EVA ELVAX 670 产品说明：

DuPont? Elvax? 670 is an ethylene-vinyl acetate copolymer resin for use in industrial applications.

Composition

• 12 % By Weight Vinyl Acetate comonomer content

• Thermal Stabilizer: BHT antioxidant

Applications

• Elvax? resins can be used in a variety of applications involving molding, compounding, extrusion, adhesives, sealants, and wax blends. For additional information and properties associated with specific applications, please refer to the Grade Selector Guides found on the Elvax? website for industrial applications. http://www2.dupont.com/Elvax/en_US/tech_info/index.html

物理性能	额定值	单位制	测试方法
比重	0.933	g/cm3	ASTM D792, ISO 1183
熔流率（熔体流动速率）(190°C/2.16 kg)	0.35	g/10 min	ASTM D1238, ISO 1133
醋酸乙烯含量	12.0	wt%

热性能	额定值	单位制	测试方法
维卡软化温度	79.0	°C	ASTM D1525, ISO 306
熔融峰值温度	95.0	°C	ASTM D3418, ISO 3146

EVA ELVAX 670

特性

是是广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。

1、乙酸乙烯含量在5%以下的EVA，其主要产品是薄膜、电线电缆、LDPE改性剂、胶粘剂等；

2、乙酸乙烯含量在5%~10% 的EVA产品为弹性薄膜等；

3、乙酸乙烯含量在20~28%的EVA，主要用于热熔粘合剂和涂层制品；

EVA是由LLDPE（线性低密度聚乙烯）和醋酸（VA）共聚而成。

EVA的聚合方法：

1、高压本体聚合 （塑料制品）

2、溶液聚合 （PVC加工助剂）

3、乳液聚合 （粘合剂制品）

4、悬浮聚合

乙酸乙烯（VA）含量高于30%的采用乳液聚合；

乙酸乙烯（VA）含量低的就采用高压本体聚合。

影响EVA性能的主要因素：

1、Melt Index 熔融指数（简称MI,溶指）

2、VA% 醋酸的含量

熔融指数（MI）一定，乙酸乙烯（VA)含量越高，其弹性、柔软性、相溶性、透明性等也越高；当VA的含量减少的时候，它的性能接近于聚乙烯（PE），刚性增高，耐磨性、电绝缘性提高。

应用

1、广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。

2、乙酸乙烯含量在5%~10% 的EVA产品为弹性薄膜等；

3、乙酸乙烯含量在20~28%的EVA，主要用于热熔粘合剂和涂层制品；

4、乙酸乙烯含量在5%~45%，主要产品为薄膜（包括农用薄膜）和片材，注塑、模塑制品，发泡制品，热熔粘合剂等。

EVA ELVAX 670 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！