ABS TERLURAN EHI-7
| Product Description | |
Terluran? EHI-7 is a medium flow, high impact extrusion grade with super high gloss and superior surface aesthetics. Styrolution" s Terluran? EHI-7 is intended for mono or multilayer sheet making it a perfect fit as a substrate for our weatherable Luran? S ASA.
|
|
| General | |
Material Status |
|
Availability |
Asia PacificLatin AmericaNorth America |
Features |
Chemical ResistantGood ColorabilityHigh GlossHigh Impact ResistanceMedium FlowPleasing Surface Appearance |
Uses |
|
Forms |
|
Processing Method |
CoextrusionExtrusionSheet ExtrusionThermoforming |
| Physical | Nominal Value |
Unit |
Test Method |
Density / Specific Gravity |
ASTM D792 | ||
Melt Mass-Flow Rate (MFR)(220°C/10.0 kg) |
g/10 min |
ASTM D1238 | |
Molding Shrinkage - Flow |
in/in |
ASTM D955 | |
| Mechanical | Nominal Value |
Unit |
Test Method |
Tensile Modulus |
psi |
ASTM D638 | |
Tensile Strength(Yield, 73°F) |
psi |
ASTM D638 | |
Tensile Elongation |
ASTM D638 | ||
Yield, 73°F |
% |
||
Break, 73°F |
% |
||
Flexural Modulus(73°F) |
psi |
ASTM D790 | |
Flexural Strength(5.0% Strain) |
psi |
ASTM D790 |
ABS TERLURAN EHI-7
成型性能
无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；
宜取高料温,高模温,但料温过高易分解(分解温度为270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；
如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；
如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；
冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢；
料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；
用途
ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。