东莞市广裕塑胶原料有限公司
日本大金PTFE MG-1050F 25%玻纤增强 耐化学 耐高温 耐磨
Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow
Polymer,Thermoplastic,Fluoropolymer,PTFE,Polytetrafluoroethylene (PTFE), Glass Filled, Molded
Daikin Industries
产品说明:
25% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.
Applications:Mechanical and electrical service. Available in all forms (e.g. bearings, gaskets, valve seats, packings.
Information provided by Daikin Industries.
25% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.
Applications:Mechanical and electrical service. Available in all forms (e.g. bearings, gaskets, valve seats, packings.
Information provided by Daikin Industries.
Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 2.13 - 2.22 g/cc | 2.13 - 2.22 g/cc | ASTM D792 |
| 吸水率 | 0.00 %
@Thickness 8.50 mm, Time 86400 sec
|
0.00 %
@Thickness 0.335 in, Time 24.0 hour
|
ASTM D570 |
| 粘度 | 1.00e+13 - 1.00e+15 cP
@Temperature 340 - 380 °C
|
1.00e+13 - 1.00e+15 cP
@Temperature 644 - 716 °F
|
Melt viscosity |
| 线性成型收缩率 | 0.020 - 0.050 cm/cm | 0.020 - 0.050 in/in | |
| 变形 | 5.0 % | 5.0 % | 6.7 MPa load, at 100°C, 24 hrs; ASTM D621 |
| 7.0 % | 7.0 % | 13.7 MPa load, at 25°C, 24 hrs; ASTM D621 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 50 - 65 | 50 - 65 | |
| 抗张强度(断裂) | 20.0 - 45.0 MPa | 2900 - 6530 psi | ASTM D638 |
| 伸长率 (断裂) | 200 - 450 % | 200 - 450 % | ASTM D638 |
| 拉伸模量 | 0.392 GPa | 56.9 ksi | ASTM D638 |
| 弯曲模量 | 0.490 - 0.588 GPa | 71.1 - 85.3 ksi | ASTM D790 |
| 抗压强度 | 5.00 - 6.00 MPa
@Temperature 25.0 °C
|
725 - 870 psi
@Temperature 77.0 °F
|
1% deformation; ASTM D695 |
| 悬壁梁无缺口冲击强度 | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| 摩擦系数 | 0.15 - 0.30 | 0.15 - 0.30 | Non-lubricating |
| 静态摩擦系数 | 0.020 | 0.020 | Coated-steel surface |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | = 1.00e+18 ohm-cm | = 1.00e+18 ohm-cm | ASTM D257 |
| 介电常数 | 2.1
@Frequency 1000 Hz
|
2.1
@Frequency 1000 Hz
|
ASTM D150 |
| 2.1
@Frequency 1e+6 Hz
|
2.1
@Frequency 1e+6 Hz
|
ASTM D150 | |
| 介电强度 | 19.0 kV/mm
@Thickness 3.20 mm
|
483 kV/in
@Thickness 0.126 in
|
Short time; ASTM D149 |
| 耗散因数 | = 0.000010
@Frequency 1000 Hz
|
= 0.000010
@Frequency 1000 Hz
|
ASTM D150 |
| 0.000020
@Frequency 1e+6 Hz
|
0.000020
@Frequency 1e+6 Hz
|
ASTM D150 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | 100 μm/m-°C
@Temperature 23.0 - 60.0 °C
|
55.6 μin/in-°F
@Temperature 73.4 - 140 °F
|
ASTM D696 |
| 导热系数 | 0.250 W/m-K | 1.74 BTU-in/hr-ft2-°F | ASTM C177 |
| 熔融温度 | 327 °C | 621 °F | |
| 最高工作温度, Air | 260 °C | 500 °F | Continuous use |
| 可燃性(UL94) | V-0 | V-0 |
PTFE:聚四氟乙烯（Teflon或PTFE），俗称“塑料王”，是由四氟乙烯经聚合而成的高分子化合物，具有优良的化学稳定性、耐腐蚀性、密封性、高润滑不粘性、电绝缘性和良好的抗老化耐力。用作工程塑料，可制成聚四氟乙烯管、棒、带、板、薄膜等。一般应用于性能要求较高的耐腐蚀的管道、容器、泵、阀以及制雷达、高频通讯器材、无线电器材等。
基本特点
耐高温——使用工作温度达250℃。
耐低温——具有良好的机械韧性；即使温度下降到-196℃，也可保持5%的伸长率。
耐腐蚀——对大多数化学药品和溶剂，表现出惰性、能耐强酸强碱、水和各种有机溶剂。
耐气候——有塑料中最佳的老化寿命。
高润滑——是固体材料中摩擦系数最低者。
不粘附——是固体材料中最小的表面张力，不粘附任何物质。聚四氟乙烯相对分子质量较大，低的为数十万，高的达一千万以上
聚四氟乙烯
聚四氟乙烯
，一般为数百万（聚合度在104数量级，而聚乙烯仅在103）。一般结晶度为90～95%，熔融温度为327～342℃。聚四氟乙烯分子中CF2单元按锯齿形状排列，由于氟原子半径较氢稍大，所以相邻的CF2单元不能完全按反式交叉取向，而是形成一个螺旋状的扭曲链，氟原子几乎覆盖了整个高分子链的表面。这种分子结构解释了聚四氟乙烯的各种性能。温度低于19℃时，形成13/6螺旋；在19℃发生相变，分子稍微解开，形成15/7螺旋。
虽然在全氟碳化合物中碳-碳键和碳-氟键的断裂需要分别吸收能量346.94和484.88kJ/mol，但聚四氟乙烯解聚生成1mol四氟乙烯仅需能量171.38kJ。所以在高温裂解时，聚四氟乙烯主要解聚为四氟乙烯。聚四氟乙烯在260、370和420℃时的失重速率（%）每小时分别为1×10-4．4×10-3和9×10-2。可见，聚四氟乙烯可在 260℃长期使用。由于高温裂解时还产生剧毒的副产物氟光气和全氟异丁烯等，所以要特别注意安全防护并防止聚四氟乙烯接触明火。
广裕塑胶现货供应:PP，PE，PVC，ABS，PC，PC/ABS，PA6，PA66，,PA6T，PA9T，PAMXD6，IXEF，PA11，PA12，PBT，PET，PPS，LCP，PEI，PPSU，PSU，氟树脂，PEEK，TPU，TPV，TPE，食品级降解塑料（PBAT，PLA，PBS，PBST）等。
免费提供原料：物性表，UL黄卡，随货同行(提供)SGS,MSDS,FDA,LFGB,USP,COA,PFOS,REACH, ROSH/SONY等资料。