Elastollan 1185AF001
热塑性聚氨酯弹性体（聚醚）
产品说明：
Elastollan? 1185AF001 is a polyether-based thermoplastic polyurethane (TPU) compound that includes a halogen-containing flame retardant. It has a "V-2" rating in accordance with the UL-94 vertical flame test (at thickness of 0.67 mm or less). This product is designed to be used in extrusion applications that include cable jacketing, film/sheet, hose/hose jacketing and profile extrusion. It exhibits excellent abrasion resistance, toughness, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan? 1185AF001 is supplied in inherently white pellet form.
Elastollan 1185AF001 物性表
| 基本信息 |
|
| 添加剂 |
|
| 特性 |
- 低温下的柔性
- 抗菌性
- 良好的撕裂强度
- 良好耐磨损性
- 韧性良好
- 水解稳定
|
| 用途 |
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.29 |
g/cm3 |
ASTM D792 |
| 熔流率（熔体流动速率）(190°C/8.7 kg) |
17 到 33 |
g/10 min |
ASTM D1238 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 肖氏硬度(邵氏 A) |
87 |
|
ASTM D2240 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量(注塑) |
20.7 |
MPa |
ASTM D412 |
| 弯曲模量(注塑) |
29.0 |
MPa |
ASTM D790 |
| 泰伯耐磨性 |
95.0 |
mg |
ASTM D1044 |
| Abrasion - DIN |
40 |
mm3 |
DIN 53516 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| Softening Point - DMA |
89 |
°C |
内部方法 |
| 弹性体 |
额定值 |
单位制 |
测试方法 |
| 拉伸应力 |
|
|
ASTM D412 |
| 100%应变 |
11.7 |
MPa |
ASTM D412 |
| 300%应变 |
24.1 |
MPa |
ASTM D412 |
| 抗张强度 |
29.0 |
MPa |
ASTM D412 |
| 伸长率(断裂) |
510 |
% |
ASTM D412 |
| 撕裂强度1 |
73.6 |
kN/m |
ASTM D624 |
| 压缩永久变形 |
|
|
ASTM D395B |
| 23°C, 22 hr |
35 |
% |
ASTM D395B |
| 70°C, 22 hr |
85 |
% |
ASTM D395B |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 玻璃转化温度 |
-35.0 |
°C |
内部方法 |
| 维卡软化温度 |
70.0 |
°C |
ASTM D1525 |
| 可燃性 |
额定值 |
|
测试方法 |
| UL 阻燃等级( 0.670 mm) |
V-2 |
|
UL 94 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 110 |
°C |
|
| 干燥时间 |
2.0 到 3.0 |
hr |
|
| 建议的最大水分含量 |
0.030 |
% |
|
| 料筒后部温度 |
190 到 220 |
°C |
|
| 料筒中部温度 |
190 到 220 |
°C |
|
| 料筒前部温度 |
190 到 220 |
°C |
|
| 射嘴温度 |
210 到 225 |
°C |
|