美国首诺PA66 VYDYNE R220 产品说明：

Vydyne R220 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in natural, it is an injection-molding grade formulated to retain the inherent processing advantages of unreinforced PA66 while enhancing rigidity, strength and heat resistance. Vydyne R220 maintains the chemical resistance typical of PA66 to a wide variety of chemicals, gasoline, oils, greases and solvents.

Vydyne R220 resin utilizes a unique mineral-reinforced PA66 system developed by Ascend Performance Materials to satisfy the market need for a high-rigidity thermoplastic as an alternative to certain metals. This mineral system provides two key features:
(1) isotropic behavior-property development in molded parts is usually independent of flow direction.
(2) a reduction in the tendency to develop sink marks in heavy cross sections such as molded-in bosses and ribs.

While not sink-free, parts made from Vydyne R220 can often permit boss and rib design or wall cross section changes that would not be tolerable in other unreinforced thermoplastic materials. Thus Vydyne R220 resin offers more uniform molded part strength and performance, as well as wider latitude in part design.

Vydyne R220 resin is a workhorse of Ascend Performance Materials" full line of mineral-reinforced PA66 resins, providing the best overall balance of properties. Vydyne R220 is heat stabilized and designed to provide increased ductility and reduced melt viscosity vs. unreinforced materials.This ductility improvement results in tougher, more impact-resistant molded parts. The reduction in melt viscosity enhances overall ease of injection-molding, resulting in minor reductions in tensile strength, modulus and heat distortion temperature. Parts manufactured from Vydyne R220 have successfully withstood paint bake oven cycles without significant loss of either dimensional stability or part properties.

物理性能	干燥	调节后的	单位制	测试方法
密度	1.48	--	g/cm3	ISO 1183
收缩率				ISO 294-4
垂直流动方向 : 23°C, 2.00 mm	1.0	--	%	ISO 294-4
流动方向 : 23°C, 2.00 mm	1.1	--	%	ISO 294-4
吸水率				ISO 62
23°C, 24 hr	1.1	--	%	ISO 62
平衡, 23°C, 50% RH	1.6	--	%	ISO 62

机械性能	干燥	调节后的	单位制	测试方法
拉伸模量(23°C)	6900	2600	MPa	ISO 527-2
拉伸应力(断裂, 23°C)	103	73.0	MPa	ISO 527-2
拉伸应变				ISO 527-2
屈服, 23°C	1.5	16	%	ISO 527-2
断裂, 23°C	6.0	30	%	ISO 527-2
弯曲模量(23°C)	6100	2300	MPa	ISO 178
弯曲应力(23°C)	124	50.0	MPa	ISO 178
泊松比	0.40	--		ISO 527

冲击性能	干燥	调节后的	单位制	测试方法
简支梁缺口冲击强度				ISO 179
-30°C	6.0	8.0	kJ/m2	ISO 179
23°C	7.0	17	kJ/m2	ISO 179
简支梁无缺口冲击强度				ISO 179
-30°C	110	130	kJ/m2	ISO 179
23°C	140kJ/m2	无断裂		ISO 179
悬壁梁缺口冲击强度				ISO 180
-30°C	7.0	7.0	kJ/m2	ISO 180
23°C	9.0	16	kJ/m2	ISO 180

PA66 VYDYNE R220

PC/ABS合金，PC与ABS共混物可以综合PC和ABS的优良性能，提高ABS的耐热性、抗冲击和拉伸强度，降低PC成本和熔体粘度，改善加工性能，减少制品内应力和冲击强度对制品厚度的敏感性。PC/ABS合金发展迅速，全球产量约为80万吨/年左右，世界各大公司纷纷开发推出PC/ABS合金新品种，如阻燃、玻纤增强、电镀、耐紫外线等品种，尤其是在汽车工业中得到广泛应用，另外还广泛应用于计算机、复印机和电子电气部件等。我国也开始一定研究和生产，如上海杰事杰公司的PC/ABS合金材料已应用于汽车装饰件、灯壳和耐热电器壳体；中科院长春应用化学所开发的高耐热、高耐热高抗冲、高耐热阻燃三个品级的PC/ABS合金材料已被国内数家汽车制造公司使用，用做前装饰板、仪表板及物品箱盖专用料等。兰州大学研究在PC/ABS共混体系中加入高压聚乙烯进行增容改性，得到混合物流动性好且低温韧性与模量几乎不受影响，适用于制作薄壁板材；国内研究人员为了降低PC/ABS两相之间的界面能，在PC和ABS中加入抗冲击剂MBS，合金的空冲击度可以达到极高值，

耐水解稳定性PC/ABS

耐水解稳定性系列PC/ABS（HAC8250R）主要应用于汽车仪表板骨架等汽车内饰产品。汽车仪表板骨架作为整个仪表板的支撑结构件，其重要性不言而喻，因此主机厂对仪表板材料提出了更苛刻的要求。目前，仪表板骨架不仅要求有良好的机械性能，加工性能，而且要有优秀的耐水解性能和热老化性能，以适应汽车在极端高温，高湿的环境下使用。

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。

化学和物理特性: PC/ABS具有PC和ABS两者的综合特性。例如ABS的易加工特性和PC的优良机械特性和热稳定性。二者的比率将影响PC/ABS材料的热稳定性。PC/ABS这种混合材料还显示了优异的流动特性。收缩率在0.5%左右。

PA66 VYDYNE R220 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！