美国杜邦FEP CJ99 食品级 高韧性 电气性能良好 绝缘材料 电线电缆
Teflon? FEP CJ 99
聚全氟乙烯-丙烯树脂
DuPont Fluoropolymers
产品说明：
For inventory control purposes product name may be followed by an X.
Products labeled FEP CJ 99 and FEP CJ 99 X are equivalent and all information in this document is applicable to both.
Typical Application
Wire and cable insulation, small tubing and injection molded parts.
DuPont Teflon ? FEP CJ 99 is a melt-processible copolymer of tetrafluoroethylene and hexafluoropropylene without additives that meets the requirements of ASTM D 2116 type I.
Thanks to the unique combination of a Melt Flow Rate in the range of 9 g/10 min and MIT flexlife above 40 000 cycles, this resin offers both attractive processing speeds and high stress-rack resistance in addition to the excellent characteristics typical of Teflon ? fluoropolymer resins, such as non-ageing characteristics, chemical inertness, exceptional electrical properties, low flammability, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption and excellent weather resistance. The increased transparency of Teflon ? FEP CJ 99 will also allow better colourability.
Stress crack resistance is an important element in establishing end-use performance. Extensive testing of wire and cable constructions is required for definitive performance evaluation. Well-known and most comprehensive tests for stress rack resistance of wire and cable are mandrel wrap tests as described in the military specification MIL-W-22759 (aerospace) and ISO 6722/LV112 (automotive). Experience has shown that the MIT folding endurance or flex life test, based on ASTM D 2176, performed on a thin film of resin, gives a good correlation with stress crack resistance. Resins with a higher MIT flex life, perform better in the stress-crack resistance tests. Teflon ? FEP CJ 99 has a higher degree of stress crack resistance than most FEP resins with similar viscosity (MFR) and offers higher productivity than FEP resins with similar stress crack resistance (MIT). We recommend that for applications involving repeated thermal and flex cycling, specific tests on the final cable always should be undertaken. The MIT test results should be viewed as guide to comparative performance of the various grades of resin.
Products labeled FEP CJ 99 and FEP CJ 99 X are equivalent and all information in this document is applicable to both.
Typical Application
Wire and cable insulation, small tubing and injection molded parts.
DuPont Teflon ? FEP CJ 99 is a melt-processible copolymer of tetrafluoroethylene and hexafluoropropylene without additives that meets the requirements of ASTM D 2116 type I.
Thanks to the unique combination of a Melt Flow Rate in the range of 9 g/10 min and MIT flexlife above 40 000 cycles, this resin offers both attractive processing speeds and high stress-rack resistance in addition to the excellent characteristics typical of Teflon ? fluoropolymer resins, such as non-ageing characteristics, chemical inertness, exceptional electrical properties, low flammability, heat resistance, toughness and flexibility, low coefficient of friction, non-stick characteristics, negligible moisture absorption and excellent weather resistance. The increased transparency of Teflon ? FEP CJ 99 will also allow better colourability.
Stress crack resistance is an important element in establishing end-use performance. Extensive testing of wire and cable constructions is required for definitive performance evaluation. Well-known and most comprehensive tests for stress rack resistance of wire and cable are mandrel wrap tests as described in the military specification MIL-W-22759 (aerospace) and ISO 6722/LV112 (automotive). Experience has shown that the MIT folding endurance or flex life test, based on ASTM D 2176, performed on a thin film of resin, gives a good correlation with stress crack resistance. Resins with a higher MIT flex life, perform better in the stress-crack resistance tests. Teflon ? FEP CJ 99 has a higher degree of stress crack resistance than most FEP resins with similar viscosity (MFR) and offers higher productivity than FEP resins with similar stress crack resistance (MIT). We recommend that for applications involving repeated thermal and flex cycling, specific tests on the final cable always should be undertaken. The MIT test results should be viewed as guide to comparative performance of the various grades of resin.
