美国杜邦PET 408 NC010 30%玻纤增强 高刚性 高抗冲击强度
DuPont Performance Polymers Rynite? 408 NC010 PET
Polymer,Thermoplastic,Polyester, TP,Polyethylene Terephthalate (PET),Polyethylene Terephthalate (PET), 30% Glass Reinforced
DuPont Performance Polymers
产品说明:
Rynite? 408 NC010 is a 30% glass reinforced modified polyethylene terephthalate with improved impact resistance. Excellent balance of strength, stiffness, toughness, and temperature resistance.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Rynite? 408 NC010 PET 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| 密度 | 1.49 g/cc | 0.0538 lb/in3 | ISO 1183 |
| 填料含量 | 30 % | 30 % | |
| 吸水率 | 0.060 %
@Temperature 23.0 °C
|
0.060 %
@Temperature 73.4 °F
|
50%RH,23°C,24h; ASTM D570 |
| 粘度 | 110000 cP
@Shear Rate 3090 1/s, Temperature 305 °C
|
110000 cP
@Shear Rate 3090 1/s, Temperature 581 °F
|
ISO 11443 |
| 138000 cP
@Shear Rate 3090 1/s, Temperature 290 °C
|
138000 cP
@Shear Rate 3090 1/s, Temperature 554 °F
|
ISO 11443 | |
| 157000 cP
@Shear Rate 1450 1/s, Temperature 305 °C
|
157000 cP
@Shear Rate 1450 1/s, Temperature 581 °F
|
ISO 11443 | |
| 172000 cP
@Shear Rate 3090 1/s, Temperature 275 °C
|
172000 cP
@Shear Rate 3090 1/s, Temperature 527 °F
|
ISO 11443 | |
| 215000 cP
@Shear Rate 1450 1/s, Temperature 290 °C
|
215000 cP
@Shear Rate 1450 1/s, Temperature 554 °F
|
ISO 11443 | |
| 218000 cP
@Shear Rate 681 1/s, Temperature 305 °C
|
218000 cP
@Shear Rate 681 1/s, Temperature 581 °F
|
ISO 11443 | |
| 260000 cP
@Shear Rate 1450 1/s, Temperature 275 °C
|
260000 cP
@Shear Rate 1450 1/s, Temperature 527 °F
|
ISO 11443 | |
| 318000 cP
@Shear Rate 681 1/s, Temperature 290 °C
|
318000 cP
@Shear Rate 681 1/s, Temperature 554 °F
|
ISO 11443 | |
| 322000 cP
@Shear Rate 316 1/s, Temperature 305 °C
|
322000 cP
@Shear Rate 316 1/s, Temperature 581 °F
|
ISO 11443 | |
| 386000 cP
@Shear Rate 681 1/s, Temperature 275 °C
|
386000 cP
@Shear Rate 681 1/s, Temperature 527 °F
|
ISO 11443 | |
| 454000 cP
@Shear Rate 316 1/s, Temperature 290 °C
|
454000 cP
@Shear Rate 316 1/s, Temperature 554 °F
|
ISO 11443 | |
| 463000 cP
@Shear Rate 146 1/s, Temperature 305 °C
|
463000 cP
@Shear Rate 146 1/s, Temperature 581 °F
|
ISO 11443 | |
| 560000 cP
@Shear Rate 316 1/s, Temperature 275 °C
|
560000 cP
@Shear Rate 316 1/s, Temperature 527 °F
|
ISO 11443 | |
| 655000 cP
@Shear Rate 146 1/s, Temperature 290 °C
|
655000 cP
@Shear Rate 146 1/s, Temperature 554 °F
|
ISO 11443 | |
| 663000 cP
@Shear Rate 73.0 1/s, Temperature 305 °C
|
663000 cP
@Shear Rate 73.0 1/s, Temperature 581 °F
|
ISO 11443 | |
| 810000 cP
@Shear Rate 146 1/s, Temperature 275 °C
|
810000 cP
@Shear Rate 146 1/s, Temperature 527 °F
|
ISO 11443 | |
| 935000 cP
@Shear Rate 73.0 1/s, Temperature 290 °C
|
935000 cP
