深圳市丰聚塑胶原料有限公司
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| IZOD缺口冲击强度 | 1/8" | ASTM D-256 | 87 | kg.cm/cm |
| 1/4" | ASTM D-256 | 14.3 | kg.cm/cm | |
| 降伏引张强度 | 23℃ | ASTM D-638 | 630 | kg/m |
| 拉伸强度 | ASTM D638/ISO 527 | 630 | kg/cm2(MPa)[Lb/in2] | |
| 洛氏硬度 | ASTM D785 | M-77 | ||
| ASTM D-785 | M-77 | M Scale | ||
| 曲折率 | ASTM D-542 | 1.585 | % | |
| 伸长率 | ASTM D638/ISO 527 | 6 | % | |
| 弯曲模量 | ASTM D790/ISO 178 | 24000 | kg/cm2(MPa)[Lb/in2] | |
| 弯曲模数 | 23℃ | ASTM D-790 | 24000 | kg/m |
| 弯曲强度 | ASTM D790/ISO 178 | 920 | kg/cm2(MPa)[Lb/in2] | |
| 23℃ | ASTM D-790 | 920 | kg/m | |
| 压缩强度 | ASTM D-695 | 780 | kg/cm | |
| 延伸率 | 降伏点，23℃ | ASTM D-638 | 6 | ℃ |
| 破裂点，23℃ | ASTM D-638 | 110 | ℃ | |
| IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 87 | kg·cm/cm(J/M)ft·lb/in | ||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 110 | % | |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 透光率 | ASTM D1003/ISO 13468 | 89 | % | |
| 折射率 | ASTM D542/ISO 489 | 1.585 | ||
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 密度 / 比重 | 23/23℃ | ASTM D-792 | 1.20 | |
| 全光穿透率 | 3mmt | ASTM D-570 | 89 | % |
| 浊度 | 3.2mmt | ASTM D-1003 | ＜0.8 | % |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 燃烧性 | 1/16" | UL 94 | V-2 | |
| 燃烧性（率） | UL94 | V-2 | ||
| 热变形温度 | ASTM D648/ISO 75 | 136 | ℃（℉） | |
| ASTM D648/ISO 75 | 125 | ℃（℉） | ||
| 未退火,18.6Kg/cm | ASTM D-648 | 125 | ℃ | |
| 未退火,4.6Kg/cm | ASTM D-648 | 136 | ℃ | |
| 热传导系数 | ASTM C-177 | 0.2 | W/m℃ | |
| 维卡软化点 | 1Kg,50℃/hr | ASTM D-1525 | 153 | ℃ |
| ASTM D1525/ISO R306 | 150 | ℃（℉） | ||
| 线膨胀系数 | 40～100℃ | ASTM D-696 | 6-8 | |
| 线性膨胀系数 | ASTM D696/ISO 11359 | 6-8 | mm/mm.℃ | |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 介电常数 | ASTM D150/IEC 60250 | 60Hz”2.95 | ||
| 10 | ASTM D-150 | 2.9 | ||
| 60Hz | ASTM D-150 | 2.95 | ||
| 介电损耗 | 60Hz | ASTM D-150 | 0.0004 | |
| 10 | ASTM D-150 | 0.009 | ||
| 绝缘破坏强度 | 1.6mm | ASTM D-149 | 30 | KV/mm |
| 耐电弧性 | ASTM D-495 | 110 | sec | |
| ASTM D495/IEC 60112 | 110 | |||
| 体积电阻率 | ASTM D257/IEC 60093 | 3 | Ω.cm | |
| ASTM D-257 | 3 | |||
| 加工性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 干燥条件 | 于120°C下烘料约4小时 | |||
| 加工温度 | 230~300 ℃ | ℃ | ||
| 250~310 ℃ | ℃ | |||
| 250~320 ℃ | ℃ | |||
| 230~320°C | ℃ | |||
| 模具温度 | 70~120°C | ℃ | ||
| 收缩率 | Parallel | ASTM D-955 | 0.5-0.7 | % |
| Across | ASTM D-955 | 0.5-0.7 | % | |
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 比重（密度） | ASTM D792/ISO 1183 | 1.2 | ||
| 成型收缩率 | ASTM D955 | 0.5-0.7 | % | |
| 熔融指数（流动系数） | ASTM D1238/ISO 1133 | （300℃.1.2kg）,10 | g/10min | |
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.20 | % | |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 熔融指数 | 300℃，1.2kg | ASTM D-1238 | 10 | g/10min |
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.20 | %
|