Teflon? FEP CJ 99 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 2.13 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率）(372°C/5.0 kg) | 9.0 | g/10 min | ASTM D2116, ISO 12086 |
| 吸水率(24 hr) | 0.010 | % | ASTM D570 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度(邵氏 D) | 56 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服, 23°C) | 28.0 | MPa | ASTM D638, ISO 12086 |
| 伸长率(断裂, 23°C) | 300 | % | ASTM D638, ISO 12086 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度(23°C) | 无断裂 | ASTM D256, ISO 180 |
| 热性能 | 额定值 | 单位制 | |
|---|---|---|---|
| 连续使用温度1 | 205 | °C | |
| 熔融温度2 | 255 | °C |
FEP: FEP全称为Fluorinated ethylene propylene，翻译为氟化乙烯丙烯共聚物（全氟乙烯丙烯共聚物） 英文商品名：Teflon* FEP，是一类化学物质。FEP是四氟乙烯和六氟丙烯共聚而成的。FEP结晶熔化点为304℃，密度为2.15g/CC（克/立方厘米）。
FEP可应用到软性塑料，其拉伸强度、耐磨性、抗蠕变性低于许多工程塑料。它是化学惰性的，在很宽的温度和频率范围内具有较低的介电常数（2.1）。
聚全氟乙丙烯FEP或者 F46，是四氟乙烯和六氟丙烯的共聚物，六氟丙烯的含量约15%左右，是聚四氟乙烯的改性材料。
F－46树脂既具有与聚四氟乙烯相似的特性，又具有热塑性塑料的良好加工性能。因而它弥补了聚四氟乙烯加工困难的不足，使其成为代替聚四氟乙烯的材料，在电线电缆生产中广泛应用于高温高频下使用的电子设备传输电线、电子计算机内部的连接线、航空宇宙用电线及其特种用途安装线、油泵电缆和潜油电机绕组线的绝缘层。
根据加工需要，F－46可分为粒料、分散液和漆料三种。其中，粒料按其熔融指数的不同，可供模压、挤出和注射成型用；分散液供浸渍烧结用；漆料供喷涂等用。
F－46中六氟丙烯的含量对共聚体的性能是有一定的影响。当前生产的F－46树脂的六氟丙烯的含量，通常在14%－25%（质量分数）左右。
物理性能
F－46树脂的分子量测定，当前尚无可行的方法。但它在380℃时的熔融粘度要比聚四氟乙烯低，为103－104Pa．s。可见F－46的分子量比聚四氟乙烯低得多。
F－46的熔点随共聚体的组分不同而有一定的差异，共聚体中六氟丙烯的含量的增加时，熔点变低。按差热分析法所测得的结果，国产F－46树脂的熔点大多在250－270℃之间，比聚四氟乙烯低。
F－46树脂是一种结晶性高聚物，结晶度比聚四氟乙烯低一些，当F－46熔体缓慢冷却到晶体熔点以下温度时，大分子重行结晶，结晶度在50%－60%之间；当熔体以淬火方式迅速冷却时，结晶度较小，在40%－50%之间。F－46的晶体结构形态，均为球晶结构，并随树脂和加工成型温度及热处理方式的不同而有一定的差异。
电绝缘性能
F－46的电绝缘性能和聚四氟乙烯十分相近。它的介电系数从深冷到最高工作温度，从50Hz到1010Hz超高频的广阔范围内几乎不变，并且很低，仅2．1左右。介质损耗角正切随频率的变化则有些变化，但随温度变化不大。
F－46树脂的体积电阻率很高，一般大于1015Ω·m，且随温度变化甚微，也不受水和潮气的影响。耐电弧大于165s。
F－46的击穿场随厚度的减少而提高，当厚度大于1mm时，击穿场强在30kV/mm以上，但不随温度的变化而变化。
热性能
F－46树脂的耐热性能仅次于聚四氟乙烯，能在－85－ 200℃的温度范围内连续使用。即使在－200℃和 260℃的极限情况下，其性能也不恶化，可以短时间使用。
F－46树脂的热分解温度高于熔点温度，在400℃以上才发生显著的热分解，分解产物主要是四氟乙烯和六氟丙烯。由于F－46大分子通常带有的等端基在熔点以上温度时也会分解，因此300℃以上进行加工时也必须注意适当的通风。F－46在熔点温度以下是相当稳定的，但在200℃高温下机械强度损失较大。图2是F－46树脂的熔融指数在恒温下的瞬间变化情况，熔融指数表示F－46在372℃，5000g重力下，10min内流过规定孔径的克数，因此，可用熔融指数的增加来分析熔体粘度的减少及共聚物发生热分解的情况。图3是F－46与F－4绝缘电线相比较的寿命曲线。
F－46在－250℃时仍不完全硬脆，还保持有很小的伸长率和一定的曲挠性，比聚四氟乙烯甚至更好些，是其他所有各类塑料所不及的。
耐化学稳定性
F－46的耐化学稳定性与聚四氟化乙烯相似，具有优异的耐化学稳定性。除与高温下的氟元素、熔融的碱金属和三氟化氯等发生反应外，与其他化学药品接触时均不被腐蚀。
力学性能
F－46与聚四氟乙烯相比，硬度及抗拉强度略有提高，摩擦系数也比聚四氟乙烯略大。常温下，F－46具有较好的耐蠕变性能；但当温度高于100℃时，耐蠕变性能反而不及聚四氟乙烯。
其他性能
F－46树脂在大气中抗氧化性能非常好，耐大气稳定性高。F－46的耐辐照性要比聚四氟乙烯好，略逊于聚乙烯。在空气中和室温下，F－46开始出现性能变化的最小吸收剂量为105－106rad?既103－104Gy，故可作耐辐照材料使用。