POM HOSTAFORM M10AE 产品说明：

POM copolymer

Stiff-flowing type with high melt strength; good chemical resistance
to solvents, fuel and strong alkalis as well as good hydrolysis
resistance; high resistance to thermal and oxidative degradation.

Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470

Burning rate ISO 3795 and FMVSS 302 100 mm/min for a thickness more
than 1 mm.

Ranges of applications: For extrusion blow molding, and for
injection molding thick-walled, void-free molded parts.

物理性能	额定值	单位制	测试方法
密度	1.41	g/cm3	ISO 1183
溶化体积流率（MVR）(190°C/2.16 kg)	0.900	cm3/10min	ISO 1133
吸水率(饱和, 23°C)	0.65	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	2900	MPa	ISO 527-2/1A/1
拉伸应力(屈服)	65.0	MPa	ISO 527-2/1A/50
拉伸应变(屈服)	9.0	%	ISO 527-2/1A/50
标称拉伸断裂应变	25	%	ISO 527-2/1A/50
拉伸蠕变模量			ISO 899-1
1 hr	2400	MPa	ISO 899-1
1000 hr	1200	MPa	ISO 899-1

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度			ISO 179/1eA
-30°C	8.0	kJ/m2	ISO 179/1eA
23°C	10	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度			ISO 179/1eU
-30°C	200	kJ/m2	ISO 179/1eU
23°C, 局部断裂	220	kJ/m2	ISO 179/1eU

POM HOSTAFORM M10AE

POM特性

POM是一种坚韧有弹性的材料，即使在低温下仍有很好的抗蠕变特性、几何稳定性和抗冲击特性。POM既有均聚物材料也有共聚物材料。均聚物材料具有很好的延展强度、抗疲劳强度，但不易于加工。共聚物材料有很好的热稳定性、化学稳定性并且易于加工。无论均聚物材料还是共聚物材料，都是结晶性材料并且不易吸收水分。POM的高结晶程度导致它有相当高的收缩率，可高达到2%~3.5%。对于各种不同的增强型材料有不同的收缩率。

POM 优点

1、具高机械强度和刚性；2、最高的疲劳强度；3、环境抵抗性、耐有机溶剂性佳；

4、耐反覆冲击性强；5、广泛的使用温度范围(-40℃~120℃)；6、良好的电气性质；

7、复原性良好；8、具自已润滑性、耐磨性良好；9、尺寸安定性优。

缺点

受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。

POM 用途

（1）农药：合成乙草胺、丁草胺和草甘膦等；

（2）涂料：合成高档汽车用漆；

（3）树脂：合成脲醛树脂、酚醛树脂、聚缩醛树脂、蜜胺树脂、离子交换树脂等及各种粘合剂；

（4）造纸：合成纸张增强剂；

（5）铸造：翻砂脱膜剂、合成铸造粘合剂；

（6）养殖业：薰蒸消毒剂。

（7）有机原料：用于制备季戊四醇、三羟甲基丙烷、甘油、丙烯酸、丙烯酸甲酯、甲基丙烯酸、N－羟基甲基丙烯酰胺、烷基苯酚、甲基乙烯基酮等。

（8）其他：医药及消毒。

POM HOSTAFORM M10AE 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！