PCTG TRITAN MX811 产品说明：

Eastman Tritan? MX811 is an amorphous copolyester with excellent appearance and clarity. Tritan MX811 contains a mold release derived from vegetable based sources. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. This new generation copolyester can also be molded into various applications without incorporating high levels of residual stress. Eastman? Copolyester MX811 has been formulated for medical devices. Eastman Tritan? Copolyester MX811 has been tested for FDA/ISO 10993 and USP Class VI Biological Evaluation testing after Gamma and ETO sterilization.

基本信息
添加剂	脱模
特性	辐射消毒 环氧乙烷消毒 抗撞击性，良好 可加工性，良好 快的成型周期 耐化学性良好 耐热性，高 清晰度，高 韧性良好 水解稳定 无定形的
用途	医疗/护理用品 医疗器械
机构评级	FDA 未评级 ISO 10993 USP 第VI类

物理性能	额定值	单位制	测试方法
比重	1.17	g/cm3	ASTM D792
收缩率 - 流动	0.50 到 0.70	%	ASTM D955

硬度	额定值	单位制	测试方法
洛氏硬度(R 级, 23°C)	115		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量(23°C)	1590	MPa	ASTM D638
抗张强度			ASTM D638
屈服, 23°C	44.0	MPa	ASTM D638
断裂, 23°C	53.0	MPa	ASTM D638
伸长率			ASTM D638
屈服, 23°C	7.0	%	ASTM D638
断裂, 23°C	140	%	ASTM D638
弯曲模量(23°C)	1590	MPa	ASTM D790
弯曲强度(屈服, 23°C)	66.0	MPa	ASTM D790

PCTG TRITAN MX811

PCTG特性:

热成型性能

PCTG板材易于生产出造型复杂及拉伸比大的制品。而且，与PC板和抗冲改性的压克力不同，这种板材无须在热成型加工前进行预干燥处理。与PC板或压克力相比，其成型周期短，温度低，成品率更高。

坚韧性:

PCTG板材的挤出板材通常比通用压克力坚韧15至20倍，比抗冲改性的压克力坚韧5至10倍。PETG板材在加工、运输和使用过程中具有足够的承受能力，有助于防止破裂。

耐候性:

PCTG板材提供了优秀的耐候性。它可以保持产品的坚韧性，防止变黄。它含有紫外线吸收剂，可共挤成一保护层，保护了板材免受紫外线的有害影响。

加工简便:

PCTG板材可进行锯切、模切、钻孔、冲孔、剪切、铆接、铣边以及冷弯，不至于破碎。表面的轻微刮痕可用热风枪来消除。溶剂粘接亦是常规操作。它比通用压克力、抗冲改性压克力或PC板更易于加工，并可进行植绒、电镀、静电等加工处理。

优秀的耐化学性能

PCTG板材可以耐受多种化学品以及常用的清洁剂。

环保: PCTG板材基材均为环保材料，符合食品接触管理要求。

经济性: 比压克力经久耐用。

PCTG TRITAN MX811 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！