东莞市铭汇塑胶有限公司
TABOREX TA 1135 HD
高密度聚乙烯
SILON s.ro
产品说明:
A chemically-crosslinkable HDPE compound for the production of multi-layer pipes for domestic hot and cold water, under floor heating and central heating application. It is designed to achieve best performance in single layer and co-extrusion products.
TA 1135 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes which are produced with the SILON grade TA 1135 HD fulfil the requirements of ASTM F876-04a, CSA 137.5-03, EN ISO 15875, BS 7291 and all related standards.
This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product has all the improved properties associated with crosslinked polyethylene.
TA 1135 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes which are produced with the SILON grade TA 1135 HD fulfil the requirements of ASTM F876-04a, CSA 137.5-03, EN ISO 15875, BS 7291 and all related standards.
This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product has all the improved properties associated with crosslinked polyethylene.
基本信息 | |
---|---|
特性 |
|
用途 |
|
机构评级 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 0.949 | g/cm3 | DIN 53479, ASTM D1505 |
表观密度 | 0.56 | g/cm3 | DIN 53466 |
熔流率(熔体流动速率) | ASTM D1238, ISO 1133 | ||
190°C/2.16 kg | 0.60 | g/10 min | ASTM D1238, ISO 1133 |
190°C/5.0 kg | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
挥发物 | % | 内部方法 | |
凝胶含量 | 70 | % | EN 579 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸应力(断裂) | 25.0 | MPa | ISO 527-2 |
拉伸应变(断裂) | 250 | % | ISO 527-2 |
挤出 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 80.0 到 90.0 | °C | |
干燥时间 | 2.0 | hr | |
料筒1区温度 | 160 到 170 | °C | |
料筒2区温度 | 170 到 180 | °C | |
料筒3区温度 | 170 到 190 | °C | |
料筒4区温度 | 170 到 190 | °C | |
口模温度 | 190 到 220 | °C |