东莞市崀峰塑胶原料有限公司
Amodel DW-1130
聚二甲苯酰胺
30% 玻璃纤维增强材料
Solvay Specialty Polymers
产品说明:
Amodel? DW-1130 is a 30% glass-fiber-reinforced resin designed for high strength and stiffness and improved hydrolytic stability. This material has low moisture absorption and a low coefficient of thermal expansion, which means excellent dimensional stability. Creep resistance is also exceptional.
This grade has been approved for use with potable water in the United States, France, Germany, and the United Kingdom.
This grade has been approved for use with potable water in the United States, France, Germany, and the United Kingdom.
Amodel DW-1130 物性表
基本信息 | |
---|---|
填料/增强材料 |
|
特性 |
|
用途 |
|
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.45 | g/cm3 | ISO 1183/A |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 11900 | MPa | ISO 527-2 |
拉伸应力(断裂, 23°C) | 210 | MPa | ISO 527-2 |
拉伸应变(断裂, 23°C) | 2.3 | % | ISO 527-2 |
弯曲模量(23°C) | 11000 | MPa | ISO 178 |
弯曲强度(断裂, 23°C) | 300 | MPa | ISO 178 |
断裂弯曲应变(23°C) | 2.9 | % | ISO 178 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 | 7.2 | kJ/m2 | ISO 179 |
简支梁无缺口冲击强度 | 56 | kJ/m2 | ISO 179 |
悬壁梁缺口冲击强度 | 7.2 | kJ/m2 | ISO 180 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
热变形温度(1.8 MPa, 未退火) | 290 | °C | ISO 75-2/Af |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 120 | °C | |
干燥时间 | 4.0 | hr | |
建议的最大水分含量 | 0.030 到 0.060 | % | |
料筒后部温度 | 315 到 330 | °C | |
料筒中部温度 | 320 到 340 | °C | |
料筒前部温度 | 325 到 345 | °C | |
加工(熔体)温度 | 340 到 360 | °C | |
模具温度 | 160 | °C |
PPA(聚邻苯二甲酰胺) AS-1945 HS/美国索尔维
特性:耐热,热稳定,高强度,抗蠕变,尺寸稳定性,高刚性,耐化学性
用途:动力工具,金属取代,工业部件,工业应用,外壳,阀门,机械,汽车应用,发动机零件,厚壁配件
加工方法:注塑
参数: 比重:1.57g/cm3 收缩率:0.2% 收缩率:0.3% 拉伸模量:15200MPa 拉伸强度:252MPa
PPA(聚邻苯二甲酰胺) AT-1116 HS/美国索尔维
特性:耐高温
用途:电气应用
加工方法:注塑
参数: 比重:1.28g/cm3 收缩率:0.6% 收缩率:0.6% 吸水率:0.2% 拉伸模量:7100MPa