东莞市铭汇塑胶有限公司
Tritan? TX1501HF
共聚多酯
Eastman Chemical Company
产品说明:
Eastman Tritan? copolyester TX1501HF is a high flow grade of Eastman Tritan?. Eastman Tritan? copolyester TX1501HF has viscosity reductions of 40-50% relative to Eastman Tritan? copolyester TX1001. Eastman Tritan? copolyester TX1501HF contains a mold release derived from vegetable based sources. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan? copolyester TX1501HF may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Eastman Tritan? copolyester TX1501HF is certified to NSF/ANSI Standard 51 for Food Equipment Materials and is also certified to NSF/ANSI Standard 61 - Drinking Water System Components-Health Effects.
基本信息 | |
---|---|
|
|
添加剂 |
|
特性 |
|
用途 |
|
机构评级 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | 1.18 | g/cm3 | ASTM D792 |
收缩率 - 流动 | 0.50 到 0.70 | % | ASTM D955 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
洛氏硬度(R 级, 23°C) | 111 | ASTM D785 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | |||
23°C | 1580 | MPa | ASTM D638 |
23°C | 1600 | MPa | ISO 527-2 |
抗张强度 | |||
屈服, 23°C | 43.0 | MPa | ASTM D638 |
屈服, 23°C | 44.0 | MPa | ISO 527-2 |
断裂, 23°C | 52.0 | MPa | ASTM D638 |
断裂, 23°C | 49.0 | MPa | ISO 527-2 |
伸长率 | |||
屈服, 23°C | 7.0 | % | ASTM D638, ISO 527-2 |
断裂, 23°C | 210 | % | ASTM D638 |
断裂, 23°C | 150 | % | ISO 527-2 |
弯曲模量 | |||
23°C | 1580 | MPa | ASTM D790 |
23°C | 1500 | MPa | ISO 178 |
弯曲应力 | |||
23°C | 60.0 | MPa | ISO 178 |
屈服, 23°C | 64.0 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
悬壁梁缺口冲击强度 | |||
23°C | 860 | J/m | ASTM D256 |
-40°C | 11 | kJ/m2 | ISO 180 |
23°C | 83 | kJ/m2 | ISO 180 |
无缺口悬臂梁冲击(23°C) | 无断裂 | ASTM D4812 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 未退火 | 94.0 | °C | ASTM D648 |
1.8 MPa, 未退火 | 81.0 | °C | ASTM D648 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
透射率(总计) | 91.0 | % | ASTM D1003 |
雾度 | 1.0 | % | ASTM D1003 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 88.0 | °C | |
干燥时间 | 4.0 到 6.0 | hr | |
加工(熔体)温度 | 260 到 282 | °C | |
模具温度 | 38.0 到 66.0 | °C |