POM CELCON GC10
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.46g/cc | 0.0527lb/in3 | ISO 1183 |
Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 |
Water Absorption at Saturation | 0.80 % | 0.80 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.0090cm/cm | 0.0090in/in | ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.012cm/cm | 0.012in/in | ISO 294-4 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 75.0MPa | 10900psi | 5mm/min; ISO 527-2/1A |
Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527-2/1A |
Tensile Modulus | 4.50GPa | 653ksi | 50mm/min; ISO 527-2/1A |
Flexural Modulus | 4.25GPa | 616ksi | ISO 178 |
Izod Impact, Notched (ISO) | 4.80kJ/m2 | 2.28ft-lb/in2 | ISO 180/1A |
Charpy Impact Unnotched | 3.00J/cm2 | 14.3ft-lb/in2 | ISO 179/1eU |
4.50J/cm2 @Temperature -30.0 °C |
21.4ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eU | |
Charpy Impact, Notched | 0.450J/cm2 | 2.14ft-lb/in2 | ISO 179/1eA |
POM CELCON GC10 我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
特点
(1)POM加工前可不用干燥,最好在加工过程中进行预热(80℃左右),对产品尺寸的稳定性有好处.
(2) POM的加工温度很窄(0~215℃),在炮筒内停留时间稍长或温度超过220℃时就会分解,产生刺激性强的甲醛气体.
(3) POM料注塑时保压压力要较大(与注射压力相近),以减少压力降.螺杆转速不能过高,残量要少;
(4) POM产品收缩率较大,易产生缩水或变形.POM比热大,模温高(80~100℃),产品脱模时很烫,需防止烫伤手指.
(5) POM宜在“中压、中速、低料温、较高模温”的条件下成型加工,精密制品成型时需用控制模温
(6)具高机械强度和刚性
(7)最高的疲劳强度
(8)环境抵抗性、耐有机溶剂性佳
(9)耐反覆冲击性强,良好的电气性质,复原性良好,具自已润滑性、耐磨性良好,尺寸安定性优.
应用
.可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等.