东莞市兆佳业高分子材料有限公司
Tritan? FX100 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.19 | g/cm3 | ASTM D792 |
| 吸水率(23°C, 24 hr, 0.250 mm) | 0.50 | % | ASTM D570 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 耐磨耗性 (23°C)1 | 23haze | % | ASTM D1044 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Carbon Dioxide Permeability (23°C, 254.0 μm)2 | 150 | cm3·mm/m2/atm/24 hr | ASTM D1434 |
| Elmendorf Tear Strength | |||
| MD : 23°C, 250.0 μm | 5 | N | ASTM D1922 |
| TD : 23°C, 250.0 μm | 6 | N | |
| PPT Tear Resistance | ASTM D2582 | ||
| MD : 23°C, 250.0 μm | 42 | N | ASTM D2582 |
| TD : 23°C, 250.0 μm | 56 | N | ASTM D2582 |
| 抗撕裂蔓延性3 | ASTM D1938 | ||
| MD : 23°C, 250.0 μm | 410 | gf | ASTM D1938 |
| TD : 23°C, 250.0 μm | 310 | gf | ASTM D1938 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UV Transmittance (250.0 μm)4 | 89 | % |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Surface Energy | ASTM D5946 | ||
| Dispersive : 23°C, 250.0 μm | 39 | dyne/cm | ASTM D5946 |
| Polar : 23°C, 250 mm | 8 | dyne/cm | ASTM D5946 |
| Total : 23°C, 250.0 μm | 46 | dyne/cm | ASTM D5946 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 250 | μm | |
| 膜刺穿强度5(250 μm) | 4.60 | J | ASTM D3763 |
| 割线模量 | ASTM D882 | ||
| MD : 250 μm | 1500 | MPa | ASTM D882 |
| TD : 250 μm | 1400 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服, 250 μm | 41.0 | MPa | ASTM D882 |
| TD : 屈服, 250 μm | 40.0 | MPa | ASTM D882 |
| MD : 断裂, 250 μm | 59.0 | MPa | ASTM D882 |
| TD : 断裂, 250 μm | 52.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 屈服, 250 μm | 7.0 | % | ASTM D882 |
| TD : 屈服, 250 μm | 7.0 | % | ASTM D882 |
| MD : 断裂, 250 μm | 180 | % | ASTM D882 |
| TD : 断裂 | 200 | % | ASTM D882 |
| 落锤冲击6 | ASTM D1709A | ||
| -30°C, 250 μm | 910 | g | ASTM D1709A |
| 23°C, 250 μm | 880 | g | ASTM D1709A |
| 裤型撕裂耐性7 | ISO 6383-1 | ||
| MD : 250 μm | 11.0 | N/mm | ISO 6383-1 |
| TD : 250 μm | 11.0 | N/mm | ISO 6383-1 |
| 透氧率(23°C, 250 μm, 50% RH) | 32 | cm3·mm/m2/atm/24 hr | ASTM D3985 |
| 水气透过率 | ASTM F1249 | ||
| 23°C, 100% RH, 250 μm | 4.0 | g/m2/24 hr | ASTM F1249 |
| 38°C, 100% RH, 250 μm | 11 | g/m2/24 hr | ASTM F1249 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 撕裂强度 | ASTM D1938 | ||
| 开裂8 | 12 | kN/m | ASTM D1938 |
| 开裂9 | 13 | kN/m | ASTM D1938 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 熔融温度 | 110 | °C | |
| 线形热膨胀系数 - 流动(23°C, 0.250 mm) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| 比热 | DSC | ||
| 60°C | 1700 | J/kg/°C | DSC |
| 100°C | 1900 | J/kg/°C | DSC |
| 150°C | 2200 | J/kg/°C | DSC |
| 200°C | 2400 | J/kg/°C | DSC |
| 250°C | 2600 | J/kg/°C | DSC |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度(60°, 250 μm) | 161 | ASTM D2457 | |
| 折射率 | 1.550 | ASTM D542 | |
| 透射率(250 μm) | 92.0 | % | ASTM D1003 |
| 雾度(250 μm) | 0.70 | % | ASTM D1003 |
| 黄度指数(250 mm) | 0.50 | YI | ASTM D1925 |
| 备注 | |
|---|---|
| 1 . | average at 25 cycles |
| 2 . | 50% RH |
| 3 . | 254 mm/min |
| 4 . | % Transmission at 380 nm |
| 5 . | Dynatup, Total Energy |
| 6 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 7 . | 200 mm/min |
| 8 . | TD, 250 μm |
| 9 . | MD, 250 μm |