PPS FORTRON MT9140L6 产品说明：

Fortron MT9140L6 is a 40% glass fiber reinforced injection molding grade with a low melt viscosity. It exhibits excellent heat and chemical resistance, inherent flame retardancy and shows high hardness and rigidity at elevated temperatures. Fortron MT9140L6 is used for thin walled parts with long flow lengths.

Components made of this grade may be used for medical, dental, pharmaceutical, and certain food handling applications. Fortron MT9140L6 is in compliance with ISO 10993, USP Class VI, and is included in the Fortron Drug and Device Master Files at the FDA. It complies with the FDA Food Contact Notification (FCN-No. 40) for repeat-use applications.

物理性能	额定值	单位制	测试方法
密度	1.65	g/cm3	ISO 1183
收缩率			ISO 294-4
垂直流动方向	0.40 到 0.60	%	ISO 294-4
流动方向	0.20 到 0.60	%	ISO 294-4
吸水率(饱和, 23°C)	0.020	%	ISO 62

硬度	额定值	单位制	测试方法
洛氏硬度(M 计秤)	100		ISO 2039-2

机械性能	额定值	单位制	测试方法
拉伸应力(断裂)	190	MPa	ISO 527-2/1A/5
拉伸应变(断裂)	1.8	%	ISO 527-2/1A/5
弯曲模量(23°C)	14000	MPa	ISO 178
弯曲应力(23°C)	280	MPa	ISO 178

PPS FORTRON MT9140L6

特性

（1）一般性能：PPS为一种外观白色、高结晶度、硬而脆的聚合物，纯PPS的相对密度为1.3，但改性后会增大。PPS有吸水率极小，一般只有0.03%左右。PPS的阻燃性好，其氧指数高达44%以上；与其他塑料相比，它在塑料中属于高阻燃材料（纯PVC的氧指数为47%、PSF为30%、PA66为29%、MPPO为28%，PC为25%）。

（2）机械性能：纯PPS的机械性能不高，尤其冲击强度比较低。以玻璃纤维增强后会大幅度提高冲击强度，由27J/m增大到76J/m，增大3倍；拉伸强度由6Mpa增大到137Mpa，增大1倍。PPS的刚性很高，在工程塑料中少见。纯PPS的弯曲模量可达3.8Gpa，无机填充改性后可达到12.6Gpa,增大5倍之多。而以刚性著称的PPO仅为2.55Gpa，PC仅为2.1Gpa。

（3）电学性能：PPS的电性能十分突出，与其他工程塑料相比，其介电常数和介电损耗角正切值都比较低，并且在较大的频率、温度及温度范围内变化不大；PPS的耐电弧好，可与热固性塑料媲美。PPS常用于电器绝缘材料，其用量可占30%左右。

PPS的应用

1、汽车工业：PPS用于汽车工业占45%左右，主要用于汽车功能件；点火器、加热器、汽化器、离合器、变速器、齿轮箱、轴承支架、灯罩、保险杠、风扇、排气系统以及反光镜和车灯座的零部件。可代替金属制作排气筒循环阀及水泵叶轮，气动信号调解器等。

2、家用电器：热风筒、卷发器、干发器、烫发器、微波炉、咖啡煲、干衣机、电熨斗、电饭煲等的防护涂层和零部件。

3、化学工业：PPS具有优良粘接性和耐蚀性，极宜作化工设备的衬里。

PPS FORTRON MT9140L6 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！