上海正逢塑胶有限公司
PC 泰国科思创 Makrolon? Sheet GP
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.20
|
g/cm3
|
ASTM D792 |
|
吸水率(24 hr)
|
0.15
|
%
|
ASTM D570 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
ASTM D785 | ||
|
M 级
|
70
|
||
|
R 级
|
118
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
2340
|
MPa
|
ASTM D638 |
|
抗张强度
|
ASTM D638 | ||
|
屈服
|
62.1
|
MPa
|
|
|
极限
|
65.5
|
MPa
|
|
|
伸长率(断裂)
|
110
|
%
|
ASTM D638 |
|
弯曲模量
|
2380
|
MPa
|
ASTM D790 |
|
弯曲强度
|
93.1
|
MPa
|
ASTM D790 |
|
压缩模量
|
2380
|
MPa
|
ASTM D695 |
|
压缩强度
|
86.2
|
MPa
|
ASTM D695 |
|
剪切模量
|
786
|
MPa
|
ASTM D732 |
|
剪切强度
|
ASTM D732 | ||
|
--3
|
68.9
|
MPa
|
|
|
--4
|
41.4
|
MPa
|
|
|
泊松比
|
0.38
|
ASTM E132 | |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度(3.18 mm)
|
960
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击(3.18 mm)
|
无断裂
|
ASTM D4812 | |
|
装有测量仪表的落镖冲击(3.18 mm)
|
63.7
|
J
|
ASTM D3763 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa, 未退火
|
138
|
°C
|
|
|
1.8 MPa, 未退火
|
132
|
°C
|
|
|
脆化温度
|
-129
|
°C
|
ASTM D746 |
|
线形热膨胀系数 - 流动
|
6.8E-5
|
cm/cm/°C
|
ASTM D696 |
|
导热系数
|
0.19
|
W/m/K
|
ASTM C177 |
|
Shading Coefficient
|
NFRC 100-2010 | ||
|
Clear : 5.99 mm
|
0.970
|
||
|
Gray or Bronze : 5.99 mm
|
0.770
|
||
|
U Factor
|
NFRC 100-2010 | ||
|
Summer : 5.99 mm
|
0.850
|
BTU/hr/ft2/°F
|
|
|
Summer : 9.53 mm
|
0.780
|
BTU/hr/ft2/°F
|
|
|
Winter : 5.99 mm
|
0.920
|
BTU/hr/ft2/°F
|
|
|
Winter : 9.53 mm
|
0.850
|
BTU/hr/ft2/°F
|
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
8.2E+16
|
ohms·cm
|
ASTM D257 |
|
介电强度(3.18 mm, in Air)
|
15
|
kV/mm
|
ASTM D149 |
|
介电常数
|
ASTM D150 | ||
|
10 Hz
|
2.96
|
||
|
60 Hz
|
3.17
|
||
|
耗散因数(60 Hz)
|
9.0E-4
|
ASTM D150 | |
|
耐电弧性
|
ASTM D495 | ||
|
--5
|
10.0
|
sec
|
|
|
--6
|
120
|
sec
|
|
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94 | ||
|
1.5 mm
|
HB
|
||
|
10.0 mm
|
V-0
|
||
|
Flash Ignition Temperature
|
440
|
°C
|
ASTM D1929 |
|
Horizontal Burn - AEB
|
2.54
|
cm
|
ASTM D635 |
|
Self Ignition Temperature
|
550
|
°C
|
ASTM D1929 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
折射率
|
1.586
|
ASTM D542 | |
|
透射率
|
ASTM D1003 | ||
|
2997 μm7
|
86.0
|
%
|
|
|
2997 μm8
|
50.0
|
%
|
|
|
2997 μm9
|
50.0
|
%
|
|
|
2997 μm10
|
18.0
|
%
|