4120 psi
@Strain 45.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 28.5 MPa
@Strain 50.0 %, Temperature 120 °C
|
4130 psi
@Strain 50.0 %, Temperature 248 °F
|
50%RH; ISO 527 | |
| 28.5 MPa
@Strain 3.00 %, Temperature 23.0 °C
|
4130 psi
@Strain 3.00 %, Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 28.8 MPa
@Strain 12.0 %, Temperature 90.0 °C
|
4180 psi
@Strain 12.0 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 28.9 MPa
@Strain 25.0 %, Temperature 120 °C
|
4190 psi
@Strain 25.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 29.6 MPa
@Strain 30.0 %, Temperature 120 °C
|
4290 psi
@Strain 30.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 29.6 MPa
@Strain 10.0 %, Temperature 90.0 °C
|
4290 psi
@Strain 10.0 %, Temperature 194 °F
|
DAM; ISO 527 | |
| 30.0 MPa
@Strain 35.0 %, Temperature 120 °C
|
4350 psi
@Strain 35.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 30.1 MPa
@Strain 6.00 %, Temperature 40.0 °C
|
4370 psi
@Strain 6.00 %, Temperature 104 °F
|
50%RH; ISO 527 | |
| 30.3 MPa
@Strain 9.00 %, Temperature 60.0 °C
|
4390 psi
@Strain 9.00 %, Temperature 140 °F
|
50%RH; ISO 527 | |
| 30.4 MPa
@Strain 40.0 %, Temperature 120 °C
|
4410 psi
@Strain 40.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 30.6 MPa
@Strain 45.0 %, Temperature 120 °C
|
4440 psi
@Strain 45.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 30.7 MPa
@Strain 15.0 %, Temperature 90.0 °C
|
4450 psi
@Strain 15.0 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 30.7 MPa
@Strain 50.0 %, Temperature 120 °C
|
4450 psi
@Strain 50.0 %, Temperature 248 °F
|
DAM; ISO 527 | |
| 31.9 MPa
@Strain 18.0 %, Temperature 90.0 °C
|
4630 psi
@Strain 18.0 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 32.7 MPa
@Strain 21.0 %, Temperature 90.0 °C
|
4740 psi
@Strain 21.0 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 33.1 MPa
@Strain 24.0 %, Temperature 90.0 °C
|
4800 psi
@Strain 24.0 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 33.3 MPa
@Strain 27.0 %, Temperature 90.0 °C
|
4830 psi
@Strain 27.0 %, Temperature 194 °F
|
50%RH; ISO 527 | |
| 33.4 MPa
@Strain 30.0 %, Temperature 90.0 °C
|
4840 psi
@Strain 30.0 %, Temperature 194 °F
|
50%RH; ISO 527 |