POM HOSTAFORM C 52021
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.41g/cc | 0.0509lb/in3 | ISO 1183 |
Density of Compound | 1.20g/cc | 0.0434lb/in3 | |
Water Absorption at Saturation | 0.65 % | 0.65 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.019cm/cm | 0.019in/in | ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.018cm/cm | 0.018in/in | ISO 294-4 |
Melt Flow | 39g/10 min @Load 2.16 kg, Temperature 190 °C |
39g/10 min @Load 4.76 lb, Temperature 374 °F |
[cm3/10min]; ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 65.0MPa | 9430psi | 50mm/min; ISO 527-2/1A |
Elongation at Break | 15 % | 15 % | |
Elongation at Yield | 7.0 % | 7.0 % | 50mm/min; ISO 527-2/1A |
Tensile Modulus | 3.00GPa | 435ksi | 50mm/min; ISO 527-2/1A |
Flexural Modulus | 2.80GPa | 406ksi | ISO 178 |
POM HOSTAFORM C 52021
特点
(1)POM加工前可不用干燥,最好在加工过程中进行预热(80℃左右),对产品尺寸的稳定性有好处.
(2) POM的加工温度很窄(0~215℃),在炮筒内停留时间稍长或温度超过220℃时就会分解,产生刺激性强的甲醛气体.
(3) POM料注塑时保压压力要较大(与注射压力相近),以减少压力降.螺杆转速不能过高,残量要少;
(4) POM产品收缩率较大,易产生缩水或变形.POM比热大,模温高(80~100℃),产品脱模时很烫,需防止烫伤手指.
(5) POM宜在“中压、中速、低料温、较高模温”的条件下成型加工,精密制品成型时需用控制模温
(6)具高机械强度和刚性
(7)最高的疲劳强度
(8)环境抵抗性、耐有机溶剂性佳
(9)耐反覆冲击性强,良好的电气性质,复原性良好,具自已润滑性、耐磨性良好,尺寸安定性优.
应用
.可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等.