深圳市丰聚塑胶原料有限公司
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 剪切强度 | ASTM D-732 | DAM｜57.9 | Mpa | |
| ASTM D-732 | 50%RH｜- | Mpa | ||
| 拉伸强度 | ASTN D-638 | DAM｜517 | Mpa | |
| ASTN D-638 | 50%RH｜41.1 | Mpa | ||
| 挠曲强度 | ASTM D-790 | 50%RH｜862 | Mpa | |
| ASTM D-790 | DAM｜1689 | Mpa | ||
| 伸长率 | 断裂 | ASTM D-638 | DAM｜80 | % |
| 断裂 | ASTM D-638 | 50%RH｜210 | % | |
| 硬度计硬度 | ASTM D-676 | DAM｜6.7 | ||
| ASTM D-676 | 50%RH｜- | |||
| IZOD冲击强度 | ASTM D-256 | 50%RH｜1068 | J/m | |
| ASTM D-256 | DAM｜907 | J/m | ||
| ASTM D-1822 | DAM｜588 | kJ/m2 | ||
| ASTM D-1822 | 50%RH｜1155 | kJ/m2 | ||
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 密度 / 比重 | ASTM D-792 | DAM｜1.06 | % | |
| ASTM D-792 | 50%RH｜1.06 | % | ||
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| UL燃烧性 | UL 94 | DAM｜HB | ||
| UL 94 | 50%RH｜HB | |||
| 热变形温度 | 0.5×106Pa | DAM｜216 | ℃ | |
| 0.5×106Pa | 50%RH｜- | ℃ | ||
| 18×106Pa | ASTM D-648 | DAM｜71 | ℃ | |
| 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 熔点 | ASTM D-789 | DAM｜255 | ℃ | |
| ASTM D-789 | 50%RH｜255 | ℃ | ||
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 介电常数 | 106Hz | ASTM D-150 | DAM｜2.9 | |
| 106Hz | ASTM D-150 | 50%RH｜3.2 | ||
| 1000Hz | ASTM D-150 | DAM｜3.2 | ||
| 1000Hz | ASTM D-150 | 50%RH｜5.5 | ||
| 108Hz | ASTM D-150 | DAM｜3.2 | ||
| 108Hz | ASTM D-150 | 50%RH｜4.5 | ||
| 损耗因数 | 106Hz | ASTM D-150 | DAM｜0.02 | |
| 106Hz | ASTM D-150 | 50%RH｜0.03 | ||
| 108Hz | ASTM D-150 | DAM｜0.01 | ||
| 108Hz | ASTM D-150 | 50%RH｜0.01 | ||
| 100Hz | ASTM D-150 | DAM｜0.01 | ||
| 100Hz | ASTM D-150 | 50%RH｜0.02 | ||
| 体积电阻率 | ASTM D-257 | DAM｜1014 | Ω.m | |
| ASTM D-257 | 50%RH｜1013 | Ω.m | ||
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 吸水率 | 饱和 | ASTM D-570 | DAM｜6.7 | % |
| 饱和 | ASTM D-570 | 50%RH｜- | % | |
| 24hr | ASTM D-570 | DAM｜1.2 | % | |
| 24hr | ASTM D-570 | 50%RH｜- | % | |
| 需氧指数 | ASTM D-2863 | DAM｜15 | % | |
| ASTM D-2863 | 50%RH｜19 | %
|