美国科慕PTFE DISP30 耐磨损 耐化学 涂覆 流延薄膜 食品级PTFE
Teflon? PTFE DISP 30
聚四氟乙烯
DuPont Fluoropolymers
产品说明：
DuPont? Teflon ? PTFE DISP 30 is a milky white aqueous PTFE dispersion stabilized with a non-ionic surfactant. It is a general-
purpose product, often preferred for coating and impregnating woven goods and for some coating processes. It imparts
properties unique to PTFE resin to porous structures, as well as to base materials when used as an additive. When properly processed, the PTFE resin in DISP 30 exhibits the superior properties typical of the fluoropolymer resin: retention of properties after service at 260 °C (500 °F), and useful properties at -240 °C (-400 °F).
DISP 30 aqueous dispersion provides:
Typical Applications
PTFE DISP 30 meets the requirements of ASTM D 4441-04, type II, grade 6, class A.
purpose product, often preferred for coating and impregnating woven goods and for some coating processes. It imparts
properties unique to PTFE resin to porous structures, as well as to base materials when used as an additive. When properly processed, the PTFE resin in DISP 30 exhibits the superior properties typical of the fluoropolymer resin: retention of properties after service at 260 °C (500 °F), and useful properties at -240 °C (-400 °F).
DISP 30 aqueous dispersion provides:
- inertness to nearly all industrial chemicals and solvents
- stability at high temperatures
- excellent dielectric properties
- lowest coefficient of friction of any solid material
- excellent weatherability
- non-stick characteristics
Typical Applications
- Coated woven fiber-glass fabric used in architectural, high-performance industrial, food processing and electronics applications
- Impregnated packing made from braided fibers for severe chemical and thermal service
- Cast film for capacitor dielectrics or chemical barriers
- Surface coatings for metallic or other high-temperature substrates
- Anti-drip additive for plastics
- Binder for battery anode or cathode matrixes
PTFE DISP 30 meets the requirements of ASTM D 4441-04, type II, grade 6, class A.
Teflon? PTFE DISP 30 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | |||
| --1 | 2.21 | g/cm3 | ISO 12086, ASTM D4895 |
| --2 | 1.51 | g/cm3 | ISO 8962, ASTM D4441 |
| pH值 | |||
| -- | 10.0 | ASTM E70 | |
| -- | 10.0 | ISO 1148 | |
| 固体含量 - % PTFE by weight | |||
| -- | 60 | % | ASTM D4441 |
| -- | 60 | % | ISO 12086 |
| 平均颗粒尺寸 | 220 | nm | 内部方法 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 布络克菲尔德粘度 | |||
| 25°C | 25 | mPa·s | ASTM D2196 |
| 25°C | 25 | mPa·s | ISO 2555 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Surfactant Content - based on PTFE solids | |||
| -- | 6.0 | % | ISO 8963 |
| -- | 6.0 | % | ASTM D4442 |
PTFE:聚四氟乙烯（Teflon或PTFE），俗称“塑料王”，是由四氟乙烯经聚合而成的高分子化合物，具有优良的化学稳定性、耐腐蚀性、密封性、高润滑不粘性、电绝缘性和良好的抗老化耐力。用作工程塑料，可制成聚四氟乙烯管、棒、带、板、薄膜等。一般应用于性能要求较高的耐腐蚀的管道、容器、泵、阀以及制雷达、高频通讯器材、无线电器材等。
基本特点
耐高温——使用工作温度达250℃。
耐低温——具有良好的机械韧性；即使温度下降到-196℃，也可保持5%的伸长率。
耐腐蚀——对大多数化学药品和溶剂，表现出惰性、能耐强酸强碱、水和各种有机溶剂。
耐气候——有塑料中最佳的老化寿命。
高润滑——是固体材料中摩擦系数最低者。
不粘附——是固体材料中最小的表面张力，不粘附任何物质。聚四氟乙烯相对分子质量较大，低的为数十万，高的达一千万以上
聚四氟乙烯
聚四氟乙烯
，一般为数百万（聚合度在104数量级，而聚乙烯仅在103）。一般结晶度为90～95%，熔融温度为327～342℃。聚四氟乙烯分子中CF2单元按锯齿形状排列，由于氟原子半径较氢稍大，所以相邻的CF2单元不能完全按反式交叉取向，而是形成一个螺旋状的扭曲链，氟原子几乎覆盖了整个高分子链的表面。这种分子结构解释了聚四氟乙烯的各种性能。温度低于19℃时，形成13/6螺旋；在19℃发生相变，分子稍微解开，形成15/7螺旋。
虽然在全氟碳化合物中碳-碳键和碳-氟键的断裂需要分别吸收能量346.94和484.88kJ/mol，但聚四氟乙烯解聚生成1mol四氟乙烯仅需能量171.38kJ。所以在高温裂解时，聚四氟乙烯主要解聚为四氟乙烯。聚四氟乙烯在260、370和420℃时的失重速率（%）每小时分别为1×10-4．4×10-3和9×10-2。可见，聚四氟乙烯可在 260℃长期使用。由于高温裂解时还产生剧毒的副产物氟光气和全氟异丁烯等，所以要特别注意安全防护并防止聚四氟乙烯接触明火。