现货 PA66 10B140 美国杜邦 40%矿物增强尼龙 介绍
产品说明:
40% Mineral Reinforced Polyamide 66
Minlon 10B140 NC010 is a 40% mineral reinforced polyamide 66 for injection molding. It has very low warpage.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Minlon? 10B140 NC010 Nylon 66 (Unverified Data**) 物性表 | |||
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
密度 | 1.50 g/cc | 0.0542 lb/in3 | DAM; ISO 1183 |
吸水率 | 5.00% | 5.00% | DAM; Sim. to ISO 62 |
@Thickness 2.00 mm | @Thickness 0.0787 in | ||
水分吸收 | 1.60% | 1.60% | DAM; Sim. to ISO 62 |
@Thickness 2.00 mm | @Thickness 0.0787 in | ||
线性成型收缩率,Flow | 0.012 cm/cm | 0.012 in/in | DAM; ISO 294-4 2577 |
线性成型收缩率,横向 | 0.012 cm/cm | 0.012 in/in | DAM; ISO 294-4 2577 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
洛氏硬度(M 级) | 95 | 95 | DAM; ISO 2039-2 |
洛氏硬度(R 级) | 121 | 121 | DAM; ISO 2039-2 |
抗张强度(断裂) | 55.0 MPa | 7980 psi | 50%RH; ISO 527-1/-2 |
85.0 MPa | 12300 psi | DAM; ISO 527-1/-2 | |
伸长率 (断裂) | 4.00% | 4.00% | DAM; ISO 527-1/-2 |
9.00% | 9.00% | 50%RH; ISO 527-1/-2 | |
拉伸模量 | 3.80 GPa | 551 ksi | 50%RH; ISO 527-1/-2 |
矿物增强尼龙mineral reinforced nylon龙树脂中添 加矿物填料,在树脂熔点以上、分解温度以卜经挤出机混炼制 得的一类填充增强塑料。具有较纯尼龙树脂更好的刚性、耐 热性、低收缩性和较低成本,有较纤维增强尼龙更好的形稳性 〔不挠曲),但补强效果不如纤维大。常用的矿物填料有碳酸钙、硫酸钙、高岭土、Gi } ,惰石、沸石和玻璃微珠等。
主要用于车辆部件、工业和民用电器、电 子仪器部件等。