Adflex Q 300 F
聚烯烃
产品说明：
Adflex Q 300 F is a thermoplastic polyolefin which has been developed for the extrusion or calendering of soft film. Adflex Q 300 F can also be used as impact/toughener modifier of polypropylene homopolymer in extrusion applications. In strapping applications for instance, it notably decreases fibrillation and improves the processability of the film at high drawing ratios. Adflex Q 300 F can be processed on any conventional PP extrusion line as well as on PVC calendars. It can also be blown on standard LDPE or LLDPE film lines.
For regulatory compliance information see the Adflex Q 300F Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS), which can be found on www.polymers.lyondellbasell.com.
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
0.890 |
g/cm3 |
ISO 1183/A |
| 熔流率（熔体流动速率）(230°C/2.16 kg) |
0.80 |
g/10 min |
ISO 1133 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 肖氏硬度(邵氏 D) |
36 |
|
ISO 868 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
ISO 527-2/25 |
| 0.0500 mm1 |
200 |
MPa |
ISO 527-2/25 |
| 0.0500 mm2 |
320 |
MPa |
ISO 527-2/25 |
| 拉伸应力 |
|
|
|
| 屈服 |
9.00 |
MPa |
ISO 527-2 |
| 断裂, 0.0500 mm3 |
18.0 |
MPa |
ISO 527-2/500 |
| 断裂, 50.0 mm4 |
27.0 |
MPa |
ISO 527-2/500 |
| 拉伸应变 |
|
|
|
| 横向流量 : 屈服, 0.0500 mm |
28 |
% |
ISO 527-2/500 |
| 流量 : 屈服, 0.0500 mm |
20 |
% |
ISO 527-2/500 |
| 断裂 |
500 |
% |
ISO 527-2 |
| 弯曲模量 |
330 |
MPa |
ISO 178 |
| Tensile Strength at Yield5 |
|
|
ISO 527-3 |
| MD |
11.0 |
MPa |
ISO 527-3 |
| TD |
8.00 |
MPa |
ISO 527-3 |
| 断裂伸长率6 |
|
|
ISO 527-3 |
| MD |
870 |
% |
ISO 527-3 |
| TD |
850 |
% |
ISO 527-3 |
| 薄膜 |
额定值 |
单位制 |
测试方法 |
| 薄膜厚度 - 经测试 |
50 |
μm |
|
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
|
|
ISO 180/1A |
| -50°C |
40 |
kJ/m2 |
ISO 180/1A |
| -20°C |
70 |
kJ/m2 |
ISO 180/1A |
| 23°C |
无断裂 |
|
ISO 180/1A |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 热变形温度(0.45 MPa, 未退火) |
50.0 |
°C |
ISO 75-2/B |
| 维卡软化温度 |
75.0 |
°C |
ISO 306/A50 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 光泽度(45°, 50.0 μm) |
4 |
|
ASTM D2457 |
| 雾度(50.0 μm) |
95 |
% |
ASTM D1003 |