PP MOPLEN HP526J 产品说明：

Moplen HP526J is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). The product is suitable for metallizable film, both as monolayer film and in coextruded structures. It contains a standard processing stabilisation but does not contain any slip, antiblocking agents and is Calcium Stearate free.
Moplen HP526J offers good optical, excellent highly consistent processing and very good film profile. Typical applications are BOPP packaging film and sheet for Solid Phase Thermoforming.
Moplen HP526J is suitable for food contact.

物理性能	额定值	单位制	测试方法
密度	0.900	g/cm3	ISO 1183
熔流率（熔体流动速率）(230°C/2.16 kg)	3.0	g/10 min	ISO 1133

硬度	额定值	单位制	测试方法
肖氏硬度	70		ISO 868

机械性能	额定值	单位制	测试方法
拉伸应力			ISO 527-2/50
屈服	34.0	MPa	ISO 527-2/50
断裂	23.0	MPa	ISO 527-2/50
拉伸应变			ISO 527-2/50
屈服	12	%	ISO 527-2/50
断裂	500	%	ISO 527-2/50
弯曲模量	1450	MPa	ISO 178
摩擦系数(Dynamic)	0.50		ASTM D1894

薄膜	额定值	单位制	测试方法
拉伸模量 - 正切(20 μm)	3000	MPa	内部方法
抗张强度 - MD1(断裂, 20 μm)	260	MPa	ASTM D882
伸长率 - MD2(断裂, 20 μm)	85	%	ASTM D882

热性能	额定值	单位制	测试方法
热变形温度(0.45 MPa, 未退火)	85.0	°C	ISO 75-2/B
维卡软化温度	154	°C	ISO 306/A50

PP MOPLEN HP526J

甲基排列在分子主链的同一侧称等规聚丙烯，若甲基无秩序的排列在分子主链的两侧称无规聚丙烯，当甲基交替排列在分子主链的两侧称间规聚丙烯。一般工业生产的聚丙烯树脂中，等规结构含量约为95%，其余为无规或间规聚丙烯。工业产品以等规物为主要成分。聚丙烯也包括丙烯与少量乙烯的共聚物在内。通常为半透明无色固体，无臭无毒。由于结构规整而高度结晶化，故熔点可高达167℃。耐热、耐腐蚀，制品可用蒸汽消毒是其突出优点。密度小，是最轻的通用塑料。缺点是耐低温冲击性差，较易老化，但可分别通过改性予以克服。

一、均聚PP-聚丙烯 [size=-1]Homo-polymer polypropylene，简称PPH聚丙烯PP的均聚物简称PPH，是单一丙烯单体的聚合物。聚丙烯（PP）作为热塑塑料聚合物于1957年开始商品化生产，是有规立构聚合物中的第一个。其历史意义更体现在，它一直是增长最快的主要热塑性塑料，2004年它的全国总产量达到300万吨。它在热塑性塑料领域内有十分广泛的应用，特别是在纤维和长丝、薄膜挤压、注塑加工等方面。

二、PP共聚物，Polypropylene Copolymer， 简称PPC，是丙烯单体与乙烯单体的共聚物；按照乙烯单体在分子链上的分布方式，共聚PP可以分为无规共聚物（PPR）和嵌段共聚物（PPB）两种。PPR的刚性好，但耐冲击性不好，尤其耐低温冲击性更不好，耐蠕变性差。PPB的耐冲击性好，但耐蠕变性和PPR一样差。PPR的耐冲击性和耐蠕变性则都不好。

PP MOPLEN HP526J 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！