@Shear Rate 73.0 1/s, Temperature 554 °F
|
ISO 11443 | |
| 1.00e+6 cP
@Shear Rate 36.0 1/s, Temperature 305 °C
|
1.00e+6 cP
@Shear Rate 36.0 1/s, Temperature 581 °F
|
ISO 11443 | |
| 1.17e+6 cP
@Shear Rate 73.0 1/s, Temperature 275 °C
|
1.17e+6 cP
@Shear Rate 73.0 1/s, Temperature 527 °F
|
ISO 11443 | |
| 1.29e+6 cP
@Shear Rate 36.0 1/s, Temperature 290 °C
|
1.29e+6 cP
@Shear Rate 36.0 1/s, Temperature 554 °F
|
ISO 11443 | |
| 1.62e+6 cP
@Shear Rate 36.0 1/s, Temperature 275 °C
|
1.62e+6 cP
@Shear Rate 36.0 1/s, Temperature 527 °F
|
ISO 11443 | |
| 1.73e+6 cP
@Shear Rate 12.0 1/s, Temperature 305 °C
|
1.73e+6 cP
@Shear Rate 12.0 1/s, Temperature 581 °F
|
ISO 11443 | |
| 1.97e+6 cP
@Shear Rate 7.30 1/s, Temperature 305 °C
|
1.97e+6 cP
@Shear Rate 7.30 1/s, Temperature 581 °F
|
ISO 11443 | |
| 2.55e+6 cP
@Shear Rate 12.0 1/s, Temperature 290 °C
|
2.55e+6 cP
@Shear Rate 12.0 1/s, Temperature 554 °F
|
ISO 11443 | |
| 2.96e+6 cP
@Shear Rate 12.0 1/s, Temperature 275 °C
|
2.96e+6 cP
@Shear Rate 12.0 1/s, Temperature 527 °F
|
ISO 11443 | |
| 3.33e+6 cP
@Shear Rate 7.30 1/s, Temperature 290 °C
|
3.33e+6 cP
@Shear Rate 7.30 1/s, Temperature 554 °F
|
ISO 11443 | |
| 4.11e+6 cP
@Shear Rate 7.30 1/s, Temperature 275 °C
|
4.11e+6 cP
@Shear Rate 7.30 1/s, Temperature 527 °F
|
ISO 11443 | |
| 线性成型收缩率 | 0.0020 cm/cm
@Thickness 3.20 mm
|
0.0020 in/in
@Thickness 0.126 in
|
Flow |
| 0.0021 cm/cm
@Thickness 1.60 mm
|
0.0021 in/in
@Thickness 0.0630 in
|
Flow | |
| 0.0063 cm/cm
@Thickness 1.60 mm
|
0.0063 in/in
@Thickness 0.0630 in
|
Transverse | |
| 0.0075 cm/cm
@Thickness 3.20 mm
|
0.0075 in/in
@Thickness 0.126 in
|
Transverse | |
| 线性成型收缩率,Flow | 0.0035 cm/cm | 0.0035 in/in | Annealed; ISO 294-4 |
| 0.0025 cm/cm
@Thickness 2.00 mm
|
0.0025 in/in
@Thickness 0.0787 in
|
ISO 294-4 | |
| 线性成型收缩率，横向 | 0.0105 cm/cm | 0.0105 in/in | Annealed; ISO 294-4 |
| 0.0085 cm/cm
@Thickness 2.00 mm
|
0.0085 in/in
@Thickness 0.0787 in
|
ISO 294-4 | |
| 化合物熔体指数 | 5.5 g/10 min
@Load 5.00 kg, Temperature 280 °C
|
5.5 g/10 min
@Load 11.0 lb, Temperature 536 °F
|
cm3/10 min; ISO 1133 |
PET:PET里面有聚对苯二甲酸乙二醇酯是热塑性聚酯中最主要的品种，英文名为Polyethylene terephthalate 简称PET或PEIT(以下或称为PET)，俗称涤纶树脂。它是对苯二甲酸与乙二醇的缩聚物，与PBT一起统称为热塑性聚酯，或饱和聚酯。
PET优点:
1.有良好的力学性能，冲击强度是其他薄膜的3~5倍，耐折性好。
2.耐油、耐脂肪、耐稀酸、稀碱，耐大多数溶剂。
3.纯PET的耐热性能不高，热变形温度仅为85℃左右，但增强处理后大幅度提高。经玻纤增强后的PET力学性能类似于PC、PA等工程塑料，热变形温度可达到225℃；PET的耐热老化性好，脆化温度为-70℃，在-30℃时仍具有一定韧性；PET不易燃烧，火焰呈黄色，燃烧油滴落。
4.气体和水蒸气渗透率低，既有优良的阻气、水、油及异味性能。
5.透明度高，可阻挡紫外线，光泽性好。
6.无毒、无味，卫生安全性好，可直接用于食品包装。
PET应用:
PET主要用于纤维，少量用于薄膜和工程塑料。PET纤维主要用于纺织工业。PET薄膜主要用于电气绝缘材料，如电容器、电缆绝缘、印刷电路布线基材，电极槽绝缘等。PET薄膜的另一个应用领域是片基和基带，如电影胶片、X光片、录音磁带、电子计算机磁带等。PET薄膜也应用真空渡铝制成金属化薄膜，如金银线、微型电容器薄膜等。PET的另一个用途就是吹塑制品，用于包装的聚酯拉伸瓶。
玻璃纤维增强PET适用于电子电气和汽车行业，用于各种线圈骨架、变压器、电视机、录音机零部件和外壳、汽车灯座、灯罩、白热灯座、继电器、晒整流器等。